Process and catalyst for dehydrogenating primary alcohols to...

Details Process and catalyst for dehydrogenating primary alcohols to... Process and catalyst for dehydrogenating primary alcohols to...

2000-04-11

2002-04-23

Gitomer, Ralph (Department: 1623)

Organic compounds -- part of the class 532-570 series

Organic compounds

Carboxylic acids and salts thereof

C562S017000, C562S014000, C562S526000, C562S553000, C562S575000, C544S385000

Reexamination Certificate

active

06376708

ABSTRACT:

FIELD OF THE INVENTION
This invention generally relates to a novel process for making a carboxylic acid salt. More particularly, this invention relates to a process for dehydrogenating a primary alcohol (especially an amino alcohol, such as diethanolamine) to make a carboxylic acid salt (such as disodium iminodiacetic acid) using a copper-containing or silver-containing catalyst which also contains other metals that provide desirable characteristics, such as durability. This invention also generally relates to novel copper-containing and silver-containing catalysts that may be used in such a process, and to processes for making such catalysts.
BACKGROUND OF THE INVENTION
Carboxylic acid salts are useful in various applications. For example, salts of iminodiacetic acid may be phosphonomethylated to form N-(phosphonomethyl)iminodiacetic acid (“PMIDA”), which, in turn, may be oxidized to form N-(phosphonomethyl)glycine (known in the agricultural chemical industry as “glyphosate”). See, e.g., Gentilcore, U.S. Pat. No. 4,775,498 (disclosing a method to phosphonomethylate a salt of iminodiacetic acid); Ebner, et al., PCT/US99/03402 (disclosing a method for oxidizing PMIDA). Salts of nitrilotriacetic acid, for example, are excellent chelating agents, and consequently may be used as detergent builders, water-softening agents, scouring aids, dyeing assistants, paper-coating agents, scale inhibitors, and agents for preventing soap degeneration. And many carboxylic acid salts (e.g., salts of glycine, salts of iminodiacetic acid, etc.) may also be neutralized to their corresponding acids and then used, for example, as chelating agents; in food preparations; and as raw materials for making pharmaceuticals, agricultural chemicals, and pesticides. See, e.g., Franz, et al.,
Glyphosate: A Unique Global Herbicide
(ACS Monograph 189, 1997) at pp. 234-41 (disclosing the use of glycine and iminodiacetic acid compounds as raw materials to form N-(phosphonomethyl)glycine).
It has long been known that a carboxylic acid salt may be prepared from a primary alcohol by dehydrogenating the alcohol using a copper-containing or silver-containing catalyst. In 1945, Chitwood first reported forming a carboxylic acid salt (specifically, the potassium salt of glycine) by oxidizing a primary alcohol (specifically, monoethanolamine) in an alkaline environment (specifically, in a mixture containing potassium hydroxide) using a copper-containing catalyst (specifically, copper metal or cupric oxide, which reportedly was reduced to copper metal under the reaction conditions) or a silver-containing catalyst (specifically, silver metal or silver oxide, which reportedly was reduced to silver metal under the reaction conditions). See Chitwood, U.S. Pat. No. 2,384,817. Chitwood, however, reported that copper-containing compounds are disadvantageous for this reaction because the copper coagulates over time, thereby causing the copper-containing compounds to have a short duration of maximum catalytic activity. Chitwood also reported that silver-containing compounds have relatively low activity (the silver oxide also reportedly coagulates over time).
In 1988, Goto et al. reported forming a carboxylic acid salt by oxidizing an ethanolamine compound in an alkaline solution (specifically, an aqueous solution containing the hydroxide of an alkali metal or an alkaline earth metal) using Raney copper. See Goto et al., U.S. Pat. No. 4,782,183. Goto et al. reported selectivities of at least 94.8% when dehydrogenating monoethanolamine, diethanolamine, and triethanolamine to form salts of glycine, iminodiacetic acid, and nitrilotriacetic acid, respectively. Raney copper, however, is disadvantageous because (like Chitwood's copper-containing compounds) Raney copper deactivates over time. See, e,g., Franczyk, U.S. Pat. No. 5,292,936, Table 1 (showing the reaction time for Raney copper to increase from 4 to 8 hours over 9 cycles).
Various developments have been reported which address the instability of copper-containing catalysts when used to dehydrogenate primary alcohols. Although these developments have made the use of copper catalysts more commercially viable, their results are still not entirely satisfactory.
Franczyk, for example, reports that copper-containing catalysts (particularly Raney copper) can be stabilized by using such a catalyst which also contains 50 to 10,000 parts per million of one or more various other metals selected from the group consisting of chromium, titanium, niobium, tantalum, zirconium, vanadium, molybdenum, tungsten, cobalt, nickel, bismuth, tin, antimony, lead, and germanium, with vanadium, chromium, and molybdenum being the more preferred metals. See Franczyk, U.S. Pat. Nos. 5,292,936; 5,367,112; & 5,739,390. Although such metals do tend to impart a stabilizing effect to a copper catalyst, this effect often decreases over time. See, e.g., Franczyk patents, Table 2 (showing the reaction time decreasing from 5.8 hours to 8.0 hours over 25 cycles) and Table 4 (showing the reaction time decreasing 3.1 to 5.5 hours over 12 cycles). This decrease is due, at least in part, to the fact that such metals tend to leach over time as the catalyst is used, particularly where the primary alcohol or the dehydrogenation product is a chelating agent (e.g., a salt of iminodiacetic acid).
Ebner et al. report using a catalyst comprising copper supported on an alkali-resistant support (particularly a carbon support) to dehydrogenate primary alcohols to make carboxylic acid salts. See Ebner et al., U.S. Pat. No. 5,627,125. This catalyst also comprises about 0.05 to about 10% by weight of a noble metal to anchor and disperse the copper to the support. Although Ebner et al. report shorter reaction times with their catalyst relative to previously disclosed copper-containing catalysts, their catalyst is costly due to the need for the noble metal to anchor the copper to the support. In addition, the added volume of Ebner et al.'s catalyst due to the carbon support can, in some instances, make handling the catalyst cumbersome, consequently reducing throughput. Further, Ebner et al.'s catalyst often loses activity over time with use (although the rate of deactivation is often less than the rate of deactivation of the Franczyk catalysts). See, e.g., Ebner et al., Table 1 (showing the reaction time increasing from 103 to 150 minutes over 9 cycles) and Table 2 (showing the reaction time increasing from 61 to 155 minutes over 8 cycles). As with the Franczyk catalysts, this problem tends to arise particularly where the primary alcohol or the dehydrogenation salt product is a chelating agent.
Other reported copper-containing catalysts contain a non-carbon support, such as, SiO
2
, Al
2
O
3
, TiO
2
, ZrO
2
, and the like. See, e.g., Akzo Nobel, WO 98/13140 (disclosing a catalyst consisting of copper on ZrO
2
). These supports, however, tend to be vulnerable to attrition under the reaction conditions normally present when dehydrogenating a primary alcohol, and are therefore usually less suitable than Ebner et al.'s carbon supports. This vulnerability to attrition tends to also cause these supports to exhibit poor filtration characteristics.
Use of copper-containing and silver-containing catalysts in other types of oxidation reactions has also been reported. Applicants, however, are unaware of any such disclosures which address the problems associated with copper-containing or silver-containing catalysts in processes involving the dehydrogenation of primary alcohols to form carboxylic acid salts.
Bournonville et al. report forming a ketone by dehydrogenating a secondary alcohol using a Raney nickel catalyst containing 0.1 to 10% by weight of copper, silver, gold, tin, lead, zinc, cadmium, indium, or germanium. See Bournonville et al., U.S. Pat. No. 4,380,673. This reaction, however, does not form a carboxylic acid salt—forming a carboxylic acid salt would further require the cleavage of an alkyl group from the carbonyl group and the subsequent attachment of a hydroxy salt to the carbonyl group. In addition, Bournonville

Affiliated with

Also associated with

Rating

Process and catalyst for dehydrogenating primary alcohols to... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Process and catalyst for dehydrogenating primary alcohols to..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process and catalyst for dehydrogenating primary alcohols to... will most certainly appreciate the feedback.