Vacuum degassing method for molten glass flow

Glass manufacturing – Processes – Fining or homogenizing molten glass

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C065S032500, C065S134900, C065S135100

Reexamination Certificate

active

06332339

ABSTRACT:

The present invention relates to a vacuum degassing method for molten glass flow capable of removing bubbles properly and effectively from a continuous flow of molten glass obtained by melting glass materials.
Heretofore, it has been common to utilize a refining procedure to remove bubbles generated in molten glass obtained by melting raw materials of glass in a melting furnace, prior to forming the molten glass by a forming apparatus, in order to improve the quality of formed glass products.
There has been known such a method that in the refining procedure, a refining agent such as sodium sulfate (Na
2
SO
4
) is previously added to raw materials of glass and the molten glass obtained by melting the raw materials containing a refining agent is stored and maintained at a predetermined temperature for a predetermined period, during which bubbles in the molten glass grow by the help of the refining agent, rise to the molten glass surface, and the bubbles are removed.
Further, there has been known a vacuum degassing method wherein molten glass is introduced into a vacuum atmosphere under a reduced pressure; under such reduced pressure condition, bubbles in a continuous flow of molten glass grow up and rise to the molten glass surface at which bubbles break and are removed, and the molten glass is taken out from the vacuum atmosphere.
In the above-mentioned vacuum degassing method, the molten glass flow is formed under a reduced pressure wherein bubbles contained in the molten glass grow in a relatively short time and rise to the surface by using buoyancy of the grown-up bubbles in the molten glass, followed by breaking the bubbles on the surface of the molten glass. In this way, the method can remove bubbles effectively from the molten glass surface. In order to remove bubbles effectively from the molten glass surface, it is necessary to provide a high rising velocity of bubbles so that the bubbles come to the molten glass surface under a reduced pressure condition. Otherwise, the bubbles are discharged along with the molten glass flow, with the result that a final glass product contains bubbles and is defective.
For this reason, it is considered that the pressure in the reduced pressure atmosphere for vacuum degassing should be small as possible to grow up bubbles and the rising velocity be increased whereby the effect of vacuum degassing is improved.
However, when the pressure in the reduced pressure atmosphere for vacuum degassing is lowered, numerous new bubbles sometimes generate in the molten glass and the bubbles rise to the molten glass surface to form a floating foam layer without breaking. A part of the foam layer may be discharged along with the molten glass flow to result a defect in the glass product. When a foam layer grows, the temperature of the upper surface of the molten glass decreases. The foam layer tends to hardly break whereby the foam layer will further develop. As a result, the inside of the vacuum degassing apparatus is filled with non-breaking bubbles. The foam layer fully filling the apparatus may be in contact with impurities on the ceiling of the apparatus; thus, it brings the impurities in the final glass product. Consequently, excessively lowering the pressure in the atmosphere for vacuum degassing is not preferred for an effective treatment for vacuum degassing.
Further, the rising velocity of the bubbles in molten glass is determined by the viscosity of the molten glass as well as the size of the bubble. Accordingly, it is considered that the lowering of the viscosity of the molten glass, or the raising of the temperature of the molten glass can raise bubbles to the surface effectively. However, when the temperature of the molten glass is excessively raised, there causes an active reaction with the material of flow path, such as refractory bricks, with which the molten glass contacts. It may lead to occurrence of new bubbles and dissolution of a part of material of the flow path into the molten glass, thus resulting in deterioration of the quality of glass products. Further, when the temperature of the molten glass is raised, the strength of the material of the flow path is decreased, whereby the service life of the flow path is shortened and an extra equipment such as a heater for maintaining the high temperature of the molten glass is required. As a result, in order to conduct a proper and effective vacuum degassing treatment, it is difficult to lower excessively the pressure for vacuum degassing and also to raise excessively a temperature of the molten glass.
In the vacuum degassing method where several restrictions are imposed, the following conditions for effective degassing has been reported(SCIENCE AND TECHNOLOGY OF NEW GLASSES, Oct. 16-17, 1991, pages 75-76).
In a vacuum degassing apparatus
40
for carrying out a vacuum degassing method for a molten glass flow as shown in
FIG. 4
, the number of bubbles (bubble density) in molten glass decreases to about {fraction (1/1,000)}, when molten glass at 1,320° C. is passed in the apparatus at a flow rate of 6 [ton/day] wherein a pressure in a vacuum degassing vessel
42
is 0.18 atom (136.8 mmHg) and a staying time of the molten glass in the vacuum degassing vessel
42
under such a reduced pressure atmosphere is 50 minutes.
Namely, the above-mentioned vacuum degassing treatment is conducted in a bench scale type vacuum degassing apparatus
40
in the following way. The molten glass obtained by melting raw materials of glass is introduced from an upstream pit
47
into the vacuum degassing vessel
42
under a reduced pressure via an uprising pipe
44
by a vacuum pump (not shown), whereby a molten glass flow is formed in a substantially horizontal direction. Then, the molten glass is passed in the vacuum degassing vessel
42
under a reduced pressure to remove the bubbles in the molten glass, and then, the molten glass is fed via a downfalling pipe
46
to a downstream pit
48
where the temperature of the molten glass is maintained to have the viscosity of 1,000 poises.
The molten glass is sampled at the inlet of the uprising pipe
44
and the outlet of the downfalling pipe
46
to check the bubble density contained in each sample of the molten glass. As a result, the bubble density contained in the molten glass in the upstream pit
47
prior to a vacuum degassing is 150 [number/kg] and the bubble density contained in the molten glass in the downstream pit
48
is 0.1 [number/kg]. Thus, it is recognized that the number of the bubbles decreases to about {fraction (1/1,000)}. It is also reported that a foam layer is not formed on the molten glass surface, although the pressure in the vacuum degassing vessel
42
is set to be low level as 0.18 atom.
The above-mentioned report discloses the vacuum degassing method wherein an effective vacuum degassing is attained when a pressure in the vacuum degassing vessel
42
is 0.18 atom (136.8 mmHg) and a staying time in the vacuum degassing vessel
42
is 50 minutes. However, it does not disclose various condition requirements for the vacuum degassing in order to obtain effectively superior results of vacuum degassing.
In particular, a vacuum degassing treatment should be carried out within a relatively short time under a reduced pressure atmosphere. Accordingly, under such conditions where the pressure in the reduced atmosphere can not be lowered excessively and the temperature of the molten glass can not be excessively high, as mentioned above, it is important to determine a staying time of the molten glass flow under the reduced pressure atmosphere.
The longer the staying time of the molten glass flowing in the vacuum degassing vessel
42
, the uprising pipe
44
and the downfalling pipe
46
, the lower the bubble density of the molten glass after vacuum degassing treatment.
In order to elongate the staying time of the molten glass under a reduced pressure atmosphere, it is considered to extend the length of flow path of the molten glass in a flow direction. However, this causes practical problems such as a remarkable incre

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Vacuum degassing method for molten glass flow does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Vacuum degassing method for molten glass flow, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Vacuum degassing method for molten glass flow will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2599008

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.