DESCRIPTION:
BRIEF SUMMARY
BACKGROUND OF THE INVENTION
The invention relates to a wear-resistant layer on a component which is exposed to a high level of wear, and a process for the production of such a layer.
Many processes are used for coating parts or workpieces, such as for example thermal spraying, CVD, PVD and galvanic processes.
Processes are also known, in which the material for the coating is applied by brushing in the form of a paste or in which it is applied as a strip. It will be appreciated that in that case they can only be fused in position in a vacuum or under a reducing protective gas.
All those processes involve very high levels of cost, because of a high level of apparatus expenditure, and for that reason such coating operations can only be carried out in the workplaces which ale equipped for that purpose.
Therefore, for producing simple and inexpensive mass-produced components, it is necessary to find a process for applying corrosion-resistant and wear-resistant layers, which process makes it possible to keep the costs of a protective coating as low as possible.
SUMMARY OF THE INVENTION
That object seen by the inventor is attained by the teachings of the present invention which; by virtue of the use of a material mass in paste or strip form, which comprises metal powder, with or without one or more hard substances, a fluxing agent and a resin-like binding agent, it is possible for the applied material to be fused in position, without taking into consideration the ambient atmosphere, for example in air or with an autogenous flame or in a muffle furnace, without protective gas.
The present invention provides a wear-resistant layer on a component which is exposed to a high wear loading, which comprises a material mixture comprising at least one metallic material in powder form and a non-metallic oxide-dissolving fluxing agent in powder form which by the addition of a resin-like non-corroding stable binding agent is converted into a form which is applied to the component by being laid or spread thereon, and fused.
In addition, the present invention provides a process for the production of a low-wear protective layer on a component which is exposed to high wear loading, which comprises mixing at least one metallic material in powder form and a non-metallic oxide dissolving fluxing agent in powder form, and adding a resin-like non-corroding stable binding agent to the material mixture, whereafter said binding agent-containing material mixture is spread on or laid on the component, and fused in position.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
Further advantages, features and details of the invention will be found hereinbelow.
EXAMPLE 1
For the production of a self-sharpening blade cutting edge, a material mass in paste form was applied to a steel plate using a brush, the material mass comprising a mixture of an Ni-Cr-B-Si-alloy powder with 25% by weight of chromium, 0.2 to 2.0% by volume of fluxing agent and 4 to 6% by volume of a water-soluble methacrylate. After drying and hardening that layer was fused with a flame.
After the fusing operation the coating produced in that way presented a clean and smooth surface which was distinguished by good corrosion resistance.
EXAMPLE 2
To produce the material mass in paste form, 0.1 to 1.5% by volume of fluxing agent and 5 to 7% by volume of methacrylate were added to a material mass in paste form comprising a mixture which contained an Ni-Cr-B-Si-alloy material and a tungsten carbide powder with a mixing ratio of 50:50. Production of the coating on a wearing component was effected as described in Example 1. The finished layer had a high level of resistance to wear.
EXAMPLE 3
A coating was produced as in Example 1, using a material mass in paste form comprising a mixture of an Ni-B-Si-alloy powder and chromium borides in a mixing ratio of 70/30. Added to that mixture were 2.5 to 4.5% by volume of fluxing agent and 3 to 10% by volume of a water-soluble methacrylate.
The coating produced in that way afforded good resistance to corrosion and wear.
EXAMPLE 4
REFERENCES:
patent: 3049435 (1962-08-01), Shwayder
patent: 3479231 (1969-11-01), Joseph
patent: 4493738 (1985-01-01), Collier et al.
Castolin S.A.
Turner Archene
LandOfFree
Wear-resistant layer on a component and process for the producti does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Wear-resistant layer on a component and process for the producti, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Wear-resistant layer on a component and process for the producti will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1308201