Dynamic magnetic information storage or retrieval – Head – Magnetoresistive reproducing head
Reexamination Certificate
2000-03-30
2002-11-19
Nguyen, Hoa T. (Department: 2652)
Dynamic magnetic information storage or retrieval
Head
Magnetoresistive reproducing head
C428S141000
Reexamination Certificate
active
06483675
ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a tunnel magnetoresistance effect element. The ferromagnetic tunnel magnetoresistance effect element is, among magnetoresistance effect films for reading the magnetic field intensity of a magnetic recording medium or the like as a signal, an element which is capable of reading a small magnetic field change as a greater electrical resistance change signal. The ferromagnetic tunnel magnetoresistance effect element is mainly incorporated in, for example, a hard disk drive.
2. Description of the Related Art
Following the high densification of hard disks (HD), highly sensitive magnetic heads with high outputs have been demanded. In response to these demands, attention has been paid to a ferromagnetic tunnel magnetoresistance effect element having a multilayered structure composed of ferromagnetic layer/tunnel barrier layer/ferromagnetic layer, which utilizes a ferromagnetic tunnel magnetoresistance effect.
The ferromagnetic tunnel magnetoresistance effect is a phenomenon that when a current is applied in a laminate direction between a pair of ferromagnetic layers which sandwich a tunnel barrier layer, a tunnel current flowing in the tunnel barrier layer changes depending on a relative angle of magnetization between both ferromagnetic layers.
In this case, the tunnel barrier layer is a thin insulation film which allows electrons to pass therethrough while keeping spins of the electrons due to the tunnel magnetoresistance effect. Generally, the tunnel barrier layer is obtained by oxidizing a thin metal, such as Al, layer of about 10 Å in thickness.
When the relative angle of magnetization between both ferromagnetic layers which sandwich the tunnel barrier layer therebetween is decreased, the tunneling probability is increased and, therefore, the resistance to current flowing therebetween is decreased. In contrast, when the relative angle of magnetization between both ferromagnetic layers is large, the tunneling probability is lowered, thus, the resistance to current flowing therebetween is increased.
When applying the TMR element to a HDD head, it is essential to lower the electrical resistance of the element. The reason is as follows: Specifically, the resistance of a TMR element is basically expressed by the following equation (1).
R
&sgr;
=C
&sgr;
exp(2
&kgr;d
) (1)
&kgr;=(2
m&phgr;/h
2
)
½
wherein d represents a thickness of a barrier layer, &phgr; represents a magnitude of a barrier potential measured from the Fermi level, and C
&sgr;
represents an amount determined by an electron state of an insulation layer and magnetic layers, and may be considered to be an amount which is approximately proportional to the product of the Fermi levels of the two magnetic layers.
According to the forgoing equation (1), it is understood that lowering of the resistance of the element can be achieved by reducing the thickness d of the barrier layer. By reducing the resistance of the element, a larger current is allowed to supply, thus, a greater output can be achieved. In addition, in order to eliminate Electro-Static Discharges, it is desirable to lower the resistance of the element.
However, when decreasing the thickness d of the barrier layer, it is expected that the surface condition of the barrier layer should be highly smoother. When the surface is not smooth enough while the thickness of the barrier layer is thin, pinholes are apt to occur in a portion of the barrier layer, and a leakage current may occur through the pinholes. When the leakage current occurs, the greater output can not be achieved. Further, an output may not be obtained when an amount of leakage current is too large.
Under the foregoing circumstances, a feasibility study for realizing a tunnel magnetoresistance effect element including a head configuration has not been sufficiently achieved, though such a feasibility study is in the initial stage. Particularly, a standard specification for surface roughness of a tunnel barrier layer to significantly improve a head output has not been proposed.
The present invention has been made under these circumstances and has an object to provide a standard specification for a tunnel barrier layer to obtain improved characteristics of a tunnel magnetoresistance effect element, particularly to achieve a high head output.
SUMMARY OF THE INVENTION
For solving the foregoing problems, according to one aspect of the present invention, there is provided a tunnel magnetoresistance effect element comprising a tunnel multilayered film having a tunnel barrier layer, a ferromagnetic free layer and a ferromagnetic pinned layer such that the tunnel barrier layer is held between the ferromagnetic free layer and the ferromagnetic pinned layer, wherein three indexes representing a surface roughness state of the tunnel barrier layer are set such that Ra≦1 nm, Rmax≦10 nm and Rrms≦1.2 nm, wherein Ra is one of the three indexes and representing the center line average roughness, Rmax is one of the three indexes and representing the maximum height, and Rrms is one of the three indexes and representing the standard deviation roughness.
According to another aspect of the present invention, there is provided a magnet-resistive tunnel junction head comprising a tunnel magnetoresistance effect element which includes a tunnel multilayered film having a tunnel barrier layer, a ferromagnetic free layer and a ferromagnetic pinned layer such that the tunnel barrier layer is held between the ferromagnetic free layer and the ferromagnetic pinned layer, wherein three indexes representing a surface roughness state of the tunnel barrier layer are set such that Ra≦1 nm, Rmax≦10 nm and Rrms≦1.2 nm, wherein Ra is one of the three indexes and representing the center line average roughness, Rmax is one of the three indexes and representing the maximum height, and Rrms is one of the three indexes and representing the standard deviation roughness.
It is preferable that the center line average roughness Ra is set to be in the range of 0.001 nm to 1 nm, the maximum height Rmax is set to be in the range of 0.01 nm to 10 nm, and the standard deviation roughness Rrms is set to be in the range of 0.001 nm to 1.2 nm.
It is preferable that the tunnel magnetoresistance effect element comprises the ferromagnetic free layer, the tunnel barrier layer, the ferromagnetic pinned layer and a pinning layer for pinning magnetization of the ferromagnetic pinned layer, which are stacked, in the order named, on an under layer formed on a substrate.
It is preferable that the tunnel magnetoresistance effect element comprises a pinning layer for pinning magnetization of the ferromagnetic pinned layer, the ferromagnetic pinned layer, the tunnel barrier layer and the ferromagnetic free layer, which are stacked, in the order named, on an under layer formed on a substrate.
It is preferable that the surface of one of the layers which have been formed before forming the tunnel barrier layer is smoothed by a gas cluster ion beam method.
It is preferable that before forming the tunnel barrier layer, the surface of an under layer is smoothed by a gas cluster ion beam method.
It is preferable that a bias magnetic field is applied to the ferromagnetic free layer in a longitudinal direction thereof by biasing means provided at both ends of the ferromagnetic free layer in the longitudinal direction thereof.
It is preferable that the ferromagnetic free layer is a synthetic ferrimagnet.
It is preferable that the ferromagnetic pinned layer is a synthetic ferrimagnet.
It is preferable that the tunnel multilayered film is electrically connected to a pair of electrodes which are oppositely positioned to sandwich the tunnel multilayered film therebetween.
It is preferable that a pair of shield layers are oppositely positioned to sandwich the pair of electrodes therebetween.
REFERENCES:
patent: 5366815 (1994-11-01), Araki et al.
patent: 5510172 (1996-04-01), Araki et al.
patent: 5514452 (1996-05-01), Araki et al.
patent: 5657190
Araki Satoru
Morita Haruyuki
Shimazawa Koji
Nguyen Dzung C.
Nguyen Hoa T.
Oblon & Spivak, McClelland, Maier & Neustadt P.C.
TDK Corporation
LandOfFree
Tunnel magnetoresistance effect element does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Tunnel magnetoresistance effect element, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Tunnel magnetoresistance effect element will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2959757