Radiation imagery chemistry: process – composition – or product th – Imaged product – Including resin or synthetic polymer
Reexamination Certificate
2000-01-18
2002-09-03
Hamilton, Cynthia (Department: 1752)
Radiation imagery chemistry: process, composition, or product th
Imaged product
Including resin or synthetic polymer
C430S325000, C430S324000, C430S311000, C430S313000, C430S300000
Reexamination Certificate
active
06444378
ABSTRACT:
The present invention is directed to methods of coating circuit boards including photoresists, such as those used in the manufacture of printed circuit boards and more particularly to waterborne, liquid plating/etching photoresists, soldermasks and waterborne protective coatings.
BACKGROUND OF THE INVENTION
Photoimageable compositions useful as resists for forming printed circuits, printing plates, solder masks or the like have been used for some time now. The earliest photoresists were solvent-borne and solvent developable. The invention of aqueous developable resists represented an advance in reducing solvent emissions in the printed circuit board manufacturing plant and the environment in general. This can be seen from U.S. Pat. Nos. 4,100,047, 4,564,580 and 4,133,909, herein incorporated by reference, which describe aqueous coatings, also from U.S. Pat. Nos. 3,953,309 and 4,361,640, herein incorporated by reference, which teach aqueous developing compositions. The continued emphasis in reducing organic solvents has spurred the search for waterborne photoresists which are formulated and applied as aqueous liquids with out the addition of any organic solvents.
A critical requirement for photoresist, especially liquid photoresist, is the ability to evaporate the solvent carrier during a brief heat cycle to yield a tack-free surface. This permits intimate contact with the artwork used to define the image. Another requirement is the ability of the liquid photoresist to fully wet the surface and form a continuous film as the copper clad laminate used to manufacture printed circuit boards often has a variety of surface irregularities. These requirements have limited the development of successful waterborne products of this type.
U.S. Pat. No. 5,045,435, herein incorporated by reference, describes a waterborne photoresist composition which is developed in alkaline aqueous solution. The composition comprises a multi functional monomer, a photo initiator and a latex of water-insoluble carboxylated acrylic copolymer. To stabilize the composition and adjust the viscosity, this patent teaches neutralizing the latex polymer to at least 25% with a base, such as ammonia, another amine, or sodium hydroxide.
A liquid such as a waterborne photoresist liquid will only wet and spread over a surface if the forces of attraction between the liquid and the substrate are greater than the cohesive forces within the liquid. Accordingly, the surface energy of the liquid must be at or below the surface energy of the substrate. Thus, to coat a copper substrate having a surface energy of 35 dynes/cm, the surface energy of water, which has a surface energy of 72 dynes/cm, must be reduced. U.S. Pat. No. 5,045,435 teaches that this can be accomplished with the aid of a suitable surfactant.
A surfactant is a material with both hydrophillic and hydrophobic properties. Surfactants can be divided into three major chemical classes; hydrocarbons, silicones and fluorochemicals, these designations referring to the hydrophobic portion of the molecule. The hydrophobe is attached to a hydrophilic group, which can be anionic, cationic or non-ionic in nature.
According to U.S. Pat. No. 5,389,495, herein incorporated by reference, neither hydrocarbon surfactants nor silicon surfactants are particularly suitable in waterborne photoimageable compositions. Although all types of surfactants are found to sufficiently lower surface energy, it is found that hydrocarbon and silicone surfactants encounter problems with respect to dewetting of the copper substrate. Dewetting produces voids which results in an unsuitable coating. Furthermore, if the photoimageable composition is intended as a plating resist, silicone from the silicone-based surfactant can leach into the plating solution, creating potential bath failure. Of the major classes of surfactants, hydrocarbon based surfactants are found to be the least effective in reducing the surface tension of the liquid and do not produce defect-free coatings. Furthermore, hydrocarbon based surfactants contribute to the overall volatile organic components (VOCs) in the coating, which is contrary to the purpose of producing waterborne coatings.
U.S. Pat. No. 5,045,435 gives examples wherein fluorocarbon-based surfactants are used in waterborne photoimageable compositions but applicant has found that these compounds do not perform well and produce undesirable side effects. U.S. Pat. No. 5,389,455 gives examples wherein fluoroaliphatic oxyethylene adduct surfactants are used in waterborne photoimageable compositions. Applicant has found that these compounds are difficult to work with in a production environment and results can vary substantially with a change in surfactant concentration as small as 0.1% by weight,of the surfactant.
SUMMARY AND OBJECTS OF THE INVENTION
It is a general object of the present invention to wholly eliminate the critical dependence on a separate surfactant to lower the surface tension between a water borne photoimageable composition and a surface by the use of binder polymers which can inherently act as surfactants, wetting the copper surface, to yield a photoimageable composition with acceptable coating quality.
It is an object of this invention to use these photo imageable compositions as a general protective coating, as a photoimagable composition for forming printed circuits, printing plates chemically milled parts and solder masks.
It is also an object of this invention to utilize as a base polymer for the photoimageable composition, a polymer that is UV reactive, soluble in both water and a caustic solution and will yield a tack-free surface after evaporation of the water. This approach is a departure form the standard technique of dispersing a multi-functional monomer and a photoinitiator into a latex of water-insoluble carboxylated acrylic copolymer.
The waterborne coatings provided by this invention completely avoid the use of organic carrier solvents. When photopolymerized these coatings are readily soluble in alkali but are resistant to the etching and plating solutions characteristic of the printed circuit board industry. Further, when they are subjected to an elevated temperature cure following photopolymerization, these coatings can withstand soldering and other rigorous environments.
DESCRIPTION OF THE INVENTION
A waterborne photoimageable composition comprised of (A) between about 30 and about 98 wt % of a binder polymer that is a waterborne dispersion of an aliphatic urethane acrylate oligomer, containing both anionic and non-ionic moieties, having carboxylic acid functionality which provides an acid number of between about 8 and 250; (B) between about 1 and about 25 wt % of a photoinitiator or photoinitiator chemical system which generates free radicals and (C) between about 1 and about 40 wt % of a neutralizing base can be used to coat a surface prior to photo polymerization of the exposed portions of the coated surface.
In a preferred composition for an etch/plating resist, a latex of an aliphatic urethane acrylate oligomer binder polymer, with an acid number of at least 12.5, neutralized with base, in at least 60% water is combined with i) a water soluble di, tri or tetra functionalized acrylate monomer and/or an acid functionalized di, tri or tetra functionalized methacrylate oligomer neutralized in ammonia 2) a photoinitiator and, 3) optionally, a colorant. This composition provides a tack-free surface, a smooth, void free coating on metals such as copper and after photopolymerization is able to withstand plating and etching solutions. The di, tri, or tetra acrylate or methacrylate monomers or mixtures of these monomers are very useful in increasing the cross-link density of the coating after irradiation with actinic light.
In a preferred composition for a solder mask, a latex of an aliphatic urethane acrylate oligomer binder polymer, with an acid number of at least 12.5, neutralized with base, in at least 60% by weight of water is combined with 1) water soluble di; tri or tetra functionalized acrylate monomer and/or an acid functionalize
Advanced Coatings International Ltd.
Blank Rome Comisky & McCauley LLP
Hamilton Cynthia
LandOfFree
Waterborne photoresists for use in manufacture of printed... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Waterborne photoresists for use in manufacture of printed..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Waterborne photoresists for use in manufacture of printed... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2875886