Metal treatment – Process of modifying or maintaining internal physical... – Heating or cooling of solid metal
Reexamination Certificate
2001-05-03
2003-07-15
Wyszomierski, George (Department: 1742)
Metal treatment
Process of modifying or maintaining internal physical...
Heating or cooling of solid metal
C420S423000
Reexamination Certificate
active
06592689
ABSTRACT:
BACKGROUND OF INVENTION
A glass is a material that when cooled from a heated liquid transforms to the solid state without forming crystals. Such non-crystallized materials are also called amorphous materials. For example, one of the better known amorphous materials is quartz, which can be used to form conventional window glass.
Most metals crystallize when they are cooled from the liquid state at reasonable rates, which causes their atoms to be arranged into a highly regular spatial pattern or lattice. A metallic glass is one in which the individual metal atoms have settled into an essentially random arrangement. Metallic glasses are not transparent like quartz glasses and are often less brittle than window glass.
A number of simple metal alloys may also be processed to form a glass-like structure. Binary metal alloys near deep eutectic features of the corresponding binary phase diagrams may be prepared into a glassy structure on cooling from the liquid state at rates greater than 1000 degrees per second. These binary metallic glasses may possess different properties than crystalline metals. These different properties may be useful in certain applications.
Bulk metallic glass forming alloys are a group of multicomponent metallic alloys that exhibit exceptionally high resistance to crystallization in the undercooled liquid state. Compared with the rapidly quenched binary metallic glasses studied prior to 1990, these alloys can be vitrified at far lower cooling rates, less than 10 degrees per second.
Many of the recently discovered bulk glass forming alloys can be broadly described as pseudo-ternary alloys of the form ETM1-x-yLTMxSMy. Typically the early transition metal couple, ETM, is a combination of elements from group IVB of the periodic table; e.g., Zr and Ti. The late transition metals, LTM, are typically combinations of the 3d transition metals from groups VIIIB and IB; e.g., Fe, Co, Ni, and Cu. The simple metal element, SM, is normally chosen groups from IIA or IIIA; e.g., Be, Mg or Al. However, the addition of a SM element is not a requirement for the formation of a bulk glass forming alloy.
Examples of some of the composition manifolds that contain ideal bulk metallic forming compositions are as follows: Zr—Ti—Cu—Ni—Be, Zr—Nb—Cu—Ni—Al, Ti—Zr—Cu—Ni, and Mg—Y—Cu—Ni—Li. There are also bulk metallic glass forming alloys based on magnesium.
Each of the chemical species and their combinations are chosen for a given alloy composition, such that the alloy composition lies in a region with low-lying liquidus surface. Alloy compositions that exhibit a high glass forming ability are generally located in proximity to deep eutectic features in the multicomponent phase diagram.
The glass forming ability of a given alloy is in part described by the critical cooling rate that is required to avoid a fraction of crystal which is either large enough to be detectable, or large enough to cause some change of property. The glass forming ability is generally considered higher if the alloy composition has a reduced glass transition temperature. The reduced glass transition temperature is defined as the ratio between the glass transition temperature T
g
to the liquidus temperature T
liq
.
Early theoretical work on crystallization of undercooled liquid metals has showed that the nucleation rate was often vanishingly small for materials with T
rg
of approximately ⅔.
Bulk metallic glass alloys can be more easily formed if the eutectic like condition is satisfied. Many believe that the alloy should be close to a eutectic in order to obtain a high T
rg
.
SUMMARY OF INVENTION
The present invention teaches that specific kinds of modifications in attributes of minor aspects of the chemical structure of certain bulk metallic glasses may change the properties of the glass structure in an unexpected way. Specifically, the constituents of the glass may be changed by an amount &dgr; to change the glass forming capability.
Another aspect teaches a specific alloy of Zr
58.47
Nb
2.76
Cu
15.4
Ni
12.6
Al
10.37
.
REFERENCES:
patent: 5380375 (1995-01-01), Hashimoto et al.
patent: 5482577 (1996-01-01), Hashimoto et al.
patent: 5735975 (1998-04-01), Lin et al.
patent: 5797443 (1998-08-01), Lin et al.
Eckert, J. et al. “Mechanically alloyed Zr55Al10Cu30Ni5metallic glass composites containing nanocrystalline W particles.”Journal of Applied Physics(1999): 7112-1779.
Xing, L.Q. et al. “High-strength materials produced by precipitation of icosahedral quasicrystals in bulk Zr-Ti-Cu-Ni-Al amorphous alloys.”Applied Physics Letters(1999): 664-666.
Xing, L.Q. et al. “Deformation mechanism of amorphous and partially crystallized alloys.”NanoStructured Materials(1999):503-506.
Eckert, J. “Mechanical alloying of bulk metallic glass forming systems.”Materials Science Forum(1999):3-12.
Schurack, F. et al. “Synthesis and properties of mechanically alloyed and ball milled high strength amorphous or quasicrystalline Al-alloys.”Materials Science Forum(1999):49-54.
Kubler, A. et al. “Nanoparticles in an amorphous Zr55Al10Cu30Ni5-matrix—the formation of composites by mechanical alloying.”Nanostructured Materials(1999):443-446.
Eckert, J. et al. “Nanophase composites in easy glass forming systems.”NanoStructured Materials(1999):439-442.
Schlorke, N. et al. “Properties of Mg-Y-Cu glasses with nanocrystalline particles.”NanoStructured Materials(1999): 127-130.
Eckert, J. et al. “Mechanically alloyed Mg-based metallic glasses and metallic glass composites containing nanocrystalline particles.”Z. Metallkd 90(1999):908-913.
Shingu, P.H. “Metastability of amorphous phases and its application to the consolidation of rapidly quenched powders.”Materials Science and Engineering(1988):137-141.
California Institute of Technology
Fish & Richardson P.C.
Wyszomierski George
LandOfFree
Fractional variation to improve bulk metallic glass forming... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Fractional variation to improve bulk metallic glass forming..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Fractional variation to improve bulk metallic glass forming... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3008219