Specialized metallurgical processes – compositions for use therei – Processes – Producing or treating free metal
Reexamination Certificate
2000-05-15
2002-04-02
Andrews, Melvyn (Department: 1742)
Specialized metallurgical processes, compositions for use therei
Processes
Producing or treating free metal
C075S500000
Reexamination Certificate
active
06364929
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The invention relates to a method for processing steel slags and iron carriers such as, e.g., electric furnace slags, converter slags, fine ores, dusts obtained from the production of and, millscale, for recovering pig iron and environmentally safe slags.
2. Description of Related Art
From WO 96/24696 a method for producing pig iron or steel and cement clinker from slags has become known, in which iron- oxide-containing molten slags such as, for instance, steel making slag was mixed with iron oxide carriers and lime, whereupon a ferritic slag was formed. After this, the ferritic slag was reduced in a reduction reactor while forming an iron bath and a sinter phase upon combustion of carbon, whereupon the sinter phase was discharged as a clinker.
Slags have a relatively low thermal conductivity and a heat capacity exceeding that of iron by about 1.5 to 2 times. Essential to the economy of such a method is the heat transfer or so-called post-combustion degree that is obtainable. The post-combustion degree is defined as follows:
Post
-
combustion
degree
=
CO
2
+
H
2
O
CO
+
CO
2
+
H
2
+
H
2
O
gaseous
phase
So far, only insufficient post-combustion degrees have been ensured by the known modes of procedure. Also the
heat
tranfer
=
1
-
H
g
-
H
b
H
pc
H
g
…
gas
enthalpy
(
at
gas
temperature
)
H
b
…
gas
enthalpy
(
at
melting
temperature
)
H
pc
…
combustion
enthalpy
(
at
melting
temperature
)
does not suffice for an economic mode of operation in the known modes of procedure.
Thermal efficiencies of far more than 70% are achieved neither in conventional blast furnace technologies nor in other processes such as, for instance, fluidized bed processes. Thus, it has already been known to blow into a fluidized bed, together with coal, prereduced and at least partially preheated charges, wherein coal is gasified in a fluidized bed while reducing the charge and sponge iron is melted and drawn off. To make things worse, such meltdown gasification reactions, generally, are optimizied with a view to the pig iron output desired such that no environmentally safe slag will be formed.
In earlier proposals made by the Applicant, methods of the initially defined kind for recovering pig iron and environmentally safe slags have already been described, in which a molten slag bath and a molten iron bath are used at a volume ratio of between 0.5:1 and 1.5:1 and carbon carriers are introduced into the bath while top-blowing hot air.
In addition to the processing of steel slags such as, for instance, electric furnace slags, the known methods, above all, aimed at processing converter slags and also oxygen was blown into the bath, if only facultatively. Compared to electric furnace slags, converter slags and, in particular, LD slags are characterized by a substantially higher basicity CaO/SiO
2
of usually more than 3, whereas electric furnace slags have a slightly lower basicity. Considering the various options discussed in earlier proposals, the realization of the method in a converter was the primary objective, thus using a more or less complex blowing technology. Yet, in principle, that earlier method was, of course, suitable also for use in furnaces or ladles.
SUMMARY OF THE INVENTION
The present invention aims to improve the known methods for. use primarily with electric furnace slags and, at the same time, to get by with less apparative expenditure than according to the earlier proposals. To solve this object, the method of the initially defined kind essentially resides in that a mixed slag having a basicity CaO/SiO
2
of between 1.2 and 2.5 is adjusted from the starting slags and iron carriers and the mixed slag is transferred into a hearth-type furnace or a ladle, that hot air is top-blown for afterburning at a post-combustion degree PC=(CO
2
+H
2
O)/CO+CO
2
+H
2
+H
2
O) of between 0.70 and 0.85 the CO formed from the carbon in the bath, and that the hot offgases from the furnace or the ladle are drawn off tangentially to the axis of the mouth of the hot air feeding lance. The use of furnaces or ladles enables the application of substantially more cost-effective devices in which also the refractory lining element of costs is substantially reduced. Taking into account that, in the instant case, a higher wear of refractory materials may be put up with without excessive investment costs, a substantially higher basicity of up to 2.5 is, thus, regarded as admissible in the method according to the invention such that, in particular, electric furnace slags may be employed directly without a lime batch or a remarkable lowering of the basicity. At the same time, it is, however, also feasible in the context of an electric steel making plant to ensure the perfect control of the waste streams occurring in electric steel making plants. There, besides electric furnace slag also ladle slags, dusts, millscale and furnace break-off material occur as waste substances, which may be disposed of or utilized immediately by the method according to the invention, whereby a favorably priced molten pig iron substantially free of trace elements will be obtained at the same time. In the method according to the invention by increasing post-combustion to values of between 0.7 and 0.85 and, in particular, values of around 0.8, the control of the method according to the invention has been substantially facilitated. It is merely required to care for the adequate supply of carbon into the bath and ensure the appropriate blending of the slag with the bath and subsequently afterburn the CO dissolved in the slag by the aid of hot air impinging at a high speed. Blowing oxygen or hot air into or through the bath may be obviated completely such that the apparative expenditure can be considerably reduced. Carbon basically may be fed via simple lances or via bottom tuyeres, which does not imply a substantial increase in the costs for the ladle or the furnace. Yet, also carbon may be blown into the bath through submerged lances. In a particularly advantageous manner, carbon also may be top-charged directly onto the melt bath in a coarse grained form, using a bottom-stirred ladle. What is, however, also essential to the efficiency of post-combustion, and hence the high heat transfer and the obviation of additional heating of the furnace or the ladle by the aid of external heating means, is the evacuation of the hot furnace offgases proposed by the invention. According to the invention, this evacuation is to be effected tangentially to the axis of the mouth of the hot air feeding lance. Such a gas flow control renders feasible to not only safely obtain the desired post-combustion degree, but also ensure the desired heat transfer such that a number of waste materials from electric steel making plants as initially described can be disposed of or utilized in a cost-effective manner.
Advantageously, the method according to the invention is carried out in a manner that the offgases drawn off are supplemented with additives selected from the group consisting of fine ores, dusts, millscale and optionally additional fuel in a further, external post-combustion course and the heated solids are blown onto the slag together with the hot air. In said post-combustion course, also waste streams from an electric steel making plant may obviously be melted at least partially, wherein, due to the adjustment of a post-combustion degree of between 0.7 and 0.85 within the furnace or ladle, sufficient chemical energy will still be contained in the offgases in order to ensure such an effective afterburning outside the furnace or ladle. After this, or alternatively, it may, however,
"Holderbank" Financiere Glarus AG
Andrews Melvyn
Joyce Kevin E.
LandOfFree
Method for reprocessing steel slags and ferriferous materials does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Method for reprocessing steel slags and ferriferous materials, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for reprocessing steel slags and ferriferous materials will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2881123