Compositions: coating or plastic – Coating or plastic compositions – Coating repellent
Reexamination Certificate
2000-11-09
2002-12-10
Koslow, C. Melissa (Department: 1755)
Compositions: coating or plastic
Coating or plastic compositions
Coating repellent
C252S008570, C252S008610, C523S169000, C106S003000, C106S004000, C106S005000, C106S006000, C106S007000, C106S008000, C106S009000, C106S010000, C106S011000, C106S287100, C106S287110, C106S287120, C106S287130, C106S287140, C106S287160, C106S287250, C106S287280, C106S271000
Reexamination Certificate
active
06491745
ABSTRACT:
DETAILED DESCRIPTION OF THE INVENTION
The present invention relates a water/oil repellent composition, more particularly to a water/oil repellent composition containing microcapsules in which a polishing agent is encapsulated. When the water/oil repellent composition of the present invention is used in a waterproofing treatment of leather products such as leather, etc., a water/oil repellent agent can permeates through leather to exert satisfactory water repellency and oil repellency. Also, when the leather surface is polished by using a dry cloth after permeation of the water/oil repellent agent and further drying, excellent gloss, i.e. polishing effect can be exerted.
PRIOR ART
To impart the water repellency and oil repellency to leather products, a method of dissolving a water/oil repellent component such as fluororesin, etc. in a solvent, applying the resultant on leather, followed by drying to evaporate the solvent has generally been used, heretofore. To further improve the resulting water repellency and oil repellency in such a water/oil repellent composition, various compositions have been suggested. For example, the present applicant has suggested a composition for treating leather, a woven fabric and a cellulose material to impart high water/oil repellency to them, comprising (i) a fluorochemical compound represented by the formula: RF-Q-A [wherein Rf represents a fluoro aliphatic portion, A represents an aliphatic portion and Q represents an organic group] and (ii) a vehicle, in Japanese Patent Publication No. 2516889. When this water/oil repellent composition is used in the treatment of leather, not only durable water/oil repellency is imparted to leather, but also there can be obtained such an effect that an adverse effect is not exerted on appearance, touch, hand feeling and other desirable qualities of leather.
To exert the polishing effect in leather products such as leather shoes, etc. various polishing agents such as solid wax, paste, emulsion, etc. have hitherto been suggested. In case of all these conventional polishing agents, the polishing effect is obtained by directly applying them on the leather surface and polishing the leather surface using a drying cloth.
Furthermore, a method used exclusively to simultaneously exert the water/oil repellent effect and polishing effect in the leather products includes a method of using a two-component composition, i.e. a method of applying a solvent water/oil repellent agent product first, drying and wiping it by using a cloth and then applying a polishing agent and polishing by using a dry cloth. In this method, an operation of two steps is essential and long labor hour is required. Therefore, it is desired to provide a water/oil repellent agent product capable of treating in one step.
As the water/oil repellent agent product capable of treating in one step, a product obtained by directly adding silicone oil to the water/oil repellent composition is placed on the market. However, sufficient effect can not be obtained in view of the polishing effect and a further improvement is desired.
An object of the present invention is to solve the above problems of the prior art, and to provide a water/oil repellent composition which can simultaneously perform a water/oil treatment and a polishing treatment to leather products such as leather shoes, etc., by using one water/oil repellent composition, and can also exert excellent water/oil repellent effect and excellent polishing effect without requiring long time in the treatment.
The present inventors have intensively studied to accomplish the above object. As a result, the present inventors have found that the expected effect can be accomplished by dispersing microcapsules, in which a polishing agent is encapsulated, in a water/oil repellent agent in a water/oil repellent composition containing the water/oil repellent agent as a main component.
As described above, the water/oil repellent composition of the present invention contains a water/oil repellent agent as a main component, particularly characterized in that microcapsules, in which a polishing agent is encapsulated, are uniformly dispersed in the water/oil repellent agent.
In the present invention, since the encapsulized polishing agent is dispersed in the water/oil repellent agent, it is possible to avoid the following disadvantages caused by directly dispersing the polishing agent in the water/oil repellent agent. That is, when the water/oil repellent agent permeates through leather, the polishing agent permeates through leather, simultaneously, and it becomes impossible to apply a sufficient amount of the polishing agent on the leather surface. Accordingly, the polishing effect can not be expected. And besides, the polishing agent penetrated through leather, together with the water/oil repellent agent, inhibits the water/oil repellency. Furthermore, when the amount of the polishing agent in the composition added increases, the phase separation occurs. When the phase separation has occurred, it becomes impossible to uniformly apply the composition to the leather products any longer.
Accordingly, the microcapsules, in which the polishing agent is encapsulated, used in the water/oil repellent composition according to the present invention are not specifically limited, as far as the above disadvantages are avoided. That is, the polishing agent-encapsulated microcapsules are not specifically limited as far as the polishing agent encapsulated in the microcapsules does not elute in a solvent contained in the water/oil repellent composition and a protective film of the microcapsules is stable in the solvent. For example, the protective film constituting the microcapsules is preferably a film of a polycondensate formed by polymerization, more preferably a film of a polycondensate such as aminoplast resin, etc. Among these films, a urea-formaldehyde condensate can be advantageously used. The polishing agent-encapsulated microcapsules can be formed by utilizing a publicly known encapsulization technique.
The polishing agent to be encapsulated in the microcapsules includes normal polishing agents, and is not specifically limited as far as the polishing effect is exerted. Taking the process of encapsulization into consideration, it is necessary that the polishing agent must be oil-soluble. Preferred examples thereof include paraffin wax, silicone oil, wax, natural fats and oils, but are not limited thereto. Such a polishing agent is normally used in the amount of 50 to 99% by weight based on the total weight of the microcapsules.
The shape and size of the microcapsules vary widely, but is preferably spherical. The size, particularly diameter (outer diameter of the protective film) is normally within the range from 50 to 2500 &mgr;m, preferably from 100 to 1500 &mgr;m. When the size of the microcapsules is too large, the microcapsules are broken only by applying a small pressure and the contents come out inadvertently. On the other hand, when the size is too small, the strength of the film is too strong and, therefore, the contents can not come out only by applying a moderate pressure. When the size of the microcapsules is too large or too small, uniform dispersion of the microcapsules can not be accomplished.
The polishing agent-encapsulated microcapsules are used in the water/oil repellent composition in the amount which satisfies the amount of the polishing agent required in single application of the water/oil repellent composition, or which secures to apply a desirable amount of the polishing agent on the leather products.
Furthermore, according to the present inventors' knowledge, the water/oil repellent agent used as the main component is preferably thickened so as to accomplish uniform dispersion of the microcapsules in the water/oil repellent composition. Examples of a suitable thickening means include use of dispersing agents such as thickener, etc., in combination. Examples of a suitable thickener include a polymer compound, which is soluble in the solvent or can be swollen in the solvent, and a compound,
3M Innovative Properties Company
Ball Alan
Chernivec Gerald F.
Koslow C. Melissa
LandOfFree
Water/oil repellent composition does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Water/oil repellent composition, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Water/oil repellent composition will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2997914