ABSTRACT:
TECHNICAL FIELD
The present invention pertains to the field of chemical vapor deposition of tin, titanium, and zinc oxides onto glass and other substrates, and to tin, titanium and zinc compounds useful therefor.
BACKGROUND ART
Tin oxide, titanium oxide, and zinc oxide films have been applied to glass substrates for a variety of purposes, notably as infrared absorbing coatings, and as transparent conductive electrodes for use in such devices as photovoltaic cells and dimmable mirror assemblies. In such applications, the physical, electrical, and optical characteristics of the metal oxide films are often critical. Among these characteristics are coating thickness, uniformity, smoothness, electrical conductivity or resistivity, spectral transmission, and optical clarity.
Tin oxide films have become commonplace. However, most applications involving SnO
2
films are relatively high product volume applications which require that the chemical vapor deposition (CVD) precursor tin compounds be inexpensive, and preferably stable. For titanium oxide and zinc oxide films, similar considerations apply. Thus, despite their ability to provide high quality films, numerous organometallic compounds of tin, titanium, and zinc cannot be used, either because they are too expensive or because of the dangers associated with use of highly flammable and toxic compounds in a commercial industrial setting.
Tin oxide and titanium oxide films have been prepared by contacting separate carrier gas streams containing tin tetrachloride or titanium tetrachloride and either water or an oxygen-containing compound which reacts with the metal halide at elevated temperatures. The streams are contacted with each other physically close to the substrate onto which the coating is to be deposited. These methods have not proven to be totally satisfactory, even though the tin halide/water reaction is widely used. Tin tetrachloride and titanium tetrachloride are volatile and highly reactive. However, the greatest difficulty with the use of metal halide/water to form metal oxide films is the formation of a fine dust or powder of tin oxide particulates in addition to the coherent metal oxide coating. The presence of these oxide particles necessitates the frequent shut down and cleaning of the coating apparatus.
For zinc oxide coating, dialkylzinc compounds have been used in conjunction with an oxidant such as water or an oxygen-containing organic compound, as disclosed in Vijayakumar et al. U.S. Pat. No. 4,751,149. Dialkylzinc compounds are highly reactive and spontaneously flammable in air. They react explosively with water. Thus, their use in large scale coating is highly problematic from a safety standpoint. Moreover, employing two separate reagent streams and allowing them to combine and react adjacent the substrate again produces particulates as well as the desired coherent film.
The foregoing methods have the additional disadvantage that the compositional nature of the film may change due to factors such as carrier gas flow, pressure, and temperature, as well as the concentration of the reactive ingredient in the carrier gas streams. With a constant ratio of reactive ingredients, films with relatively constant stoichiometry but varying smoothness and thickness may result due to variations in the foregoing carrier gas parameters. If the reactant ratios also vary, films of different stoichiometry, electrical, and optical properties will result. Examples of tin and titanium oxide films with varying properties prepared by different ratios of tin or titanium tetrachloride and organic carboxylic acid esters in separate gas streams is given in PCT published application WO 98/06675.
Use of single component tin oxide, titanium oxide, or zinc oxide CVD precursor systems requiring but one supply stream has thus far not met with success, either because of the cost of the organometallic precursors, or because the desired film thickness and uniformity cannot be achieved. In non-critical applications such as the surface modification of tempered hot glass, solutions of tin and titanium compounds dissolved in organic solvent have been used, the organic solvent also functioning as a potential oxidizing agent. Examples of tin and titanium oxide coatings to strengthen molded glassware, and formed by applying solutions of tin or titanium halide in excess organic esters of acetic, propionic, or butyric acids are given in Great Britain Patents GB 1,187,784 (1967; tin) and GB 1,187,783 (1967; titanium). The use of excess organic solvent renders these processes less ecologically desirable today. Moreover, application of the solutions by spraying renders precise control of film physical, chemical, and electrooptical parameters virtually impossible, and encourages carbon contamination. Thus, such coatings cannot be used for products such as dimmable mirrors and photovoltaic cells.
DISCLOSURE OF INVENTION
It has now been surprisingly discovered that novel ligated compounds of tin, titanium, and zinc can be used to prepare uniform, high quality metal oxide coatings on glass and other substrates without the use of separate reactant streams and without application in the form of a solution. These tin, titanium, and zinc compounds have exhibited high relative stability as compared to precursors such as tin tetrachloride, titanium tetrachloride and dialkylzinc.
BEST MODE FOR CARRYING OUT THE INVENTION
The tin and zinc compounds of the present invention have the formula MX
n
L
2
where M is Sn or Zn and L is a C
1-4
alkylformate, preferably ethylformate; X is Cl and n is 4 when M is Sn; and X is C
1-4
lower alkyl and n is 2, when M is Zn, with the proviso that when M is Sn, the ethylformate ligands are preferably positioned cis to each other. The preferred chemical vapor deposition compounds are
where R is —CH
3
or —CH
2
CH
3
. As will be discussed infra, these compounds are well characterized, easily synthesized, and form excellent coatings. The zinc compounds are far more stable then dialkylzinc compounds previously used to produce zinc oxide coatings; for example, rather than react explosively with water, they slowly react, liberating alkane gas in the process. The compounds are low melting solids or liquids which can easily accept dopant compounds, allowing a means of providing a stable, constant concentration of dopant atoms to the coating process rather than employ a yet further stream of dopant compound. Examples of C
1-4
alkyl groups in the alkyl formates include methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, and t-butyl alkyl groups.
Thus, in general, the tin and zinc compounds have the formula:
MX
n
L
2
where
M is Sn or Zn;
L is selected from the group consisting of methylformate, ethylformate, n-propylformate, i-propyl formate, n-butylformate, i-butylformate, t-butylformate, and mixtures thereof;
X is Cl and n is 4 when M is Sn; and
X is R and n is 2 when M is Zn,
where
R is C
1-8
lower alkyl or C
2-8
lower alkenyl; and
when M is Sn, the ethyl formate ligands are preferably positioned cis to each other.
The preferred tin compound may be prepared by contacting tin tetrachloride in the gas phase with gaseous ethyl formate, preferably in stoichiometric ratio (1:2, respectively). The contact is preferably performed at relatively low temperatures, i.e., at room temperature, and in an inert atmosphere, preferably a dry nitrogen atmosphere. Upon contact of the gas streams, large white crystals of the desired product immediately form. Alternatively, the reactants may be dissolved in a non-polar aprotic solvent such as hexane. The white crystalline product may be recovered by filtration. The compound is characterized by a melting point of 52-53° C.;
1
H NMR (CDCl
3
, ppm) 1.33 (t, 3H, CH
3
), 4.31 (q, 2H, CH
2
), 8.18 (S, 1H, CH);
13
C NMR (CDCl
3
, ppm) −0.02, 14.0, 61.5;
119
Sn NMR −823. The IR spectrum showed notable absorbance at 1717cm
−1
(KBr disk) and 1616 cm
−1
(gas phase). X-ray crystallography indicates a molecule with ethyl formate ligands occupying cis positions relative to each other.
The obtai
First Solar LLC
Fish & Richardson P.C.
Meeks Timothy
LandOfFree
Volatile organometallic complexes of lowered reactivity... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Volatile organometallic complexes of lowered reactivity..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Volatile organometallic complexes of lowered reactivity... will most certainly appreciate the feedback.