Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Mixing of two or more solid polymers; mixing of solid...
Reexamination Certificate
1993-10-29
2001-08-14
Woodward, Michael P. (Department: 1631)
Synthetic resins or natural rubbers -- part of the class 520 ser
Synthetic resins
Mixing of two or more solid polymers; mixing of solid...
C525S240000
Reexamination Certificate
active
06274675
ABSTRACT:
BACKGROUND OF THE INVENTION
Closed loop recycling, (i.e. recycling materials for use in their original application) is not a viable alternative for post consumer, high density polyethylene, milk container resins due to, in part, the inability of of these resins to meet FDA regulations for food contact applications. A logical use for post consumer, high density polyethylene, milk container resins is in containers for household and industrial chemicals. However, the physical requirements for these types of containers are much greater than the physical requirements for high density polyethylene, milk container resins. Consequently, solutions to this problem should be found.
Currently, the typical approach is to blend non-virgin resin with a high performance virgin resin. This usually results in a blend with intermediate physical properties. The drawback is that the broadening of the molecular weight distribution resulting from blending these two resins increases the die swell of the blend beyond the desired range.
SUMMARY OF THE INVENTION
It is an object of this invention to provide a process that produces a multicomponent ethylene polymer composition.
It is another object of of this invention to provide a process that produces a multicomponent ethylene polymer composition that is useful in making household and industrial containers.
In accordance with this invention a process to produce a multicomponent ethylene polymer composition is provided. This process comprises: contacting an organic peroxide with at least one post consumer, ethylene polymer resin that has a density from about 0.95 to 0.97 grams per cubic centimeter and a melt index from about 0.3 to about 1 gram per ten minutes; and thereafter blending the above composition with at least one virgin ethylene polymer resin that has a density from about 0.93 to 0.945 grams per cubic centimeter and a melt index from about 0.01 to about 0.16 grams per ten minutes; to form said multicomponent ethylene polymer composition.
These and other objects, features, aspects, and advantages of this invention will become better understood with reference to the following detailed description of the invention and the claims.
DETAILED DESCRIPTION OF THE INVENTION
In general, the multicomponent ethylene polymer compositions of this invention comprise a post consumer, ethylene polymer resin and a virgin ethylene polymer resin.
The post consumer ethylene polymer resins used in this invention have a melt index from about 0.3 to about 1 gram per ten minutes. Preferably, the melt index is from about 0.4 to about 0.9 grams per ten minutes and most preferably from 0.5 to 0.8 grams per ten minutes. If the melt index is substantially below 0.3 grams per ten minutes the resulting resin will exhibit poor processability. If the melt index is substantially more than 1 gram per 10 minutes the environmental stress crack resistance of the resulting blend could be lower than desired. The melt index is determined in accordance with ASTM D-1238.
The post consumer ethylene polymer resins used in this invention have a density from about 0.95 to about 0.97 grams per cubic centimeter. Preferably, the density is from about 0.955 to about 0.965 grams per cubic centimeter. If the density is substantially below 0.95 grams per cubic centimeter then the stiffness of the resulting blend will be too low. The density is determined in accordance with ASTM D-1505.
The virgin ethylene polymer resins used in this invention have a melt index from about 0.01 to about 0.16 grams per ten minutes. Preferably, the melt index is from about 0.05 to about 0.16 grams per ten minutes and most preferably from 0.08 to 0.16 grams per ten minutes. If the melt index is substantially below 0.01 grams per ten minutes the resulting resin will exhibit poor processability. If the melt index is substantially more than 0.16 grams per 10 minutes the environmental stress crack resistance of the resulting blend could be lower than desired.
The virgin ethylene polymer resins used in this invention have a density from about 0.93 to about 0.945 grams per cubic centimeter. Preferably, the density is from about 0.935 to about 0.945 grams per cubic centimeter and most preferably from 0.936 to 0.940 grams per cubic centimeter. If the density is substantially below 0.93 grams per cubic centimeter then the stiffness of the resulting blend could be too low.
If the density is substantially more than 0.945 grams per cubic centimeter the environmental stress crack resistance of the resulting blend could be too low.
The post consumer ethylene polymer resins and the virgin ethylene polymer resins used in this invention can be made by any manner known in the art.
The post consumer ethylene polymer resin is contacted with an organic peroxide before the post consumer ethylene polymer resin is blended with the virgin ethylene polymer resin to produce the multicomponent ethylene polymer composition.
The organic peroxides useful in this invention are those that have decomposition temperatures from about 300 to about 600 degrees Fahrenheit. Preferably, the decomposition temperature is from about 350 to 500 degrees Fahrenheit and most preferably from 400 to 450 degrees Fahrenheit. If the decomposition temperature is substantially less than about 300 degrees Fahrenheit then inadequate crosslinking will occur, resulting in inferior physical and processing properties in the resulting blend. If the decomposition temperature is substantially greater than 600 degrees Fahrenheit then peroxide decomposition will be too rapid to allow efficient crosslinking and the properties of the resulting blend will be inferior. Suitable examples of such organic peroxides are 2,5-dimethyl-1,5-bis(t-butylperoxy) hexane, di-tert-butylperoxide, 2,5-dimethyl-2,5-bis(t-butylperoxy) hexyne-3.
The post consumer ethylene polymer resin can be contacted with the organic peroxide in any manner known in the art. One suitable method for contacting the resin and the organic peroxide is extruding these compounds together. The temperature of the extruder can be from about 300 to about 600 degrees Fahrenheit. Preferably, the extruder's temperature is from about 350 to 500 degrees Fahrenheit and most preferably from 400 to 450 degrees Fahrenheit. If the extruder's temperature is substantially less than about 300 degrees Fahrenheit then the crosslinking reaction will not occur during the resin's residence time in the extruder. If the extruder's temperature is substantially greater than 600 degrees Fahrenheit then the crosslinking reaction will occur too quickly, thereby making flow through the extruder more difficult.
It should be noted that the temperature in the extruder should be substantially the same as the decomposition temperature of the organic peroxide. Preferably, the temperature of the extruder should be within about 20 degrees Fahrenheit of the decomposition temperature of the organic peroxide. However, it is most preferred if the residence time of the resin in the extruder is at least about three times the ½ life of the peroxide at the decomposition temperature.
The amount of organic peroxide to contact with the post consumer ethylene polymer resin is from about 1 to about 1000 parts per million by weight based on the weight of the post consumer ethylene polymer resin. Preferably, from about 10 to about 500 parts per million and most preferably from 20 to 200 parts per million are used in this application.
The post consumer ethylene polymer resin should be contacted with the organic peroxide for a time period and temperature sufficient to cause the decomposition of substantially all of the organic peroxide. Preferably, less than 10 weight percent of the organic peroxide is left after this contacting procedure and more preferably less than 5 weight percent is left.
After the post consumer ethylene polymer resin is contacted with the organic peroxide, it is then blended with the virgin ethylene polymer resin. This blending can be accomplished by any manner known in the art. One suitable method for blending these resins is by ext
DePorter JoEllen
Fodor Lawrence M.
Bowman Edward L.
Phillips Petroleum Company
Woodward Michael P.
LandOfFree
Process to produce a multicomponent ethylene polymer... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process to produce a multicomponent ethylene polymer..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process to produce a multicomponent ethylene polymer... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2548529