Thermoplastic desiccant

Details Thermoplastic desiccant Thermoplastic desiccant

2002-04-26

2003-09-02

Gorr, Rachel (Department: 1711)

Synthetic resins or natural rubbers -- part of the class 520 ser

Synthetic resins

From reactant having at least one -n=c=x group as well as...

C053S400000, C053S449000, C252S194000, C528S053000, C528S056000, C034S329000, C521S159000

Reexamination Certificate

active

06613865

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to the use of thermoplastic polymer compositions containing reactive isocyanate groups as a drying agent for protecting moisture-sensitive goods.
Various goods and products of everyday life have to be protected against moisture, more particularly moisture from the surrounding atmosphere. These include in particular highly reactive one-component moisture-curing adhesive systems such as, for example, one-component moisture-curing polyurethane adhesives, moisture-curing systems based on reactive silane groups and the like.
2. Description of the Related Art
A typical method of protecting such moisture-sensitive reactive adhesive/sealant systems comprises packing them in water-impermeable containers such as, for example, flanged metal cartridges, airtight drums or casks, optionally using inner packs of laminated films consisting of a layer of metal foil and one or more layers of plastic films. Packs such as these are described, for example, in DE-A-3605422, EP-A-413049 or in DE-U-9912012.
Moisture-reactive polyurethane hotmelts are particularly sensitive to moisture. It is known that moisture-sensitive polyurethane hotmelts are produced in such a way that they contain very few reactive isocyanate groups which react even with traces of moisture and form crosslinked infusible polymers. Accordingly, moisture-sensitive polyurethane hotmelts have to be packed and stored in the strict absence of moisture, as illustrated by the following example: in order completely to harden 1 kg of a polyurethane hotmelt with an isocyanate content of 1%, i.e. to react all the isocyanate groups, takes ca. 1 gram of water. Accordingly, a skin is formed on the surface of such a hotmelt even if only fractions of this amount of water pass to the surface of the product.
Consequently, where moisture-sensitive polyurethane hotmelts are packed in drums, casks, cartridges or laminated film bags, even traces of penetrating moisture are sufficient to render the entire contents of the container unusable through skin formation.
In order to achieve a shelf life of 9 months or longer for a packed polyurethane hotmelt, the imperviousness of the packs has to meet very stringent requirements, particularly in regard to the tightness of the seal used and the dimensional stability of the container. Since the tightness of the container can never be satisfactorily tested, even with 100% incoming goods control, it happens fairly frequently in the present state of the art that individual containers are only detected as leaky after they have been filled with the hotmelt. It is a serious disadvantage that the customer and user is also unable to detect such faulty packs because the crosslinked infusible skin is difficult to tell apart from the uncrosslinked fusible reactive hotmelt at room temperature. Although it is possible to melt the surface every time the container is changed in order to assess whether a skin has already formed, this is a labor-intensive and time-consuming step, especially since in industrial application very little time is generally available for changing containers. As a rule, the processor only notices skin formation in the container through a steep fall in the quantity of hotmelt delivered through the installation. Since the crosslinked skin can block the throughflow pipes, faulty bonding and expensive, time-consuming breaks in production are the outcome.
There has been no shortage of attempts to develop suitable packs for reactive polyurethane hotmelts where the skin formation and surface hardening mentioned above are avoided. Thus, DE-A-4404631 describes a process for the self-sealing of containers in which moisture-sensitive fusible materials, such as polyurethane hotmelts for example, are covered with an insert consisting of a heat-resistant plastic film impermeable to water vapor and a plastic disk of a thermoplastic material with a linear expansion coefficient of 6.10
−5
/K. This cover enables the surface of such moisture-sensitive fusible materials to be self-sealed. In addition, in one particular embodiment of the process in question, a small bag filled with molecular sieve as a moisture adsorber is placed on the insert after the fusible material has been sealed and the container is then closed with a lid.
The use of molecular sieves, silica gels or sharply dried, hygroscopic inorganic salts with a tendency towards hydrate formation as a water collector or water adsorber has been repeatedly proposed in the prior art, cf. DE-A-19722789, US-A-5900226, JP-02760769 B2 or JP-07048546 A.
All these adsorbers are either used to dry the raw materials used or are incorporated in the pack as a drying agent. For the second of these two applications, however, the adsorbers in question perform their function to only a very limited extent. This is because the adsorption of water onto molecular sieves, silica gels or inorganic salts containing water of crystallization is reversible, i.e. the water initially adsorbed desorbs again and is then able to react irreversibly with the reactive groups, such as the isocyanate groups, of a polyurethane hotmelt adhesive in a crosslinking reaction. This water is thus irreversibly removed from the adsorption/desorption equilibrium and ultimately leads to optionally complete crosslinking of the packed material.
Accordingly, there is still a need to find improved ways of protecting moisture-sensitive goods.
BRIEF SUMMARY OF THE INVENTION
The solution to this problem as provided by the invention is defined in the claims and consists essentially in the use of thermoplastic polymer compositions containing reactive isocyanate groups as a drying agent in the packaging of moisture-sensitive goods.
In a preferred embodiment, these thermoplastic polymers have a content of reactive NCO groups of 0.3 to 20% by weight and preferably 0.6 to 15% by weight, based on the composition as a whole.
DETAILED DESCRIPTION OF THE INVENTION
Reactive polymers of the type in question may be obtained in known manner by reacting compounds or polymers containing OH or amino groups with an excess of polyisocyanates. These polyisocyanates should preferably have a high reactivity so that aromatic polyisocyanates are preferably used. The crude technical isomer and homolog mixture of diphenyl methane diisocyanate (MDI) is particularly suitable from the cost perspective. Suitable polyols are polyester polyols or polyether polyols solid at room temperature with a melting point below 150° C. or fusible mixtures of polyester polyols, polyether polyols and sugars. Examples of sugars are mainly the monosaccharides or oligosaccharides such as, for example, glucose, galactose, mannose, fructose, arabinose, xylose, ribose or even cane sugar. In principle, other low molecular weight polyols or polyamines may also be at least partly used. It is important in this regard that the reaction product of polyisocyanate and polyalcohol is still fusible at temperatures below 180° and preferably below 130° so that it may readily be converted into the “surface-rich” form. In order to achieve a high water adsorption capacity, the polyisocyanate is preferably used in a large stoichiometric excess. Chemically non-bound polyisocyanate is physically fixed in the solidifying matrix of the thermoplastic drying agent. After reacting off with water in the function of the moisture scavenger, the chemically non-bound polyisocyanate is chemically irreversibly bound to the drying agent, thus avoiding health hazards from unreacted monomeric isocyanate at the time of disposal of the thermoplastic polymer. Where polyisocyanates of relatively high functionality, such as crude MDI, or sugars are used, it can be useful to add monohydric C
1-12
alcohols or corresponding secondary amines as chain terminators in order to prevent a high degree of crosslinking of the reaction mixture and hence the formation of a thermoset.
In order to obtain high reactivity of the drying agent to moisture, particularly preferred embodiments of the thermoplastic polymer drying agent compositi

Affiliated with

Also associated with

Rating

Thermoplastic desiccant does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Thermoplastic desiccant, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Thermoplastic desiccant will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3033579