ABSTRACT:
This invention relates to tunnel boring and-to-compositions for use therein.
Earth-pressure balance shield tunnel boring machines (EPBS) are increasingly frequently used in the boring of tunnels in non-rock strata, because they offer many advantages, such as the ability to bore in a wide variety of strata. An EPBS comprises a circular rotatable cutting head mounted on a cylindrical shield of similar diameter such that its axis of rotation coincides with the longitudinal axis of the shield. Within the shield there are contained means for feeding materials to the cutting head and means for conveying away the soil. The soil thus passes through apertures in the cutting head to an excavation chamber immediately behind the cutting head, from which it is then removed by conveyor, generally a screw-type conveyor.
EPBS perform especially well in cohesive soils with good plastic properties, but they are not so efficient in others, for example in thick and sticky soils. One solution to this problem was the addition at the cutting head of a foamed aqueous material, which makes soil removal much easier. An example of such a process can be found in PCT published application WO 99/18330.
Ideally, the soil at the cutting head should be rendered sufficiently plastic by injection of a foamed material, such that it passes through the cutting head into the excavation chamber. At this point, it should be suitable for disposal by conveyor, but this is not always the case. For example, a problem encountered with soil from strata with a high proportion of clay and water is that the soil remains very fluid, and this not only makes efficient removal from the excavation chamber difficult, but also results in soil flowing out of the excavation chamber behind the shield.
It has now been found that it is possible to remove such soil efficiently by using a modified process involving a foaming agent. The invention therefore provides a process of boring a tunnel using an earth-pressure balance shield boring tunnelling machine having a cutting head, an excavation chamber for soil removed by boring and conveying means for removal of said soil from the excavation chamber; wherein there is injected into a stratum being bored at the cutting head a foamed aqueous solution, characterised in that
(a) the aqueous solution contains two essential components which are (i) a sulphate- or sulphonate-containing anionic surfactant, and (ii) &bgr;-naphthalene sulphonate-formaldehyde condensate; and in that
(b) there is applied to the soil removed by boring in at least one of the excavation chamber and the conveyor a second aqueous solution containing essentially a high molecular weight polyethylene oxide and optionally a sulphate- or sulphonate-containing anionic surfactant.
The aqueous solution described at (a) above shall hereinafter be referred to as “the first aqueous solution”.
The invention is based on the discovery that, in the conditions of tunnelling, the &bgr;-naphthalene sulfonate-formaldehyde condensate (hereinafter referred to by its well-known abbreviation “BNS”) and the polyethylene glycol interact in a way whose precise nature is not known but which results in a stiffening of the medium in which they occur together. As a result, the soil containing both becomes less fluid and more suitable for removal by conveyor.
The anionic surfactant, which is an essential component in the first aqueous solution and an optional component in the second aqueous solution, may be selected from any such sulphate- or sulphonate-containing surfactant known to the art. One particularly preferred type is polyalkylene alkyl ether sulphate, where the polyalkylene oxide chain has an average chain length of 2-3 alkylene oxide units. Typical commercial materials include the “Alscope” (trade mark) series of Toho Chemical Industry Co.
Other particularly preferred types include monoisopropanol ammonium lauryl alcohol sulphate (commercially available as, for example, “Sulfetal” (trade mark) Cjot 160, &agr;-olefin sulphonate (CAS Registry Number 68439-57-6), commercially available as, for example, “Rhodocal” (trade mark) A-246-L, and C
8-22
fatty alcohol sulphate salts and C
8-22
fatty alcohol ether sulphate salts, the fatty alcohol preferably being lauryl alcohol, the ether being an ether formed with a alkylene oxide (preferably ethylene oxide) chain of from 1-3 alkylene oxide units, and the salt-forming cation being preferably selected from alkali metal, magnesium and alkanolamine.
The BNS useful in this invention may be selected from any of the wide range of such materials commercially available. BNS is used in large quantities in the construction industry as a so-called “superplasticiser” for concrete. Examples of commercially—available materials include RHEOBUILD (trade mark) 1100 and RHEOBUILD 5500.
Polyethylene oxides (PEO) are well-known items of commerce and a suitable material may be selected from the wide range available. Typical examples are the “Polyox” (trade mark) materials of Union Carbide. “By high molecular weight” is meant a material with a weight-average molecular weight of from 100,000-8,000,000. The preferred molecular range is from 2,000,000-5,000,000.
In addition to these two essential components, there can be added to the first aqueous solution other materials known to the art to be useful for performing specific specialised functions, for example, biocides and complexing agents. In some circumstances, foam stabilisers, typically amines with long fatty acid chains, may also be useful. These additional materials may be used in art-recognised quantities. When a polyalkylene alkyl ether sulphate surfactant is used, a useful adjunct material is urea, added to the extent of 0.03-0.8%, preferably 0.06-0.25% by weight of the foamed solution.
In the preparation of the first aqueous solution (for foaming and addition at the cutting head) the percentage ratio (solids by weight) of surfactant to BNS may vary from 1:99-99:1, more preferably 90:10-10:90, most preferably 70:30-30:70. (It is of course possible to add the two essential components independently in different aqueous solutions, but this merely increases the handling problems with no increase in performance). For most convenient handling, the two components are dissolved in water to form a concentrate suitable for further dilution, foaming and injection. Typically, the concentrate will comprise from 5-40%, preferably from 8-20%, by weight solids of surfactant plus condensate. For injection at the cutting head, this concentrate is diluted with water such that it constitutes from 1-20%, preferably from 2-6% by weight of the final first aqueous solution, and it is then foamed by conventional means to give a foam having from 2-15 times, preferably 8-12 times, the volume of the first aqueous solution prior to foaming. The volume of foam injected is from 10-1000 L, preferably 200-600 L, per cubic meter of soil.
The invention additionally provides a foamable liquid concentrate as hereinabove defined.
The invention additionally provides a foam as hereinabove defined.
In the preparation of the second aqueous solution, the polyethylene oxide is dissolved in water to the extent of from 0.5-2.0%, preferably 0.8-1.2%, by weight. If sulphate- or sulphonate-containing anionic surfactant is used in the second aqueous solution, it is present to the extent of from 5-40%, preferably from 8-20% by weight of the second solution. The presence of sulphate- or sulphonate-containing anionic surfactant can assist in the removal of soil from the excavation chamber. When surfactant is present in the second aqueous solution, the solution is foamed by conventional means prior to addition to the excavation chamber and/or the conveyor.
In addition to the essential polyethylene oxide and optional anionic surfactant, the second aqueous solution can also contain art-recognised materials in known quantities to perform specific functions. Examples include biocides and defoamers.
In use, the first aqueous solution is foamed by conventional means and then injected from ports in the cutting head into the st
Kreck John
MBT Holding AG
Norris McLaughlin & Marcus PA
LandOfFree
Tunnel boring with foamed composition does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Tunnel boring with foamed composition, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Tunnel boring with foamed composition will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3316705