Colloid systems and wetting agents; subcombinations thereof; pro – Continuous liquid or supercritical phase: colloid systems;... – Aqueous continuous liquid phase and discontinuous phase...
Reexamination Certificate
1999-08-25
2001-02-13
Lovering, Richard D. (Department: 1712)
Colloid systems and wetting agents; subcombinations thereof; pro
Continuous liquid or supercritical phase: colloid systems;...
Aqueous continuous liquid phase and discontinuous phase...
C106S286200, C428S403000, C502S304000, C424S059000
Reexamination Certificate
active
06187824
ABSTRACT:
BACKGROUND OF THE INVENTION
This invention is directed to an improved method for making small particle zinc oxide sols having utility in diverse applications such as cosmetic/UV sunscreens, UV absorption applications in plastics, paint and glass, general catalysis applications, etc.
As is well known and reported in the literature, zinc oxide has the property of being transparent to visible light but opaque to ultra violet (UV) light, thereby making it very useful in UV screening applications where transparency to visible light is desired.
The opacity of a suspension of fine material is dependent upon the particle size of the material, the difference in the refractive index of the dispersed material and the dispersing medium, the degree of absorption of the light by the particles of material and the wavelength of light used in the opacity measurement.
The refractive index (measure of speed of light in the given substance relative to the speed of light in air) of zinc oxide is relatively high, being~2.0, making it a good opacifying pigment, e.g. for paints. Since the refractive index is a fixed characteristic, the approach to alter opacity is to manipulate particle size.
The surface of a zinc oxide crystal effectively reflects visible light. Opacity to visible light reaches a maximum at a particle size of 0.25 micron (250 nm). Smaller particles actually transmit more light than their larger counterparts. This is because particles smaller than~0.25 micron no longer simply reflect back the light, but instead, they scatter it in all directions. Some of this scattered light goes forward, becoming transmitted light.
Zinc oxide owes its opacity below 370 nm to its absorbing power, practically no light being reflected. Because absorption is the mechanism of action, it is possible to make transparent to visible light (non-reflecting) zinc oxide formulations that effectively attenuate UV radiation. Particle sizes on the order of~0.1 micron or less will provide UV absorption while being effectively transparent to visible light. Above this size, “whitening” will occur.
While a search of the patent literature is not necessary in order to demonstrate the efficacy of transparent zinc oxide coatings on a substrate to block transmission of UV radiation, attention is invited to a brief description of the following patents which are thought to be relevant to the instant invention to be described hereinafter.
U.S. Pat. No. 5,252,356 issued to Yoshida et al. discloses a method of producing a transparent zinc oxide film having an even thickness and which is especially useful as a ultraviolet rays cutoff, comprising applying an organic solution of a zinc salt of a 3-7 carbon fatty acid and a chelate compound of a 5-8 carbon diketone to a substrate and then baking. Preferably, the solution further contains an aluminum, indium, tin, or titanium organometallic compound to provide a zinc oxide film having a higher transparency.
U.S. Pat. No. 5,688,439 issued to Chopin et al. discloses colloidal particulates comprising a core of cerium oxide at least partially coated with a sheathing layer of titanium oxide are well suited for the photocatalytic coating of a variety of substrates to impart anti-UV, anti-reflecting and/or anti-staining properties to the substrate. In Col. 1, line 55 through Co. 2, line 18 four alternative methods of effecting precipitation of titanium oxide onto the cerium oxide are disclosed.
The colloidal dispersions comprise colloids in which the particle size thereof ranges from 5-100 nm, preferably 5-30 nm. The colloidal dispersions are said typically to contain a cerium oxide:titanium oxide ratio by weight of 30/70 to 70/30, preferably 50/50.
Advantageously (co. 3, lines 50-55), the colloidal dispersions additionally contain at least one metal serving as a doping agent to reinforce the photocatalytic activity of the titanium dioxide, e.g. palladium, tungsten, platinum or rhodium.
The present invention is also directed to providing a transparent UV absorber consisting of a layer of one oxide over a “core” of another oxide sol. The problem Applicant has confronted in attempting this approach is the difficulty in making very small particle size transparent sols (less than 50 nm) exhibiting optimum screening of UV radiation by prior art methods known to him.
Stated simply, this problem is the task to which to which the present invention is directed.
SUMMARY OF THE INVENTION
In accordance with the present invention this task is solved in an elegant and efficacious manner suitable for commercial manufacture by forming a zinc oxide-containing sol comprising a core of cerium dioxide the surface of which contains a coating of zinc oxide, the zinc oxide/cerium dioxide sol being prepared in the manner described hereinafter in the detailed description of the invention.
DETAILED DESCRIPTION OF THE INVENTION
As was discussed in the BACKGROUND OF THE INVENTION, the present invention is directed to the task of preparing zinc oxide-containing sols having a particle size less than 50 nm (0.05 micrometer).
This task is solved by preparing a sol comprising a cerium dioxide core having on its surface a layer of zinc oxide.
The zinc oxide/cerium dioxide sol is prepared by first mixing zinc oxide powder with an aqueous cerium dioxide sol at a pH of~1.0 to 3.5 and continuing the mixing until the sol is once again “substantially transparent”, indicating that the zinc oxide has coated the cerium oxide particles to form a slightly larger particle size sol.
As used herein and in the appended claims, the term “substantially transparent” is used to define an effective transmission of actinic light to be regarded by those skilled in the art as being effectively transparent, although the sol, while clear, has a slight yellow color. In any case, the sol when coated on a transparent support will be regarded as viewed by the eye to be transparent.
The amount of zinc oxide added to the mix to coat the cerium dioxide sol is such that the pH of the coated sol will rise to a range from~2 to~7.
The cerium dioxide sol prior to coating may have a particle size of on the order of about 5 to about 30 nm, preferably from about 5 to about 10 nm.
Following the coating with zinc oxide particles, the resulting zinc oxide/cerium dioxide sol has been found to be stable only for several hours, after which the ZnO/CeO
2
composition starts to agglomerate and the particle size increases, changing its appearance from clear (transparent) yellow to an opaque white/yellow dispersion.
Accordingly, a critical part of this invention is the step of stabilization of the sol while it is still substantially transparent.
The desired stability for commercialization of this invention is obtained simply by overcoating the zinc oxide with an effective amount of a positive charged oxide such as yttrium oxide (Y
2
O
3
), samarium oxide (Sm
2
O
3
), aluminum oxide (Al
2
O
3
), zirconium dioxide (ZrO
2
), etc.
As used herein and in the appended claims, the term “effective amount” of a positive charged oxide connotes an amount sufficient to maintain the stability of the sol, i.e. to maintain its physical properties, e.g. transparency, particle size and freedom from agglomeration such that they were shortly after preparation. The amount of stabilizer to be employed will in part be dependent upon the stabilizer selected and will in part be dependent upon the ratio of ZnO to cerium dioxide in the sol. Accordingly, it is not thought possible positively to recite a range of stabilizer to be used which would at all amounts within that range reflect the stabilization that is desired. For this reason, the amount of stabilizer is recited simply as being an “effective amount”. In any case, the selection of a precise amount of stabilizer to use would be within the expected judgment of the skilled worker in the light of this description.
The novel sols of this invention can be applied from an aqueous medium as a coating on the desired substrate in per se known manner, e.g., by immersion, spraying, flowing, vacuum evaporation, etc. In any case the manner of application
Isaacs Alvin
Lovering Richard D.
Metzmaier Daniel S.
Nyacol Nano Technologies, Inc.
LandOfFree
Zinc oxide sol and method of making does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Zinc oxide sol and method of making, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Zinc oxide sol and method of making will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2596030