Method for fabricating fiber-reinforced slag gypsum cement-based

Details Method for fabricating fiber-reinforced slag gypsum cement-based Method for fabricating fiber-reinforced slag gypsum cement-based

1994-03-24

1994-11-22

Group, Karl

Compositions: coating or plastic

Coating or plastic compositions

Inorganic settable ingredient containing

106695, 106711, 106723, 106782, 106789, 264333, C04B 714

Patent

active

053665490

ABSTRACT:
A method is provided for making a fiber-reinforced slag gypsum cement lightweight hardened product. The method consists essentially of mixing (1) from 5 to 140 parts by weight of aggregates having a maximum size of not larger than 2000 .mu.m to (2) 100 parts by weight of a mixture which comprises 100 parts by weight of Portland cement, (3) from 20 to 350 parts by weight of slag fine powder which has a fineness ranging from 6,000 to 12,000 cm.sup.2 /g as Blaine's specific surface area, (4) from 0 to 20 parts by weight of lime, (5) from 20 to 100 parts by weight of calcium aluminate and gypsum fine powder, (6) 0.01 to 1.5 parts of a setting retardant; mixing water, prefoamed foams and reinforcing fibers with the mixture to obtain a slurry; subjecting the slurry to molding to obtain a molded product; removing the molded product to obtain a hardened product; and curing the hardened product with steam. In the method of the invention, the slurry sets and hardens within a short time, permitting the hardened product to be immediately removed from a mold.

REFERENCES:
patent: 1995540 (1935-03-01), Harrison
patent: 2880100 (1959-03-01), Ulfstedt
patent: 4146402 (1979-03-01), Kira et al.
patent: 4157263 (1979-06-01), Gaines et al.
patent: 4166749 (1979-09-01), Sterrett et al.
patent: 4187118 (1980-02-01), Nakagawa et al.
patent: 4229393 (1980-10-01), Wesche et al.
patent: 4266980 (1981-05-01), Chudo et al.
patent: 5030289 (1991-07-01), Sattler et al.
patent: 5108679 (1992-04-01), Rirsch et al.
Design and Control of Concrete Mixtures, Portland Cement Association, 1988, pp. 30, 31, 53-57 and 70.
Chemical Abstract--"Lightweight Inorganic Hardened Product" Mireshita et al. JP 54116023 (Sep. 10, 1979) Japan Matsushita Electric Works Ltd.

Affiliated with

Also associated with

Rating

Method for fabricating fiber-reinforced slag gypsum cement-based does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Method for fabricating fiber-reinforced slag gypsum cement-based, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Method for fabricating fiber-reinforced slag gypsum cement-based will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-1988672