Plastic and nonmetallic article shaping or treating: processes – Pore forming in situ – By gas forming or expanding
Patent
1997-06-09
1999-09-21
Kuhns, Allan R.
Plastic and nonmetallic article shaping or treating: processes
Pore forming in situ
By gas forming or expanding
264 55, 264146, B29C 4402
Patent
active
059550155
DESCRIPTION:
BRIEF SUMMARY
TECHNICAL FIELD
The present invention relates to the production of polyolefin foam and similar materials.
More particularly, although not exclusively, the present invention relates to processes and apparatus for the production of polyolefin foams, polyolefin foam intermediate products and moulding processes for polyolefin foam.
BACKGROUND TO THE INVENTION
Polyolefin foams are produced by modifying a raw polymer material by introducing a dispersed-gas phase into the structure of the polymer. This process is conventionally performed by dispersing a blowing agent and cross-linking agents into a polymer melt and exposing the resulting compound to an environment where the blowing agent decomposes thereby releasing the gas and expanding the polymer.
Cross linking modifies the physical characteristics of the expanded foam product, the primary characteristics being the cell size and degree of cell closure.
To the present time, methods of producing polyolefin foam include forming calendered or otherwise preformed flat sheets which are then expanded in a one or two stage process. The sheets are heated in a mould to activate a decomposable, gas-releasing blowing agent. This process will cause the calendered or otherwise formed sheets to expand to up to approximately twenty times their original volume.
The heating and subsequent blowing agent activation step may be carried out in two steps using two different sized moulds. The sheets may be blown in one mould to an intermediate size following which they are blown to their final size in a second mould. The intermediate moulding step helps limit the stresses produced in the foam during the expansion process. The sheets must be blown in restraining moulds as flat sheets distort during blowing by expanding more in the centre and along the long sides. This is due to variations in surface tension of the foam surface. Surface tension effects are less significant in these regions than at the corners.
Other techniques include single step extrusion of planks, rounds and special purpose profiles. In this process, the extrusion of the polymer-blowing agent mixture is conventional, however before the mixture is allowed to expand it is passed through, for example, an annular channel. As the mixture leaves the channel, it is expanded. The product can be expanded to useful volumes, however the extruded product incorporates integral nonexpanded skins which can reduce the overall density by about a half.
Further objects and advantages of the invention will become apparent from the following description which is given by way of example only.
The object of the present invention is to provide alternative methods and apparatus for producing moulded polyolefin foams, said methods and apparatus having reduced energy requirements compared to conventional processes and employing a simplified and compact mould construction requiring reduced clamping pressures or to at least provide the public with a useful choice.
DISCLOSURE OF THE INVENTION
According to a first aspect of the invention there is provided a process for the production of foams including: formed by either moulding or extruding a compounded material.
Preferably the unexpanded material includes a polymer, blowing agent, cross-linking agent, and blowing agent activator.
Preferably the process for the production of foams further comprises: cylindrical tube is confined in a mould having a substantially annular cavity.
In an alternative embodiment, the blowing agent undergoes at least partial decomposition while the material is heated in the mould.
Preferably the preformed cylindrical tube of material is at least partially cross-linked while being heated in the mould.
Preferably the at least partial cross-linking can be controlled by rapid cooling of the mould.
Preferably the process for the production of foams further comprises:
Preferably the material is expanded or blown free of expansion constraints in a hot air oven or similar environment.
Preferably the preformed tubes are expanded or blown while oriented with their longitud
REFERENCES:
patent: 620286 (1899-02-01), Dodge
patent: 3812225 (1974-05-01), Hosoda et al.
patent: 4048275 (1977-09-01), Usamoto et al.
patent: 4073844 (1978-02-01), Wada et al.
patent: 4102966 (1978-07-01), Duperray et al.
patent: 4282277 (1981-08-01), Austen et al.
patent: 4367185 (1983-01-01), Nojiri et al.
patent: 4435346 (1984-03-01), Ito et al.
patent: 4578231 (1986-03-01), Molteni
patent: 4671910 (1987-06-01), Fuhrmann
patent: 4867923 (1989-09-01), Topcik et al.
patent: 4882108 (1989-11-01), Nakajima et al.
patent: 4900490 (1990-02-01), Kozma
patent: 4973609 (1990-11-01), Browne
patent: 5043115 (1991-08-01), Aoshima et al.
patent: 5071886 (1991-12-01), Aoshima et al.
patent: 5242634 (1993-09-01), Matsumoto et al.
patent: 5281377 (1994-01-01), Iwano et al.
patent: 5700407 (1997-12-01), Branger
Jackson Kevin
Scott Anthony J
Evolution Foam Moldings Limited
Kuhns Allan R.
LandOfFree
Two-stage process for making foam mouldings from tube blanks does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Two-stage process for making foam mouldings from tube blanks, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Two-stage process for making foam mouldings from tube blanks will most certainly appreciate the feedback.