ABSTRACT:
The present invention relates to water-based two-component protective coatings for steel. In particular, it relates to heat resistant protective coating compositions. More particularly, it relates to water-based weldable shop primers.
Rolled steel for the heavy steel construction industry (such as the ship-building industry) is generally blasted on-line using automated procedures and immediately coated with a thin layer of a protective coating called shop primer or pre-construction primer.
The requirements for shop primers are multiple:
(i) as to the liquid primers:
both their shelf-life and pot-life should be sufficient;
they should be easily sprayable, particularly in thin layers;
they should dry fairly rapidly;
(ii) as to the dry coatings:
they should provide a good protection against corrosion until overcoated;
they should have a good mechanical resistance;
they should not interfere with the welding and cutting operations;
they should withstand the welding and cutting operations;
they should not induce health hazards during welding operations;
they should be compatible (particularly overcoatable) with the further coatings to be applied.
Silicate-based shop primers are known in the art. EP-A-346385 discloses shop primer compositions comprising:
(i) fillers and pigments, at least 25 wt % of which have electrical conductive properties;
(ii) zinc powder, dust or flakes, in a weight ratio of 1:6 to 1:1 to the total amount of fillers and pigments;
said zinc, fillers and pigments being milled to a sufficient fineness;
(iii) anti-settling agents;
(iv) optionally, thickening agents;
(v) a silicate-type binder, in an amount such that the weight ratio of the SiO2 content of said binder to the total amount of zinc, fillers and pigment is of 1:4 to 1:16; and
(vi) solvents.
Such compositions contain solvents; it is a general trend in the coatings industry to demand a reduction in the use of solvents.
Water-based protective coatings for steel are already known. U.S. Pat. No. 5,580,371 disclosed water-based coating compositions comprising zinc, iron phosphide and potassium silicate. U.S. Pat. No. 5,888,280 disclosed water-based protective coating compositions prepared by combining in the presence of water (i) zinc dust, (ii) a Group IA metal silicate, (iii) a colloidal silica ingredient that is modified with a Group IA metal silicate, and (iv) a carbonate-containing internal hardener. Such compositions however are strongly alkaline; this is found to be generally detrimental to the overcoatability of the shop primer coating.
There is accordingly a need in the art for providing an improved protective coating composition. Thus, it is an object of the invention to provide a shop primer composition that would be water-based and that would not be strongly alkaline. This and other objects are achieved by the compositions of the invention.
The compositions of the present invention are normally two-component compositions that after mixing essentially consist of the following components in aqueous solution:
(a) from the first component:
(i) at least one omega-aminoalkyl trialkoxysilane;
(ii) at least one strong acid, in an amount sufficient to obtain a pH of 7 to 9;
(iii) at least one compound each having as terminal groups a trialkoxy or alkyldialkoxy silane and an epoxy group, in an amount such that the ratio of the amine hydrogen equivalent of the omega-aminoalkyl trialkoxysilanes to the epoxy equivalent of the said compound is of 3 to 7; the reaction of (i) to (iii) forming a binder;
(iv) one or more pigments, at least 25 wt % of which having conductive properties;
(b) from the second component:
(v) finely divided zinc, the weight ratio of zinc to pigments being of from 1:10 to 10:1;
the weight ratio of solid binder to the total of zinc and pigments being of 1:1 to 1:50.
Omega-aminoalkyl trialkoxysilanes (hereinafter the aminosilanes) may be represented by the general formula NH2—R′—Si(OR″)3; as used in organic chemistry, omega defines the terminal location for a substituent or function. R′ is an alkylene group, preferably containing 1 to 6 carbon atoms, more preferably 2 to 4, most preferably 3; also R′ is preferably a n-alkylene group. Each R″ is an alkyl group which may be the same or different, preferably containing 1 to 6 carbon atoms, more preferably 1 to 4, most preferably 2 or 3; also, R″ is preferably a n-alkyl group. The most preferred compound is 3-aminopropyl triethoxy silane.
As acid, there can be used any strong or relatively strong acid, preferably organic. Preferred acids include formic acid, acetic acid, oxalic acid and mixtures thereof. The most preferred acid is formic acid, which is one that contributes least organic matter among the organic acids. The amount of acid added must be such as to obtain a pH of 7 to 9, preferably of 7.5 to 8.5, most preferably of about 8.
Among the compounds having an epoxy terminal group and a trialkoxy silane terminal group (hereinafter the epoxysilanes), linear compounds are preferred. According to a preferred embodiment, there can be used any compound of general formula
CH2—O—C
H—R′—Si(OR″)3, with R′ and each R″ as above. According to another preferred embodiment, there is alternatively used a compound of general formula
CH2—O—C
H—R′—O—R′—Si(OR″)3, with each R′ (which may be the same or different) and each R″ as above. According to yet another preferred embodiment, there is used a compound of general formula
CH2—O—C
H—R′—Si R″(OR″)2 or
CH2—O—C
H—R′—O—R′—Si R″(OR″)2, wherein each R′ and each R″ is as above. The most preferred compounds are 3-glycidoxypropyl trimethoxy and triethoxysilane. The amount of epoxysilanes added is such that the ratio of the amine hydrogen equivalent of the aminosilane to the epoxy equivalent of the epoxysilane is of 3 to 7, preferably of 4 to 6, more preferably of 4.5 to 5.5, most preferably of about 5. Higher ratios decrease the water resistance of the coating, whereas lower ratios decrease the shelf life of the first component of the composition, without improving the water resistance of the coating.
Finely divided zinc is used as anti-corrosive agent, effective because of its galvanic action on the steel substrate. Zinc powder, zinc dust or zinc flakes can be used.
Conductive pigments improve both the anti-corrosive properties (by electrically connecting zinc particles with the substrate) and the arc welding properties. Examples of pigments known to have conductive properties include ferro alloy, di-iron phosphide, micaceous iron oxide types, copper flakes, nickel flakes, stainless steel flakes, aluminium flakes. Conductive pigments should represent at least 25 wt % of all pigments, preferably at least 40 wt %, more preferably at least 50 wt %.
The pigments may optionally comprise an amount of materials that can interact with the steel substrate, resulting e.g. in some inhibition or passivation of said substrate. This is assumed to slow the consumption of the finely divided zinc. Examples of pigments having such properties include molybdates, phosphates like calcium diphosphate, zinc phosphate, sodium potassium polyphosphate or aluminium polyphosphate, or borates like zinc metaborate or barium metaborate, or zinc oxide.
Pigments believed to be inactive are obviously not essential to the invention, but their inclusion in the composition is often desired, e.g. for economical reasons (fillers) or to provide the primer with a desired colour. As example of the numerous possible inactive pigments, it may be cited titanium dioxide, red iron oxide, calcium carbonate, talc, aluminium silicate, yellow iron oxide, and aluminium silicate.
The pigments are normally provided with the first component, wherein they have been previously dispersed.
The weight ratio of zinc to the total amount of pigments is of 1:10 to 10:1, preferably of 1:2 to 8:1, more preferably from 2:3 to 6:1, most preferably from 1:1 to 4:1.
The weight ratio of solid binder to the total of zinc and pigments is of
de Jong Jan
Nederlof Arnold Johan
van Vliet Cornelis Hubertus
van Zanten Cors Daniël
Goodwin & Procter LLP
Sigma Coatings B.V.
Wood Elizabeth
LandOfFree
Water-based two component protective coating compositions does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Water-based two component protective coating compositions, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Water-based two component protective coating compositions will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3232434