ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to an additive useful in improving the water-resistance of gypsum products. The present invention also relates to an emulsion which includes an alkyl phenol, a wax, or a combination of waxes, and a complexed starch, the emulsion useful in improving the water resistance of gypsum products. The present invention further relates to a method of making the emulsion.
BACKGROUND OF THE INVENTION
Certain properties of gypsum (calcium sulfate dihydrate) make it very popular for use in making industrial and building products; especially gypsum board. It is a plentiful and generally inexpensive raw material which, through a process of dehydration and rehydration, can be cast, molded or otherwise formed to useful shapes. The base material from which gypsum board is manufactured is the hemihydrate form of calcium sulfate (gypsum), commonly termed stucco, which is produced by the heat conversion of the dihydrate from which the water phase has been removed.
In the making of gypsum board, the gypsum slurry must flow onto a paper substrate. In a continuous process, the slurry/substrate combination is then sized by passing this combination between rollers. Simultaneous with this sizing step, a paper backing is positioned over the sized gypsum slurry. Accordingly, the gypsum slurry must possess sufficient fluidity so that a properly sized gypsum board can be made. Fluidity refers to the ability of the gypsum slurry to flow.
It is also important to the manufacture of gypsum board, that the gypsum slurry be capable of being foamed to a limited extent. Foamability refers to this ability to be foamed. When the gypsum slurry and paper substrate are passed through the sizing rollers, a certain amount of the gypsum slurry must back flow and accumulate in the rollers nip so that a steady flow of gypsum is delivered to the sizing rollers. Foamability is important to this ability of the gypsum slurry to back flow at the rollers nip.
Because of the continuous nature of a gypsum board manufacturing process wherein the gypsum slurry flows onto a substrate which then passes through sizing rollers, the extent to which the gypsum slurry flows after it is sized is critical to maintaining the finished product dimensions of the gypsum board. The time at which the gypsum slurry ceases its flow is referred to as the pre-set time. Therefore, pre-set time is an important property of the gypsum slurry. The set time of the gypsum slurry is also an important property. The set time refers to the amount of time it takes the gypsum slurry to be dried, under heat, to the finished, solid gypsum board. As is well known in the art, in a continuous gypsum board manufacturing process, it is important that the gypsum slurry possess a consistent set time.
Gypsum board absorbs water, which reduces the strength of the wallboard. Prior art products, like ordinary gypsum board, gypsum tile, gypsum block, gypsum casts, and the like have relatively little resistance to water. When ordinary gypsum board, for example, is immersed in water, the board quickly absorbs a considerable amount of water, and loses a great deal of its strength. Actual tests have demonstrated that when a 2 inch by 4 inch cylinder of gypsum board core material was immersed in water at about 70° F., the cylinder showed a water absorption of 36% after immersion for 40 minutes.
Previous attempts to provide water-resistant properties to gypsum board include incorporation of asphalt, metallic soaps, resins, and wax additives into a aqueous gypsum slurry. The resulting materials were difficult to use and the core properties difficult to control. Polysiloxane-based systems have also been used in attempts to impart water-resistance to gypsum board. However, the polysiloxane-based systems are both expensive and difficult to use. A finished gypsum product has also been coated with water resistant films or coatings. One specific example of a past attempt to provide a water-resistant gypsum product is the spraying of a molten paraffin, wax or asphalt into an aqueous gypsum slurry.
Another example of a prior art attempt to provide a water resistant gypsum product is the addition of an emulsion of wax, such as paraffin wax, and asphalt, in the relative proportions of from about 1 part to about 10 parts of asphalt per part of wax to the aqueous gypsum slurry. Since the asphalt is a relatively poor solvent for paraffin wax and similar wax at ordinary temperatures, the solution formed at high temperatures tends on cooling to deposit microscopic wax crystals on the asphalt-wax surface.
Polyvinyl alcohol has been used in an attempt to provide a room temperature system for use in adding water resistant properties to gypsum. However, the polyvinyl alcohol system tends to rapidly separate and thus typically requires continuous mixing prior to use. The inherent instability of the polyvinyl alcohol systems tends to produce stratification of the compounds in the formulation. Therefore, the polyvinyl alcohol systems tend to be compositionally inconsistent. In addition, because of destabilization into different phases, there is also the potential for bacterial growth.
Accordingly, there is a need for an additive which is useful in imparting water-resistance to gypsum products, and which is economical to apply. There is a need for a water-resistance additive which does not require the use of costly components such as polysiloxane. There is a need for a stable, water-resistance additive. There is a further need for a water-resistance additive which is stable at room temperature and which does not require heating prior to application to a gypsum solution. There is still a further need for a stable water-resistance additive which does not require continuous mixing or agitation to maintain its stability. There is yet a further need for a stable water-resistance additive which does not require the addition of a bactericide to control bacterial growth inherent in existing systems. Of course, such additives should perform these functions without affecting fluidity, foamability, pre-set time or set time.
SUMMARY OF THE INVENTION
The present invention, in one embodiment, provides an emulsion which comprises a plurality of waxes, at least one saponified wax, a complexed starch, a polymerized alkyl phenol, and a small amount of a co-surfactant. In another embodiment, the present invention provides an emulsion comprising a single wax, a balanced dual surfactant system, a complexed starch and a polymerized alkyl phenol. Emulsions of this embodiment may be added to hot, even boiling, water without the emulsion separating or curdling. The emulsions of the present invention are stable for extended periods of time when stored at room temperature and do not require the addition of a bactericide. The emulsions of the present invention are pourable liquids at room temperature.
The emulsions of the present invention are useful in imparting water resistance to gypsum products. The emulsions of the present invention also include a fire retardant. The emulsions of the present invention may be used in the manufacture of conventional gypsum board, composites made using gypsum, such as gypsum/fiber composites, and other gypsum products.
REFERENCES:
patent: 3891453 (1975-06-01), Williams
patent: 3935021 (1976-01-01), Greve et al.
patent: 4019920 (1977-04-01), Burkard et al.
patent: 4042409 (1977-08-01), Terada et al.
patent: 4094694 (1978-06-01), Long
patent: 4174230 (1979-11-01), Hashimoto et al.
patent: 4392896 (1983-07-01), Sakakibara
patent: 4421704 (1983-12-01), Reily
patent: 4748196 (1988-05-01), Kuroda et al.
patent: 5009269 (1991-04-01), Moran et al.
patent: 5120355 (1992-06-01), Imai
patent: 5482551 (1996-01-01), Morris et al.
patent: 5695553 (1997-12-01), Claret et al.
patent: 5922447 (1999-07-01), Baig
patent: 5968237 (1999-10-01), Sinnige
patent: 5980628 (1999-11-01), Hjelmeland et al.
patent: 6010596 (2000-01-01), Song
patent: 6162839 (2000-12-01), Klauck et al.
patent: 6165261 (2000-12-01), Wantling
patent: 6172122 (2001-01-01), Lawate et al.
Wantling Steven Joseph
Zepka Bonnie Sherrard
Fleet Capital Corporation
Marcantoni Paul
LandOfFree
Water-resistant gypsum formulations does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Water-resistant gypsum formulations, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Water-resistant gypsum formulations will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3008230