ABSTRACT:
FIELD OF THE INVENTION
The present invention relates to the field of semiconductor devices and semiconductor processing. More particularly, the present invention relates to methods of suppressing or eliminating transient enhanced diffusion (TED) of ion implanted dopant impurities in semiconductor substrates. Even more particularly, the present invention relates to reduction or elimination of TED of ion implanted p- or n-type dopant impurities in silicon semiconductor substrates.
BACKGROUND OF THE INVENTION
The escalating requirements for high density and performance associated with ultra-large-scale integration (ULSI) semiconductor devices require design features of 0.18 &mgr;m and below, such as 0.15 &mgr;m below, increased transistor and circuit speeds, high reliability, and increased manufacturing yield and throughput for economic competitiveness. The reduction of design features to 0.18 &mgr;m and below challenges the limitations of conventional semiconductor manufacturing techniques.
The abovementioned continuing trend toward greater microminiaturization of semiconductor devices has engendered a need for reduced junction depths of integrated circuit components, e.g., transistors, to between about 70-100 nm. A problem confronting the achievement of such shallow junction depths is transient enhanced diffusion (“TED”), i.e., redistribution of implanted dopant impurities during thermal annealing following ion implantation of the dopant.
In semiconductor device fabrication, dopant containing impurities, i.e., n- and/or p-type dopant impurities, are introduced into the semiconductor material to alter its electrical conductivity characteristics. A preferred technique for use in high-density integration semiconductor devices is ion implantation. During ion implantation, a beam containing ions is directed at the surface of the semiconductor substrate material (i.e., target). As the ions enter the substrate material, they collide with the atoms constituting the target material and come to rest at an average depth within the substrate. The average depth at which the implanted ions are distributed varies with the implant energy, size (i.e., radius) of the implanted species, and the target material. For a given target material and ion species, higher implantation energy generally corresponds to a deeper penetration of the ions into the material. The implantation dose (i.e., total number of ions entering the target material) is controlled by monitoring the ion current during implantation as well as the duration thereof.
However, ion implantation incurs undesirable side effects. For example, during implantation the impinging ions displace target atoms, thereby creating damage in the crystal lattice structure of the target. Such damage typically is in the form of vacancies (i.e., holes or vacant lattice sites) and interstitials (i.e., atoms occupying interstices between normal lattice sites), which are referred to as point defects. In extreme instances, the lattice damage is severe enough to transform the semiconductor target into an amorphous material.
As for silicon target material, ion implantation is the preferred technique for introducing p- and n-type dopant species, such as boron and phosphorus, respectively. The atomic collisions which occur during the implantation process create large numbers of the above-described point defects, including silicon interstitials produced by displacement of silicon atoms from their normal sites in the crystal lattice. Some of these defects agglomerate into small extended defects, such as rod-like interstitial defects that tend to orient along the (113) crystal direction. During the post-implantation thermal annealing step, the silicon interstitials (Si
I
) that are released from such agglomerates promote a rapid redistribution of the implanted dopant atoms, particularly p-type boron atoms. Redistribution occurs because silicon interstitials interact with substitutional boron atoms, thereby replacing the boron atoms and resulting in highly mobile boron interstitials (B
I
). The resulting redistribution of dopant caused by an increase in the effective diffusion rate of the dopants during the first few seconds of thermal annealing treatment is known as TED. In some instances, TED increases the diffusion rate by a factor of 10 to 100.
TED makes it difficult, if not impossible, to control implanted boron depth distribution in silicon targets. As a consequence, p-junction depth cannot be controlled by simply reducing the boron ion implantation energy (and thus the range of ion penetration into the silicon crystal lattice). Moreover, high temperature cycles, such as are encountered during annealing for activation of implanted dopant and lattice damage relaxation, can cause appreciable diffusion of the dopants, thereby significantly altering the dopant impurity concentration profiles, which effects are disadvantageously exacerbated by TED. Moreover, with the reduction of device sizes to the submicron range, there is a further need for close control of dopant diffusion. Techniques such as rapid thermal annealing (RTA) have been used to reduce undesirable diffusion of dopants during repair of implant damage. RTA refers to various techniques for heating the implanted target material for short periods of time, e.g., on the order of seconds.
However, even when RTA is utilized, TED has been observed during the post-implant annealing process. As indicated above, TED makes it difficult to control the implant profile. In the past, this was not a significant concern because the diffusion of dopants attributable to TED was considered to be within tolerable limits. But as technology now enables reduction of device sizes to below submicron dimensions, the effects of TED have become more pronounced and cannot be disregarded. For example, in MOS devices, lateral diffusion of the source and drain implants adversely affects the threshold-adjust implant at the gate region even though these regions are separated by, for example, several tenths of a micron. This results in an increase in gate threshold voltage V
T
which controls the conduction path between the source and drain as device size decreases (i.e., reverse short-channel effect). TED also causes impurity atoms to accumulate at the target surface in high concentration. This accumulation degrades channel mobility as it inhibits the movement of electrons between the source and the drain, thereby decreasing the speed of the resultant device. In addition, submicron-dimensioned devices require ultra-shallow junctions having depths of, e.g., less than 1000 Å to maintain low contact resistance. Vertical diffusion of dopants resulting from TED makes it difficult to achieve the shallow implant profiles necessary for such devices.
U.S. Pat. No. 5,670,391 issued Sep. 23, 1997 is directed to a process for fabricating a semiconductor device which includes a step for reducing the enhanced diffusion of dopant atoms that occurs during post-implant anneal. Prior to annealing the substrate wafer, the surface of the ion implanted region is etched to bring it closer to the level of the implant damage. The etch process is preferably controlled to prevent etching the surface significantly beyond the peak of the dopant concentration profile in order to avoid removing a significant portion of the implanted dopant. By bringing the implanted surface closer to the implant damage, the effects of TED during post-implant annealing are reduced.
U.S. Pat. No. 5,759,904 issued Jun. 2, 1998 discloses a method for suppressing TED of ion-implanted dopants in a semiconductor substrate comprising bombarding the substrate in a vacuum with a beam of bubble-forming ions at a first temperature, a first energy, and a first ion dose sufficient to form a dispersion of bubbles at a depth equivalent to a peak of lattice damage distribution in the substrate from implantation of dopant ions into the substrate in a vacuum at a second temperature, a second energy, and a second ion dose, the dispersion of bubbles being sufficient to reduce TED of the implanted
Advanced Micro Devices , Inc.
Niebling John F.
Roman Angel
LandOfFree
Use of knocked-on oxygen atoms for reduction of transient... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Use of knocked-on oxygen atoms for reduction of transient..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Use of knocked-on oxygen atoms for reduction of transient... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2841815