sPS nanocomposite and processes for producing the same

Details sPS nanocomposite and processes for producing the same sPS nanocomposite and processes for producing the same

2000-07-14

2002-06-25

Kiliman, Leszek (Department: 1773)

Stock material or miscellaneous articles

Coated or structually defined flake, particle, cell, strand,...

Particulate matter

C428S403000, C428S404000, C428S522000, C523S202000, C523S209000, C523S210000, C523S211000

Reexamination Certificate

active

06410142

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates in general to a new nanocomposite material. More particularly, it relates to syndiotactic polystyrene (sPS) nanocomposites and processes for producing the same.
2. Description of the Related Arts
Nanocomposites are a new class of material containing minerals that exhibit ultra-fine phase dimensions, typically in the range 1-100 nm. Experimental work on these minerals has generally shown that virtually all types and classes of nanocomposites lead to new and improved properties such as increased stiffness, strength, and heat resistance, and decreased moisture absorption, flammability, and permeability, when compared to their micro- and macrocomposite counterparts. Specifically, commercially available Nylon 6/clay nanocomposite shows that the polymer matrix having layered clay minerals dispersed therein exhibits improved mechanical strength, heat distortion temperature (HDT), and impermeability to gas and water.
Syndiotactic polystyrene (sPS) was developed in 1986 by Ishihara using a metallocene catalyst composition. The syndiotactic polystyrene has a syndiotacticity of at least 90% and exhibits a very high melting point (270° C.). In addition, the syndiotactic polystyrene has the properties of low dielectric constant, low specific gravity, and excellent chemical resistance, which make it a suitable candidate for many engineering plastics applications.
In spite of a variety of sPS composites have been developed in order to broaden the range of its applications, those containing layered silicates dispersed at a nanoscale (i.e., sPS/clay nanocomposites) have never been reported. The present invention aims to provide such sPS nanocomposites.
As widely known to the art, the syndiotactic polystyrene suffers from the problem of having relatively lower crystallization rate, thus causing molding difficulties. A known method to raise the crystallization rate involves the use of nucleating agents and crystallizing aids. However, the improvement is not sufficient enough for some practical uses.
In consequence, it would be a significant improvement in the state of the art if sPS composites with improved mechanical and other properties could be prepared at a faster crystallization rate.
SUMMARY OF THE INVENTION
An object of the invention is to provide a new nanocomposite material and processes for producing the same.
Another object of the invention is to provide a sPS nanocomposite with high mechanical strength and a process for producing the same.
A further object of the invention is to provide a sPS nanocomposite with improved crystallization characteristics and a process for producing the same.
To attain the above objects, a layered clay material is modified with an organic onium cation by ion exchange and optionally together with a oligomer or polymer which is compatible or partially compatible with sPS, and the modified clay material is dispersed in a styrene monomer to undergo in-situ polymerization by using a metallocene catalyst, thus obtaining the modified clay material uniformly dispersed in sPS polymer matrix. Alternatively, the sPS nanocomposite can be obtained by directly blending (e.g., solution blending, melt blending) the modified clay material with a syndiotactic polystyrene. X-ray diffraction (XRD) analysis of the composite material thus obtained indicates delamination of the clay material in nano-scale.
In the nanocomposite of the present invention, the nano-dispersed clay material not only imparts mechanical reinforcement to the polymer matrix, but also, surprisingly, improves the crystallization properties of sPS significantly.
DETAILED DESCRIPTION OF THE INVENTION
The sPS/clay nanocomposite of this invention comprises a polymer matrix containing syndiotactic polystyrene (sPS), and a layered clay material uniformly dispersed in the polymer matrix, said layered clay material being intercalated with an organic onium cation, and the interlayer distances of said layered clay material being at least 20 Å. Optionally, the layered clay material may be intercalated with a polymer or oligomer which is compatible or partially compatible with sPS. The amount of the optionally intercalated polymer or oligomer is preferably in the range from 0.5 to 50 parts by weight per 100 parts by weight of the clay material.
The polymer matrix in the composite material of this invention is a resin containing sPS, namely, a sPS or a mixture thereof with other polymers. The molecular weight of the sPS to be used in the present invention is not specifically limited, but is preferably within the range from about of 15,000 to 800,000 in terms of weight-average molecular weight (M
w
).
The layers of clay material in the composite material of this invention, which are intended to impart the polymeric material with high mechanical strength, have a thickness of about 7 to 12 Å. Also, it has been found that the nano-dispersed clay material unexpectedly increases the crystallization rate and crystallization temperature of sPS. The greater the proportion of the clay material in the sPS matrix, the more marked the effects achieved.
The amount of the clay material dispersed in the composite material of this invention is preferably in the range from about 0.1 to 40 parts by weight per 100 parts by weight of the polymer matrix. If this amount is less than 0.1 parts, a sufficient reinforcing effect cannot be expected. If the amount exceeds 40 parts, on the other hand, the resulting product is powdery interlayer compound which cannot be used as moldings. In addition, it is also preferable that the composite material of this invention be such that the interlayer distance is at least 30 Å. The greater the interlayer distance is, the better the mechanical strength will be.
Next, the process for manufacturing composite material of this invention is described below.
The first step is to bring a cation-type surfactant into contact with a clay material having a cation-exchange capacity of about 50 to 200 meq/100 g, thereby adsorbing the surfactant on the clay material. This can be accomplished by immersing the clay material in an aqueous solution containing the surfactant, followed by washing the treated clay material with water to remove excess ions, thereby effecting ion-exchange operation.
The clay material used in this invention can be any clay material (both natural and synthesized) having a cation exchange capacity of about 50 to 200 meq/100 g. Typical examples include smectite clays (e.g., montmorillonite, saponite, beidellite, nontronite, hectorite, and stevensite), vermiculite, halloysite, sericite, and mica. With a clay material whose cation-exchange capacity exceeds 200 meg/100 g, its interlayer bonding force is too strong to give intended composite materials of this invention. If the capacity is less than 50 meq/100 g, on the other hand, ion exchange or adsorption of surfactant will not be sufficient, making it difficult to produce composite materials as intended by this invention.
The cation-type surfactant serves to expand the interlayer distance in a clay material, thus facilitating the formation of polymer between the silicate layers. The surfactants used in the present invention are organic compounds containing onium ions which-are capable of forming a firm chemical bond with silicates through ion-exchange reaction. Particularly preferred surfactants are ammonium salts containing at least 12 carbon atoms, such as n-hexadecyl trimethylammonium bromide and cetyl pyridinium chloride.
Optionally, the surface modified clay material may be intercalated with a polymer or oligomer, which is compatible or partially compatible with sPS, as a subsequent modification. For example, this can be accomplished by admixing the modified clay material with a styrene monomer or 2,6-xylenol monomer, and polymerizing the monomer to obtain atactic polystyrene (aPS) or poly(2,6-dimethyl-1,4-phenylenen oxide) (PPO) intercalated in the modified clay material, respectively.
The next step in the process of this invention is to mix a

Affiliated with

Also associated with

Rating

sPS nanocomposite and processes for producing the same does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with sPS nanocomposite and processes for producing the same, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and sPS nanocomposite and processes for producing the same will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2900843