Lithium metal fluorophosphate materials and preparation thereof

Chemistry: electrical current producing apparatus – product – and – Current producing cell – elements – subcombinations and... – Electrode

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C429S231100

Reexamination Certificate

active

06387568

ABSTRACT:

FIELD OF THE INVENTION
This invention relates to improved materials usable as electrode active materials, and electrodes formed from it for electrochemical cells in batteries.
BACKGROUND OF THE INVENTION
Lithium batteries are prepared from one or more lithium electrochemical cells containing electrochemically active (electroactive) materials. Such cells typically include an anode (negative electrode), a cathode (positive electrode), and an electrolyte interposed between spaced apart positive and negative electrodes. Batteries with anodes of metallic lithium and containing metal chalcogenide cathode active material are known. The electrolyte typically comprises a salt of lithium dissolved in one or more solvents, typically nonaqueous (aprotic) organic solvents. Other electrolytes are solid electrolytes typically called polymeric matrixes that contain an ionic conductive medium, typically a metallic powder or salt, in combination with a polymer that itself may be ionically conductive which is electrically insulating. By convention, during discharge of the cell, the negative electrode of the cell is defined as the anode. Cells having a metallic lithium anode and metal chalcogenide cathode are charged in an initial condition. During discharge, lithium ions from the metallic anode pass through the liquid electrolyte to the electrochemically active (electroactive) material of the cathode whereupon they release electrical energy to an external circuit.
It has recently been suggested to replace the lithium metal anode with an insertion anode, such as a lithium metal chalcogenide or lithium metal oxide. Carbon anodes, such as coke and graphite, are also insertion materials. Such negative electrodes are used with lithium- containing insertion cathodes, in order to form an electroactive couple in a cell. Such cells, in an initial condition, are not charged. In order to be used to deliver electrochemical energy, such cells must be charged in order to transfer lithium to the anode from the lithium- containing cathode. During discharge the lithium is transferred from the anode back to the cathode. During a subsequent recharge, the lithium is transferred back to the anode where it reinserts. Upon subsequent charge and discharge, the lithium ions (Li
+
) are transported between the electrodes. Such rechargeable batteries, having no free metallic species are called rechargeable ion batteries or rocking chair batteries. See U.S. Pat. Nos. 5,418,090; 4,464,447; 4,194,062; and 5,130,211.
Preferred positive electrode active materials include LicoO
2
, LiMn
2
O
4
, and LiNiO
2
. The cobalt compounds are relatively expensive and the nickel compounds are difficult to synthesize. A relatively economical positive electrode is LiMn
2
O
4
, for which methods of synthesis are known. The lithium cobalt oxide (LiCoO
2
), the lithium manganese oxide (LiMn
2
O
4
), and the lithium nickel oxide (LiNiO
2
) all have a common disadvantage in that the charge capacity of a cell comprising such cathodes suffers a significant loss in capacity. That is, the initial capacity available (amp hours/gram) from LiMn
2
O
4
, LiNiO
2
, and LicoO
2
is less than the theoretical capacity because significantly less than 1 atomic unit of lithium engages in the electrochemical reaction. Such an initial capacity value is significantly diminished during the first cycle operation and such capacity further diminishes on every successive cycle of operation. For LiNiO
2
and LiCoO
2
only about 0.5 atomic units of lithium is reversibly cycled during cell operation. Many attempts have been made to reduce capacity fading, for example, as described in U.S. Pat. No. 4,828,834 by Nagaura et al. However, the presently known and commonly used, alkali transition metal oxide compounds suffer from relatively low capacity. Therefore, there remains the difficulty of obtaining a lithium-containing electrode material having acceptable capacity without disadvantage of significant capacity loss when used in a cell.
SUMMARY OF THE INVENTION
The invention provides novel lithium-metal-fluorophosphate materials which, upon electrochemical interaction, release lithium ions, and are capable of reversibly cycling lithium ions. The invention provides a rechargeable lithium battery which comprises an electrode formed from the novel lithium-metal-fluorophosphates. Methods for making the novel lithium-metal-fluorophosphates and methods for using such lithium-metal-fluorophosphates in electrochemical cells are also provided. Accordingly, the invention provides a rechargeable lithium battery which comprises an electrolyte; a first electrode having a compatible active material; and a second electrode comprising the novel lithium-metal-fluorophosphate materials. The novel materials, preferably used as a positive electrode active material, reversibly cycle lithium ions with the compatible negative electrode active material. Desirably, the lithium-metal-fluorophosphate is represented by the nominal general formula LiM
1−y
MI
y
PO
4
F where 0≦y≦1. Such compounds include LiMPO
4
F for y=0. Such compounds are also represented by Li
1−x
MPO
4
F and Li
1−x
M
1−y
MI
y
PO
4
F, where in an initial condition, “x” is essentially zero; and during cycling a quantity of “x” lithium is released where 0≦x≦1. Correspondingly, M has more than one oxidation state in the lithium-metal-fluorophosphate compound, and more than one oxidation state above the ground state M
0
. The term oxidation state and valence state are used in the art interchangeably. Also, MI may have more than one oxidation state, and more than one oxidation state above the ground state MI°.
Desirably, M is selected from V (vanadium), Cr (chromium), Fe (iron), Ti (titanium), Mn (manganese), Co (cobalt), Ni (nickel), Nb (niobium), Mo (molybdenum), Ru (ruthenium), Rh (rhodium) and mixtures thereof. Preferably, M is selected from the group V, Cr, Fe, Ti, Mn, Co, and Ni. As can be seen, M is preferably selected from the first row of transition metals, and M preferably initially has a +3 oxidation state. In another preferred aspect, M is a metal having a +3 oxidation state and having more than one oxidation state, and is oxidizable from its oxidation state in lithium-metal-fluorophosphate compound. In another aspect, MI is a metal having a +3 oxidation state, and desirably MI is an element selected from the group V, Cr, Fe, Ti, Mn, Co, Ni, Nb, Mo, Ru, Rh, B (boron) and Al (aluminum).
In a preferred aspect, the product LiM
1−y
MI
y
PO
4
F is a triclinic structure. In another aspect, the “nominal general formula” refers to the fact that the relative proportions of the atomic species may vary slightly on the order of up to 5 percent, or more typically, 1 percent to 3 percent. In another aspect the term “general” refers to the family of compounds with M, MI, and y representing variations therein. The expressions y and 1−y signify that the relative amount of M and MI may vary and that 0≦y≦1. In addition, M may be a mixture of metals meeting the earlier stated criteria for M. In addition, MI may be a mixture of elements meeting the earlier stated criteria for MI.
The active material of the counter electrode is any material compatible with the lithium-metal-fluorophosphate of the invention. Where the lithium-metal-fluorophosphate is used as a positive electrode active material, metallic lithium may be used as the negative electrode active material where lithium is removed and added to the metallic negative electrode during use of the cell. The negative electrode is desirably a nonmetallic insertion compound. Desirably, the negative electrode comprises an active material from the group consisting of metal oxide, particularly transition metal oxide, metal chalcogenide, carbon, graphite, and mixtures thereof. It is preferred that the anode active material comprises a carbonaceous material such as graphite. The lithium-metal-fluorophosphate of the invention may also be used as a negative electrode material.
The starting (precursor) materials include a lit

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Lithium metal fluorophosphate materials and preparation thereof does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Lithium metal fluorophosphate materials and preparation thereof, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Lithium metal fluorophosphate materials and preparation thereof will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2829988

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.