Compositions: coating or plastic – Coating or plastic compositions – Corrosion inhibiting coating composition
Reexamination Certificate
2003-05-20
2004-08-03
Green, Anthony J. (Department: 1755)
Compositions: coating or plastic
Coating or plastic compositions
Corrosion inhibiting coating composition
C106S014130, C106S014430, C106S403000, C106S404000, C428S405000
Reexamination Certificate
active
06770124
ABSTRACT:
FIELD OF THE INVENTION
This invention relates to dispersions of zinc powder in water, and to zinc powder-containing water base paints suitable for imparting corrosion-inhibiting and rust-inhibiting films onto metal surfaces.
BACKGROUND OF THE INVENTION
A water-based treatment agent, containing zinc powder and chromic acid as its principal components, has been widely used as a rust inhibitor on metallic surfaces. The treatment agent contains hexavalent chromium, which exerts a passivating action, allowing the zinc, which is otherwise liable to react with water over time, to be maintained in water as a stable dispersion over a long period of time. After a film is formed on an iron substrate, however, the hexavalent chromium allows the zinc to revert to an active state so that it can exert a sacrificial anti-corrosive action. The zinc prevents the elution of iron since zinc is electrochemically anodic to iron, and is eluted more readily than iron. At the same time the hexavalent chromium forms an anti-corrosion film.
Since the conventional treatment agent contains hexavalent chromium ions, which are hazardous, adverse effects on the human body, and environmental contamination, due to the elution of chromium from protective films have been a serious concern. Furthermore, legal restrictions have been imposed in various countries on the use of hexavalent chromium even in rust inhibitors for metallic surfaces. Accordingly a need exists for the establishment of a chromium-free technology.
In the general movement toward the use of water base paints, even zinc powder-containing paints are required to be water based. However, since zinc powder is liable to react with water in the absence of chromic acid, the market need for a dispersion of zinc powder in water, which is stable over a long period of time, has not been satisfied.
Accordingly, the principal objects of the invention are to make zinc powder stably dispersible in water for long period of time without the use of hexavalent chromium, and to provide an environmentally safer, zinc powder-containing, water base paint.
SUMMARY OF THE INVENTION
A water-dispersible, zinc powder-containing, material in accordance with the invention comprises zinc powder and a silane coupling agent, the molecules of which have a mercapto group. The coupling agent is present in the material in an amount in the range from 0.1 to 10 parts by weight for every 100 parts by weight of zinc powder. A water base paint can be made from a water dispersion of the above material.
In the above composition, the zinc powder remains stably dispersed in water for a long period of time, and the performance of the paint is not impaired by the reaction of zinc powder with water, or by the generation of a large amount of gas. Furthermore, since the silane coupling agent does not contain a hazardous substance such as hexavalent chromium and the like, adverse influences on the human body and environment are greatly reduced.
The mechanism by which the silane coupling agent having a mercapto group stably disperses zinc powder in water over a long period of time is not clearly understood. However, it is believed that the mercapto group in the molecules of the silane coupling agent becomes selectively chemically bonded with the zinc powder so that it prevents the reaction of zinc powder with water.
The stable dispersibility of the zinc powder in water, using a silane coupling agent with a mercapto group makes it possible to produce a chromium-free, zinc powder-containing water base paint.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
The zinc powder used in the dispersion in accordance with the invention is not limited to any particular range of particle diameters or shapes. For example, the particles can be spherical, flat, rod-shaped, or in any of a wide variety of forms. Some forms are more desirable than others, however. For example in the case of the flat form, the zinc powder has a superior coating effect on the surface to which it is applied so that it has superior rust-preventing performance.
This flat-shaped zinc powder particles are obtained by a developing and elongation process, using a ball mill, an attritor or the like. The average aspect ratio (average of long dimension divided by thickness) is preferably 10 or more.
In developing and elongating the zinc powder, the associated silane coupling agent is used as a grinding assistant in such a manner that the zinc surface is directly coated by the coupling agent. Additionally, as a general grinding assistant, saturated fatty acid such as stearic acid or the like, and unsaturated fatty acid such as oleic acid or the like may be used.
Furthermore, when the surface of the zinc powder is coated with the above-mentioned general grinding assistant, the surface may be treated by the silane coupling agent in a kneading process or the like.
This kneading process may be performed in the presence of an organic solvent. However, it is particularly advantageous to use a water-soluble solvent, since a processed slurry of dispersed zinc powder can be developed in water base paint as it is. Of course, after processing the kneading using a water-insoluble solvent, the solvent may be dried and removed, and then the processed dispersed zinc powder may be mixed with water.
Suitable water-soluble solvents include glycol series solvents such as propylene glycol, ethylene glycol and the like, alcohol series solvents such as ethanol, isopropanol and the like, and the series of ethylene glycol ethers known by the trademark CELLOSOLVE, for example ethylene glycol monomethyl ether (Methyl CELLOSOLVE) or ethylene glycol monobutyl ether (Butyl CELLOSOLVE).
If the molecule of the silane coupling agent used in the invention contains a mercapto group, other reactive groups and substituting groups are not limited particularly. Suitable silane coupling agents include &ggr;-mercapto propyl trimethoxysilane, &ggr;-mercapto propyl methyl dimethoxysilane and the like. Two or more types of silane coupling agents may be used in the same zinc powder material.
The amount of the silane coupling agent added to the zinc powder is preferably 0.1 to 10 parts by weight for every 100 parts by weight of zinc powder. An amount of silane coupling agent less than 0.1 parts of weight is insufficient to process the surface of the zinc powder and does not afford sufficient stability of the zinc powder in water. An amount of silane coupling agent in excess of 10 parts by weight is excessive and its cost outweighs its advantages.
The zinc powder according to the invention may be used with resin to produce a water base paint, and the zinc powder-containing water base paint can be produced by conventional known paint-making methods.
Suitable resins for the water base paint include, for example, inorganic series resins such as silicate of soda, ethyl silicate and the like, and organic resins such as acrylic resin, urethane resin, epoxy resin, silicone resin and the like. Although only one type of resin is usually required, two or more different types of resin may be used together. In the case of inorganic resins, the presence of numerous voids allows the zinc to be brought into direct contact with the metal surface, so that the sacrificial anti-corrosive action of the zinc can be realized.
Other additives may be included in the zinc powder-containing water base paint. For example, a different metallic powder such as aluminum flakes, a water-soluble solvent such as an alcohol solvent, CELLOSOLVE solvent, a glycol solvent, and paint additives such as pigment, dye, defoaming agent, or the like may be added. Aluminum flakes are particularly useful because they prevent the occurrence of white oxides in zinc powder.
Although the zinc powder composition according to the invention can exist stably in water, and is preferably used in water base paint, the zinc powder composition may also be used in a solvent type paint without any problems.
REFERENCES:
patent: 3388144 (1968-06-01), Musolf et al.
patent: 4172737 (1979-10-01), Magee, Jr.
patent: 4518726 (1985-05-01), Kato et al.
pate
Homi Makoto
Ikegami Makoto
Green Anthony J.
Howson and Howson
Tsubakimoto Chain Co.
LandOfFree
Zinc powder dispersible in water and zinc powder-containing... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Zinc powder dispersible in water and zinc powder-containing..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Zinc powder dispersible in water and zinc powder-containing... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3344873