ABSTRACT:
TECHNICAL FIELD AND INDUSTRIAL APPLICABILITY OF THE INVENTION
The present invention is related generally to bituminous coating materials, and more particularly to a method of improving the weathering of a bituminous coating material.
BACKGROUND OF THE INVENTION
Bituminous coating materials are used in many different outdoor applications to provide protection from the weather. For example, asphalt-based coating materials are used in roofing products such as roofing shingles, built-up roofing and roll roofing to protect the underlying building from rain and sunlight. Over an extended period of time, exposure of the coating material to the weather may cause deterioration of the coating material, such as brittleness and cracking. Therefore, it would be desirable to provide a method of improving the weathering of bituminous coating materials.
Carbon black obtained from conventional combustion processes has been used in plastics for resistance to UV radiation. It has also been added to roofing and paving asphalts to increase the stiffness of the asphalt, most probably through filler-filler interactions of the carbon black particles. However, in such prior uses in roofing and paving asphalts, addition of conventional carbon black to asphalt-based coating materials has been shown not to improve the weathering of the coating materials.
Several patents describe carbon black produced by microwave heating, but there is no suggestion in the patents to use the carbon black to improve the weathering of bituminous coating materials. For example, U.S. Pat. No. 6,152,306 to Miller discloses a process in which solid waste is reduced to carbon black and oil by heating the waste with microwave energy and externally applied heat. The carbon black is used for energy purposes or as feedstock. U.S. Pat. No. 4,647,443 to Apffel discloses a process for recovering carbon black from used vehicle tires, including a conventional pyrolysis step followed by a microwave heating step. The carbon black is used as a feed stock to make new tires. U.S. Pat. No. 5,364,821 to Holland discloses a method of producing active carbon by microwave heating a carbonaceous material. The active carbon is used for filtration of liquids.
SUMMARY OF THE INVENTION
The above object as well as others not specifically enumerated are achieved by a method of improving the weathering of a bituminous coating according to the invention. The method comprises adding to the bituminous coating a microwave-produced carbon black in an amount sufficient to increase the cycles-to-failure of the coating by at least about 10% compared to the same coating without the added microwave-produced carbon black, when tested for weathering according to ASTM D 4799-00.
In another embodiment of the invention, the method comprises adding to the bituminous coating a microwave-produced carbon black in an amount sufficient to increase the cycles-to-failure of the coating by at least about 10% compared to the same coating containing a conventional carbon black (Industry Reference Black 7) in place of the microwave-produced carbon black.
The invention also relates to a bituminous coating material with improved weathering properties. The coating contains a bituminous coating material and a microwave-produced carbon black added in an amount sufficient to increase the cycles-to-failure of the coating by at least about 10% compared to the same coating without the added microwave-produced carbon black, when tested for weathering according to ASTM D 4799-00.
Various objects and advantages of this invention will become apparent to those skilled in the art from the following detailed description of the preferred embodiments.
DETAILED DESCRIPTION AND PREFERRED EMBODIMENTS OF THE INVENTION
Conventional carbon black has been tested numerous times to determine if its addition improves the weathering of asphalt-based coating materials, and uniformly it has not shown an improvement in weathering when testing the coating material using the Weatherometer test (ASTM Test Method D 4799-00). However, unlike conventional carbon black, it has been discovered that the addition of even a small amount of microwave-produced carbon black to a bituminous coating material substantially improves its weathering under this test.
In the method of the present invention, microwave-produced carbon black is added to a bituminous coating material in an amount sufficient to increase the cycles-to-failure of the coating material by at least about 10% compared to the same coating material without the added microwave-produced carbon black, and preferably at least about 15%. The cycles-to-failure of the coating material is measured by testing it for weathering according to ASTM D 4799-00, “Standard Test Method for Accelerated Weathering Test Conditions and Procedures for Bituminous Materials (Fluorescent UV and Condensation Method)”, published March 2000. Using Cycle A of the test method, the coating material is exposed to cycles of four hours of UV light at 60° C., alternating with fours hours of condensation at 50° C. The cycles are continued until the coating material fails due to cracking as determined by ASTM Test Method D 1670.
In a related embodiment of the invention, microwave-produced carbon black is added to a bituminous coating material in an amount sufficient to increase the cycles-to-failure of the coating material by at least about 10% compared to the same coating material containing a conventional carbon black in place of the microwave-produced carbon black, and preferably at least about 15%. For purposes of comparison, the conventional carbon black is defined as an Industry Reference Black 7, which is a standard reference carbon black that can be used to achieve good agreement with standard ASTM test comparisons. The Industry Reference Black 7 is commercially available from Laboratory Standards and Technologies, LLC, 227 Somerset Street, Borger, Tex. 79007.
The addition of the microwave-produced carbon black improves the weathering of the bituminous coating material even at low addition levels where particle-particle interactions of the carbon black particles provide no stiffening or other mechanical benefits to the coating material. For example, the microwave-produced carbon black improves the weathering when added in an amount within a range between about 0.5% and about 10% by weight, preferably within a range between about 0.5% and about 8% by weight, and more preferably within a range between about 1% and about 5% by weight. The addition of the microwave-produced carbon black at a level of about 2% by weight has improved the weathering of the coating material by about 15%. Amounts of microwave-produced carbon black greater than about 10% could also be used. The given weight percentages are by total weight of the bituminous coating material, excluding any filler in the coating material.
The microwave-produced carbon black is carbon black that is produced at least primarily by the application of microwave energy (greater than 50% microwave energy), although other forms of heat energy can also be applied. Preferably, the carbon black is produced substantially solely by the application of microwave energy. The microwave-produced carbon black is usually produced by applying microwave energy to an organic material in a reducing atmosphere to break down the organic material and produce carbon black and oil. The reducing atmosphere is an oxygen-poor atmosphere in which the organic material is broken down by heat alone, with substantially no oxidation (burning). Preferably, the mass temperature of the organic material remains below about 700° F. (371° C.) during the process of applying the microwave energy.
Substantially any type of organic material can be used as the raw material. Preferably, the organic material is selected from municipal solid waste, waste tires, carpet waste, fluff organics from vehicle recycling, and mixtures thereof. Most preferably the organic material is waste tires.
A preferred microwave-produced carbon black for use in the invention is commercially available as “MICAR
Jones, IV David R.
Trumbore David C.
Brunsman David
Dottavio James J.
Eckert Inger H.
Owens Corning Fiberglas Technology Inc.
LandOfFree
Use of microwave-produced carbon black to improve weathering... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Use of microwave-produced carbon black to improve weathering..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Use of microwave-produced carbon black to improve weathering... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3009914