Chemistry: electrical current producing apparatus – product – and – Current producing cell – elements – subcombinations and... – Electrode
Reexamination Certificate
2000-06-15
2002-11-26
Chaney, Carol (Department: 1745)
Chemistry: electrical current producing apparatus, product, and
Current producing cell, elements, subcombinations and...
Electrode
C429S233000, C029S002000
Reexamination Certificate
active
06485865
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a porous metal sheet composed of a layered structure, a battery electrode plate composed of the porous metal sheet, and a battery having the electrode plate. More particularly, the present invention relates to a porous metal sheet that is wound spirally to accommodate it in a cylindrical battery can of a secondary battery such as a nickel cadmium battery, a nickel hydrogen battery, and the like.
2. Description of the Related Art
As a positive plate and a negative plate for use in the nickel cadmium battery, the nickel hydrogen battery, and the like, porous metal sheets are hitherto used. The porous metal sheet is formed by plating a foamed three-dimensional reticulate porous material such as a polyurethane sponge; a nonwoven cloth; and a mesh net.
Of the above porous metal materials, a foamed metal sheet, which is formed by plating the polyurethane sponge and then burning the polyurethane, has a higher porosity than a punching metal and the like. Thus, the foamed metal sheet can be charged with a larger amount of an active substance than other porous metal sheets. Further, pores are three-dimensionally present in the foamed metal sheet. Thus, the foamed metal sheet holds the active substance therein in a high extent. Therefore, the porous metal sheet consisting of the foamed metal sheet is preferably used as an electrode substrate.
In the conventional electrode substrate composed of only the foamed metal sheet, needless to say, the number of cells on one side (surface) of the electrode substrate is almost equal to the number of cells on the other side thereof. In the case of the electrode substrate composed of the foamed metal sheets disposed on its both sides and a mesh metal sheet or a nonwoven metal sheet sandwiched between the foamed metal sheets, the number of cells of the foamed metal sheet disposed on its one side is almost equal to that of cells of the foamed metal sheet disposed on its other side. This is because both-side foamed metal sheets are formed by plating the urethane sponge made of the same material.
The electrode substrate composed of the foamed metal sheet is charged with the active substance to form an electrode plate. The rigidity of the electrode substrate is increased by charging it with the active substance. When the electrode plate is accommodated in a cylindrical can, which has a small inner diameter, by spirally winding it, it is wound at a very small curvature to accommodate it in the cylindrical can in a required volume or more than the required volume. Thus, normally, the electrode plate is so wound that the inner diameter of an innermost spiral circle of the electrode plate is as small as about 3 mm. Consequently, as shown by the photograph of FIG.
7
A and the illustration of
FIG. 7B
, the rigid electrode plate is susceptible to crack. Because the electrode plate has a certain thickness, the elongation percentage of the outer periphery thereof is higher than that of the inner periphery thereof. Thus, a crack C and a breakage B are liable to occur from the outer periphery of the electrode plate. With the recent demand for the development of a miniaturized battery and for increase in its capacity, this type of crack and breakage occur more frequently than before.
With reduction of the strength of the electrode plate relative to a tensile force, the electrode plate is susceptible to small cracks but is not susceptible to a large crack or breakage when it is wound. As a method of reducing the strength of the electrode plate, it is conceivable to increase the number of cells of the foamed sheet and to increase the number of frameworks surrounding the cells (pores). Supposing that the same amount is deposited on a unit area of a foamed sheet, the amount deposited on a surface area-increased framework becomes small. Consequently, the foamed metal sheet has a narrow framework and hence a low strength. However, when a resulting foamed metal sheet is charged with the active substance while it is being successively fed, the foamed metal sheet cannot be charged with the active substance efficiently at a high feeding speed because it has a low strength relative to a tensile force. Further, when the foamed material is plated while it is being successively fed, it cannot be plated efficiently at a high feeding speed as in the case of the time when the foamed metal sheet is charged with the active substance. Further, when the number of cells is increased, it is difficult to plate the inner side of the foamed material made of the urethane sponge, because the diameters of the cells are small. In this case, the foamed material is plated non-uniformly.
On the other hand, as a method of increasing the strength of the electrode plate, it is conceivable to decrease the number of cells of the foamed material to reduce the surface area of the framework surrounding the cells. Supposing that the same amount is deposited on a unit area of a foamed material, the amount deposit on a surface area-decreased framework becomes large. Consequently, the foamed metal sheet has a thick framework and hence a high strength. Therefore, it is possible to charge the resulting foamed metal sheet with the active substance efficiently at a high feeding speed. However, because the foamed metal sheet has a high strength relative to the tensile force, it is difficult to wind the foamed metal sheet when the foamed metal sheet is wound at a small curvature. Further, the foamed metal sheet cracks occur deep into the inner peripheral side thereof and is thus susceptible to breakage. The broken portion of the foamed metal sheet may break through a separator.
SUMMARY OF THE INVENTION
The present invention has been made in view of the above-described situation. Thus, it is an object of the present invention to prevent a electrode from cracking deeply and broken when it is spirally wound, allow a winding work to be accomplished smoothly, and prevent a feeding speed from being reduced when it is charged with an active substance.
In order to achieve the object, according to the present invention, there is provided a porous metal sheet, for use in a battery electrode substrate, composed of a two-layer structure consisting of a first foamed metal layer and a second foamed metal layer or a structure having three or more layers consisting of the first foamed metal layer, the second foamed metal layer, one or more metal layer sandwiched between said first foamed metal layer and said second foamed metal layer and selected from a group consisting of a mesh metal layer, a nonwoven metal layer or/and a metal sheet layer having uniform pattern pores formed therethrough. In the porous metal sheet having the construction, the number of cells of the first foamed metal layer and that of the second foamed metal layer are different from each other.
The number of cells of the second foamed metal layer is more than that of the first foamed metal layer by specifying the number of cells of the first foamed metal layer to 30 PPI or more and less than 60 PPI and specifying the number of cells of the second foamed metal layer to 50 PPI or more and less than 80 PPI.
The number of cells of the first foamed metal layer is set to 30 PPI or more and less than 60 PPI for the following reason: if the number of cells of the first foamed metal layer is less than 30 PPI, i.e., because the number of cells thereof is too small, the first foamed metal layer has a small active substance-holding force. Further, because the diameters of cells are large, the utilization percentage of the active substance deteriorates because the active substance is not electrically conductive. If the number of cells of the first foamed metal layer is 60 PPI or more, it is difficult to allow the mechanical property of the first foamed metal layer to be different from that of the second foamed metal layer. The reason the number of cells of the second foamed metal layer is set to 50 PPI or more is because if the number of cells of the second foamed metal layer is less than
Chaney Carol
Katayama Special Industries Ltd.
LandOfFree
Porous metal sheet, battery electrode plate composed of... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Porous metal sheet, battery electrode plate composed of..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Porous metal sheet, battery electrode plate composed of... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2937881