ABSTRACT:
BACKGROUND OF THE INVENTION
a) Field of the Invention
The present invention relates to techniques of supplying ultra fine particles of ceramic, metal and the like not larger than about 1 &mgr;m to a substrate to form a ultra fine particle film. Such techniques of forming a ultra fine particle film are applied to the technical fields of forming a functional ceramic thin film, a metal thin film or the like on a substrate.
b) Description of the Related Art
As one of techniques of forming a ultra fine particle film, it is known to mix ultra fine particles with transport gas and spray the particles mixed with the transport gas from a nozzle toward a substrate surface to form a ultra fine particle film.
This conventional ultra fine particle film forming method is, however, associated with some problems that the film surface is not smooth and flat and the density of the film is not uniform. Specifically, with the conventional ultra fine particle film forming method, if ultra fine particles contain defective particles (such as particles having a diameter of 1 &mgr;m or larger and insufficiently accelerated particles) unable to physically form a film, these defective particles are mixed in a deposit on a substrate.
More specifically, if ultra fine particles jetted out during a film deposition contain a particle (defective particle)
31
having a large particle diameter or an insufficient speed, as shown in a schematic diagram of
FIG. 9A and a
microscopic photograph shown in
FIG. 10A
, the large diameter defective particle
31
attaches to and sinks in the surface layer of a deposit
32
under growth, and this defective particle
31
functions as a mask so that deposition does not occur thereafter on the surface of this defective particle
31
. As shown in
FIGS. 9A and 10B
, the film
33
after cleaning has a depression
34
. As shown in a microscopic photograph of
FIG. 11
, the film surface is very rough, which adversely affects later deposition. Since the defective particle is in a floating state in the deposit
32
, the film is not dense and the surface of the deposit is abraded by ultra fine particles to be later blown toward the surface. Also in this case, as shown in
FIG. 9B
, the film
33
has a depression
34
and the film surface is very rough, which adversely affects later deposition. If such a conventional film forming method is applied to forming a ceramic electronic component which is required to have a homogeneously controlled fine structure of the film, excellent electrical characteristics cannot be expected.
It is also practically difficult to make the amount of fine particles to be jetted out of a nozzle uniform and constant, so that the film thickness changes at positions. It is also difficult to control a film thickness and a surface uniformity, which becomes a large obstacle against forming films having uniform performance and good film quality. Such irregular film thickness and surface roughness become a critical issue when the conventional method is applied to forming an optical thin film.
It has been desired to provide techniques of forming a ultra fine particle film which has ultra fine particles sufficiently bonded together, sufficient density, flat surface and uniform density.
SUMMARY OF THE INVENTION
The invention has been made under such circumstances. It is an object of the present invention to provide a ultra fine particle film forming apparatus capable of forming a ultra fine particle film which has ultra fine particles sufficiently bonded together, sufficient density, and particularly flat surface and uniform density.
In order to achieve the above object of the invention, there is provided a planarized ultra fine particle film forming method for forming a planarized ultra fine particle film from a deposited film of ultra fine particles formed by supplying the ultra fine particles to a substrate, the method comprising one or more of a planarizing step of planarizing a surface of the deposited film of the ultra fine particles supplied to the substrate.
According to another aspect of the invention, there is provided a planarized ultra fine particle film forming apparatus for forming a planarized ultra fine particle film from a deposited film of ultra fine particles formed by supplying the ultra fine particles to a substrate, the apparatus comprising at least one of: an attached particle removal apparatus for rolling or scraping a surface layer portion of the deposited film of the ultra fine particles supplied to the substrate; a film surface processing apparatus for grinding or polishing the surface layer portion; and a pressure apparatus for pressing the deposited film.
According to another aspect of the invention, there is provided a planarized ultra fine particle film forming method for forming a planarized ultra fine particle film from a deposited film of ultra fine particles formed by supplying the ultra fine particles to a substrate, the method comprising one or more of a planarizing step of planarizing a surface of the deposited film of the ultra fine particles by blowing planarizing fine particles having a grinding/polishing function at an oblique incidence angle toward the surface of the deposited film.
According to another aspect of the invention, there is provided a planarized ultra fine particle film forming apparatus for forming a planarized ultra fine particle film from a deposited film of ultra fine particles formed by supplying the ultra fine particles to a substrate, wherein planarizing fine particles having a grinding/polishing function are blown at an oblique incidence angle toward the surface of the deposited film.
REFERENCES:
patent: 5116561 (1992-05-01), Kagawa
patent: 5830568 (1998-11-01), Kondo
patent: 5981305 (1999-11-01), Hattori
patent: 6235118 (2001-05-01), Hayashi
patent: 6329061 (2001-12-01), Kondo
patent: 6531187 (2003-03-01), Akedo
patent: 6579608 (2003-06-01), Kondo
Akedo et al. “Jet Molding System for Realization of Three-Dimensional Micro-Structures”, Sensors and Actuators A69, 1998, 106-112.
JP-A-10-208998 Aug. 13, 1999 2963993.
JP-A-11-117328.
Agency of Industrial Science and Technology
Farber Martin A.
Rachuba M.
LandOfFree
Ultra fine particle film forming method and apparatus does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Ultra fine particle film forming method and apparatus, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Ultra fine particle film forming method and apparatus will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3319159