Stock material or miscellaneous articles – Coated or structually defined flake – particle – cell – strand,... – Rod – strand – filament or fiber
Reexamination Certificate
1999-07-29
2001-07-03
Edwards, N. (Department: 1774)
Stock material or miscellaneous articles
Coated or structually defined flake, particle, cell, strand,...
Rod, strand, filament or fiber
C428S370000
Reexamination Certificate
active
06254987
ABSTRACT:
DESCRIPTION
The invention relates to monofils in the form of bicomponent (conjugate) fibres of the sheath/core type which surround a core containing a liquid-crystalline polymer; it also relates to their manufacture and use, especially in the production of paper machine clothing and paper machine fabrics.
A monofil as defined in this invention means a continuous yarn consisting of a single continuous fibre made with or without twist and having a diameter of at least 0.01 mm, preferably 0.08 mm, and in particular 0.1. mm and more. It differs, especially by its considerably larger diameter, from monofilaments in the form of sheath/core fibres which are commonly made for textile purposes.
Monofils are used primarily in the manufacture of technical articles and in particular surface structures with technical applications, contrary to multifilament yarns which are constructed of fine individual filaments for use mainly in the textile industry.
Monofils in the form of bicomponent fibres of the sheath/core type are known in prior art and have been described, for example, in EP 0 763 611 A1. There, the core component is a polyester, while the sheath is a polyamide. The polyester of the core can also be a liquid crystalline polymer. To improve adhesion between the core and the sheath components, the sheath contains an adhesion-promoting polymer.
In spite of an adhesion-promoting means, adhesion still leaves something to be desired, which means that especially under strong mechanical loads, the core is at least partly separated from the sheath component, which has a negative effect on the mechanical properties of the product made from such monofils. Their strength characteristics could be improved as well.
Japanese patent application JP-07/097,719-A teaches the manufacture of multi-component fibres of the sheath/core type, whose core consists of an aromatic polyester and whose sheath contains a semi-aromatic polyamide. The abstract of this Japanese application does not include notes for manufacturing monofils, and in that case, too, adhesion between core and sheath leaves something to be desired.
Finally, Japanese patent application JP-07/243,128 describes a sheath/core type filament that contains a liquid-crystalline polyester core and a sheath of thermoplastic polymer. This thermoplastic polymer of the sheath forms a so-called sea component and contains an anisotropic aromatic polyester as so-called island components. This means that the sheath is made of a matrix of a thermoplastic polymer in which large inclusions are embedded which are not compatible with the matrix.
Although a number of monofils of the sheath/core type are already known whose core contains a liquid-crystalline polymer, there is still a demand for improved monofils of this type.
It is therefore the object of the present invention to make available monofils. in the form of bicomponent fibres of the sheath/core type which comprise a core containing a liquid-crystalline polymer and a sheath enclosing this core in which cohesion between core and sheath components is very good, which are not prone to fibrillation, have a very high degree of abrasion resistance and good strength characteristics, and whose sheath provides excellent protection for the core.
A monofilament which displays enhanced abrasion resistance is provided having a diameter of at least 0.01 mm and the sheath is formed by the melt extrusion of a substantially homogeneous blend of 1 to 5 percent by weight polycarbonate and a polyester selected from the group consisting of polyethylene terephthalate, polypropylene terephthalate, polybutylene terephthalate, polyethylene-2,6-naphthalate, poly(1,
4
-bis(hydroxymethyl)-cyclohexaneterephthalate, and mixtures of the foregoing.
The monofils according to the invention can be manufactured, for example, in the following manner:
Core and sheath components are molten separately in extruders and spun in a bicomponent spin pack using a one-step process. After leaving the spinneret, the issuing monofils below the spinneret are cooled in a shaft, for example with a tempered gas stream. It is also possible to cool the fibres by means of a liquid. In that case, the strands are cooled down to a temperature which is preferably at least 0 to 30° C. below that of vitrification of the sheath material. The spray speed and the doffing (the so-called spin speed) are adjusted to each other until a draft of at least 1:5 to 1:30, preferably 1:8 to 1:15, is achieved.
Since the spin draft and also the quenching process can already be used to determine the final characteristics of the monofils, neither subsequent stretching nor thermal fixing are necessary to allow for shrinkage. Subsequent stretching is not necessary either. By adjusting the drawing conditions, it is possible to provide the monofils with a partial orientation, which means that purely amorphous as well as partly crystalline states can be achieved.
In general, the monofils are wound in a roll after they are drawn off.
It is possible to temper the monofils in an additional step. It has been proven advantageous when tempering is performed within a certain temperature range. Thus, it is possible to begin tempering at 200° C. and then to increase the temperature continuously to 270° C., for example. Of course, the tempering conditions depend especially on the sheath material used. The maximum temperature should lie 20 to 30° C. below the melting temperature of the sheath polymer.
The core can make up 40 to 90 percent of the cross-sectional area and the sheath can make up 10 to 60 percent of the cross-sectional area. The core can be arranged centrally or asymmetrically. The monofilament cross-section can be oval, rectangular or n-sided where n≧3.
A customary liquid-crystalline polymer can be used as the core component. A single polymer can be used, but it is also possible to use a mixture of several liquid-crystalline polymers. Such a mixture should be spun in a form that is as homogeneous as possible. Instead of using mixtures of pure liquid-crystalline polymers, it is also possible to use mixtures of one or more liquid-crystalline and one or more non-liquid-crystalline polymers.
Preferred as liquid-crystalline polymers are polycondensation products on the basis of p-hydroxybenzoic acid and 2,6-hydroxynaphthoic acid, especially those synthesized of 70 to 80, preferably 72 to 74 mol % of p-hydroxybenzoic acid and 20-30, preferably 26 to 29 mol % 2,6-hydroxynaphthoic acid.
Sheath components to be used can be customary polyesters such as polyethylene-terephthalate, polypropyleneterephthalate, polybutyleneterephthalate, but also polyethylene-2,6-naphthalate or poly-(1,4-bis(hydroxymethyl)-cyclohexaneterephthalate.
These polyesters can be used alone or as mixtures.
Another polymer suitable for the sheath are polycarbonates. These are commercially available; the product sold under the trade name of Makrolon has been very successful. In terms of the invention, polycarbonates are especially suitable as sheath components when mixed with other polyesters.
In a particularly advantageous embodiment of the invention, the sheath contains one or more elastomeric polyesters. These are in particular copolyesters on the basis of dicarboxylic acid such as terephthalic acid or its derivatives and a diol such as 1,4-butane diol or ethylene glycol and a polyglycol, especially for example polyglycol on the basis of tetrahydrofuran.
Preferred is polytetrahydrofuran butylenterephthalate. This elastomeric polyester can be synthesized, for example, by polycondensation of dimethylterephthalate, butane diol and polytetrahydrofuran of the formula HI(CH
2
CH
2
CH
2
CH
2
O)
n
H.
In this formula, n is a mean and can assume various values, with corresponding molecular weights which are advantageous in the range of about 600 to 2000, and especially at a magnitude of 1000. A mean molecular weight of about 1000 corresponds to a mean of 17 for n.
The sheath of the monofil bicomponent fibre should be substantially homogeneous, i.e. have no macroscopically discernible heterogeneous structure as, for example, a
Burns Doane Swecker & Mathis L.L.P.
Edwards N.
Johns Manville International Inc.
LandOfFree
Monofil bicomponent fibres of the sheath/core type does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Monofil bicomponent fibres of the sheath/core type, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Monofil bicomponent fibres of the sheath/core type will most certainly appreciate the feedback.