Metal fusion bonding – Process – Plural joints
Reexamination Certificate
2000-01-24
2002-09-03
Dunn, Tom (Department: 1775)
Metal fusion bonding
Process
Plural joints
C228S196000
Reexamination Certificate
active
06443354
ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to a process for the production of a composite component that can resist high thermal stress. The composite comprises at least one graphite part and at least one metal part made of a hardenable copper alloy, which is surface-bonded to the graphite part.
As a result of its special characteristics, such as high thermal stress capacity, good thermal conductivity, and low pulverization rate, graphite is very suitable for structural parts that are under strong thermal stress. Graphite is used in very different forms, such as polycrystalline graphite, pyrolytic graphite, or even fiber-reinforced graphite. A disadvantage of graphite is that it has only limited mechanical strength and ductility in the fiber-reinforced form. Moreover, because of leakage, the porosity of the graphite generally prohibits direct contact with liquids, such as is necessary for sufficient dissipation of heat with actively cooled thermal shields. Therefore, as a rule, the situation is such that for structural parts under high thermal stress, graphite is not generally used alone, but rather in combination with metal parts, which serve as carriers that can withstand mechanical stress and with actively cooled structural parts, also for the conduction of the used cooling media. A good high temperature-resistant bonding of graphite parts with metal parts, which generally is brought about by a high-temperature soldering, is therefore important.
Generally, metal parts bonded with graphite should have thermal expansion coefficients similar to those of graphite, in order to avoid thermal stresses of the composite structural part and moreover, to retain the strength values required at high temperature for the maintenance of sufficient stability. If the composite structural parts are used in fusion reactors, good stress capacity under neutron stress is also of importance.
Molybdenum has proven to be a good material for the metal parts. An actively cooled cooling device, in which one or more parts of graphite are bonded with cooling agent conduits made of molybdenum, is described, for example, in DE 34 16 843 A1. The disadvantage of such composite structural parts which use molybdenum as a material for the metal parts are the relatively high costs and the difficulty in processing and welding molybdenum. Therefore, an attempt has been made to replace molybdenum with other high temperature-resistant metals, for example, high-strength copper alloys. Such a copper alloy, which exhibits practically no structural conversion up to the melting point and thus retains its good high-temperature characteristics, is, for example, a dispersion-reinforced copper alloy, with fine Al
2
O
3
dispersoids embedded in a copper matrix.
This alloy can be soldered also with high-temperature solders at approximately 900° C., without disadvantageous effects on its mechanical characteristics, so that parts made of this alloy can be bonded with parts made of graphite.
One disadvantage of this copper alloy is that its fracture toughness drops below a critical minimum with neutron stress, so that it is suitable, in only a qualified manner, for structural parts which are to be used in fusion reactors.
Other known copper alloys which have optimal high-temperature strength characteristics are hardenable copper-chromium-zirconium alloys made of approximately 0.3-1.2 wt % chromium, 0.03-0.3 wt % zirconium, and the remainder, copper.
In comparison to dispersion-reinforced copper alloys, these alloys have, above all, substantially better values for fracture toughness after neutron stress, so that they are basically very suitable for structural parts used in fusion reactors.
Copper-chromium-zirconium alloys are hardenable alloys that attain their good characteristics with respect to strength and elongation by a special process during production and by a final hardening cycle at approximately 500° C. In order to retain these good characteristics in the hardened state, these alloys should not exceed the hardening temperature of 500° C. in further processing, in particular, during the bonding with the parts made of graphite or in use, since otherwise, fatigue of the alloy occurs and strength values rapidly decline.
Thus, the known high-temperature soldering for the bonding of parts made of this alloy with graphite parts is practically out of the question. One possibility of bonding graphite with parts made of high-strength copper alloys, among others also, made of copper-chromium-zirconium alloys, without damaging the rigidity of the composite structural parts by the bonding process, is the use of electron beam welding, as it is described, for example, in EP 0 741 116 A1. One disadvantage of that process is that it is only suitable for parts made of copper-chromium-zirconium alloys having a relatively large wall thickness. In the case of structural parts with thin walls, the heat, which appears during the electron beam welding and is, in fact, relatively low, is still too great to rule out a decline in the good mechanical characteristics of the copper-chromium-zirconium alloy. Moreover, especially with more complex structural parts, for example, with actively cooled installations, where several graphite parts must be bonded in several planes with cooling agent conduits, electron beam welding cannot be used frequently because of an insufficient accessibility of the surfaces to be bonded.
OBJECT OF THE INVENTION
The object of the present invention is to create a process for the production of a composite structural part having a high thermal stress capacity, which can be used even with thin-wall parts made of copper-chromium-zirconium alloys, or with more complex composite structural part constructions, without the good mechanical characteristics of the copper-chromium-zirconium alloy in the hardened state being destroyed.
SUMMARY OF THE INVENTION
In accordance with the invention, these objectives are obtained by employing the HIP (hot isostatic press processes) process to bond a metal part with a graphite part wherein a layer of copper or of a copper alloy is provided on the bonding surface.
DETAILED DESCRIPTION OF THE INVENTION
With the known HIP processes for the bonding of different materials, temperatures are usually used which are at least 70% of the melting point of the lower-melting partner to be joined. Simultaneously, high pressures in the range of clearly over 1000 bar are applied, so as to attain sufficient bonding of the individual partners to be joined. Since the use of such high pressures might destroy graphite materials, the use of HIP processes for the bonding of different parts has been limited up to now to only metal partners to be joined. It was a complete surprise when it became evident that by the preparation of a layer of copper or a copper alloy on the bonding surface of the graphite to the metal part, a HIP process can be successfully used to bond different parts even with the use of temperatures and pressures which are clearly lower than were previously common, and the process is therefore suitable for bonding of graphite parts with heat-sensitive, high-strength copper alloys in excellent quality. The layer made of copper or a copper alloy can thereby be presented, in different ways, between the surfaces to be bonded for the partners to be joined. For example, it is conceivable to bond the graphite part with the copper layer before the HIP process, or to place the copper in the form of a thin film between the surfaces to be bonded before the introduction of the HIP process.
In a particularly advantageous embodiment of the process, an alloy with approximately 0.3-1.2 wt % chromium, 0.03-0.3 wt % zirconium, and the remainder, copper, is used as a hardenable copper alloy. When using this alloy, particularly good mechanical characteristics are attained with high-temperature stress even after neutron stress, which are not impaired by using the HIP process to bond with the graphite part, so that such structural parts are particularly suitable for use in fusion reactors.
What has proven
Plochl Laurenz
Schedler Bertram
Johnson Jonathan
Morgan & Finnegan L.L.P.
Plansee Aktiengesellschaft
LandOfFree
Process for the production of a composite component that can... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for the production of a composite component that can..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for the production of a composite component that can... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2835742