DESCRIPTION:
BRIEF SUMMARY
This application is the national phase entry, under 35 USC .sctn.371, of International Application No. PCT/JP95/00708, filed Apr. 11, 1995.
FIELD OF THE INVENTION
The present invention relates to a process for preparing a propylene polymer composition, and a propylene polymer composition prepared by the process, more particularly to a process for preparing a propylene polymer composition using multistage polymerization and a propylene polymer composition prepared by such process.
BACKGROUND OF THE INVENTION
Because of their excellent rigidity, heat resistance and impact resistance, propylene polymers are used for various molded articles in many fields.
For further improving the impact resistance of propylene polymers, there is known a process comprising initially homopolymerizing propylene and then copolymerizing propylene and ethylene to prepare a block copolymer.
For example, Japanese Patent Laid-Open Publication No. 337308/1992 discloses a process for preparing a block copolymer in which propylene is first homopolymerized or copolymerized with ethylene in the presence of a transition metal compound having as a ligand a cyclopentadienyl bridged with a silylene group and an organoaluminum compound so as to produce a propylene homopolymer or a propylene copolymer containing less than 6% by weight of ethylene, in an amount of 40 to 95% by weight based on the total weight of the final polymer product; and then ethylene and propylene in a weight ratio of 10/10 to 95/5 are further copolymerized in the presence of the same transition metal compound and the same organoaluminum compound until a copolymer is produced in an amount of 60 to 5% by weight based on the total weight of the final polymer product. This publication also describes that the block copolymer obtained by this process has well balanced properties between impact resistance and rigidity.
Japanese Patent Laid-Open Publication No. 202152/1993 discloses a process for preparing a polypropylene molding material comprising (1) 20 to 99% by weight of a crystalline polymer having a propylene unit content of not less than 95% by weight and (2) 1 to 80% by weight of a non-crystalline ethylene-propylene copolymer having an ethylene unit content of 20 to 90% by weight, in the presence of a catalyst comprising a transition metal compound and an organoaluminum compound, in which polymerization to prepare the non-crystalline ethylene-propylene copolymer is carried out using a specific bridged metallocene compound and aluminoxane. This publication also describes that the polypropylene molding material obtained by this process has excellent properties, particularly in low-temperature impact strength.
However, there has recently been an increasingly severe demand for properties of polypropylene compositions. In addition, there has also been a need for a propylene polymer composition having well balanced properties among rigidity, heat resistance and impact resistance, and a process capable of preparing such composition.
DESCRIPTION OF THE INVENTION
The first process for preparing a propylene polymer composition according to the invention comprises: and (c) in the presence of cyclopentadienyl skeleton and each of the second and subsequent stage polymerizations is carried out in the presence of a polymer or polymers obtained in the preceding stage or stages, respectively, to produce a propylene polymer composition comprising 20 to 90% by weight of a propylene (co)polymer (a) obtained in the step (a), 5 to 75% by weight of a propylene/olefin copolymer (b) obtained in the step (b) and 5 to 75% by weight of an ethylene/olefin copolyemr obtained in the step (c), said composition having a melt flow rate, as measured at 230.degree. C. under a load of 2.16 kg, of 0.01 to 500 g/10 min; least one olefin selected from ethylene and olefins of 4 to 20 carbon atoms to prepare a propylene (co)polymer (a) comprising not less than 80 mol % of constituent units derived from propylene, said propylene (co)polymer (a) having a melting point, as measured by a differential scanni
REFERENCES:
patent: 4245062 (1981-01-01), Suzuki
patent: 4337326 (1982-06-01), Shiga
patent: 4550145 (1985-10-01), Kasahara
patent: 4910262 (1990-03-01), Fujii
patent: 4990640 (1991-02-01), Tsutsui et al.
patent: 5155080 (1992-10-01), Elder et al.
patent: 5225500 (1993-07-01), Elder et al.
patent: 5232993 (1993-08-01), Winter et al.
patent: 5280074 (1994-01-01), Schreck et al.
patent: 5321106 (1994-06-01), LaPointe
patent: 5322902 (1994-06-01), Schreck et al.
patent: 5326639 (1994-07-01), Leonard
patent: 5330948 (1994-07-01), Marks
patent: 5336746 (1994-08-01), Tsutsui
patent: 5350817 (1994-09-01), Winter
patent: 5352520 (1994-10-01), Katajima
patent: 5387568 (1995-02-01), Ewen et al.
patent: 5391629 (1995-02-01), Turner
patent: 5416178 (1995-05-01), Winter
patent: 5416228 (1995-05-01), Ewen
patent: 5453466 (1995-09-01), Pellegatti
patent: 5504172 (1996-04-01), Imuta
Fukuoka Daisuke
Hashimoto Mikio
Imuta Jun-ichi
Kawasaki Masaaki
Ueda Takashi
Mitsui Petrochemical Industries Ltd.
Zemel Irina S.
LandOfFree
Process for preparing propylene polymer composition and propylen does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Process for preparing propylene polymer composition and propylen, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Process for preparing propylene polymer composition and propylen will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1854086