ABSTRACT:
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a torsion bar to be used as a load limiter in a seat belt retractor.
2. Description of the Related Art
FIG. 2
is an exploded perspective view schematically showing one example of a seat belt retractor. Housed in a base frame
1
is a spool
2
on which a seat belt is wound. A torsion bar
3
has a first hexagonal portion
3
a
which is fitted into and fixed to a hexagonal hole of a locking base
4
. The locking base
4
has a thread portion
4
a
which is threaded into a stopper
5
. The stopper
5
is fitted into a hole
2
a
of the spool
2
.
The torsion bar
3
has a second hexagonal portion
3
b
which is fitted into and fixed to a hexagonal hole formed in a portion of the hole
2
a
of the spool
2
near a speed-reduction/clutch mechanism casing
10
.
A portion of the torsion bar
3
near its one end is fitted into a lock gear
6
. Through the lock gear
6
, the torsion bar
3
is supported by a retainer
7
. The other end of the torsion bar
3
is journaled to the gear in the speed-reduction/clutch mechanism casing
10
through a spline shaft. The lock gear
6
and a flywheel
8
compose a lock activating mechanism called a webbing sensor. When the spool
2
rotates at an acceleration higher than a preset value, i.e., the seat belt is rapidly withdrawn, a projection of a flywheel
8
engages one of the internal teeth formed in the retainer
7
to stop the rotation of the lock gear
6
. Therefore, relative rotation is caused between the lock gear
6
and the locking base
4
. This brings a projection of a pawl
4
b
to protrude circumferentially outside of the locking base
4
so that the projection of the pawl
4
b
engages one of the ratchet teeth
1
b
formed around an opening
1
a
of the base frame
1
to stop the rotation of the locking base
4
. As the rotation of the locking base
4
is stopped, the rotation of the first hexagonal portion
3
a
of the torsion bar
3
is also stopped.
The seat belt retractor is further provided with a vehicle sensor
9
which acts to stop the rotation of the lock gear
6
, i.e., stop the rotation of the locking base
4
when a vehicle tilts at an angle exceeding a preset angle or is subjected to acceleration or deceleration exceeding a preset value.
When a webbing sensor or the vehicle sensor is actuated to stop the rotation of the locking base
4
, the rotation of the first hexagonal portion
3
a
of the torsion bar
3
is stopped. Since the second hexagonal portion
3
b
of the torsion bar
3
is fixed to the spool
2
, the spool
2
still rotates while a body portion
3
c
of the torsion bar
3
is twisted so that relative rotation is caused between the stopper
5
fitted in the spool
2
which is rotating and the locking base
4
which is stopped from rotating so that the stopper
5
is introduced by a threaded portion
4
a
of the locking base
4
to come closer to an end surface of the locking base
4
. During this, the spool
2
is allowed to rotate because the body portion
3
c
of the torsion bar
3
is twisted even though the rotation of the locking base
4
is stopped. After that, the stopper
5
comes in contact with the end surface-of the locking base
4
and is thus stopped from further rotating. This also stops the rotation of the spool
2
.
That is, as the webbing sensor or the vehicle sensor is actuated, the spool
2
is allowed to rotate a predetermined number of turns after the actuation of the sensor and is then stopped from rotating. During this, force acting on the spool
2
in a direction withdrawing the seat belt is absorbed to some extent by plastic deformation of the twisted torsion bar
3
, thereby softening shock applied to a vehicle occupant. Since this structure of a seat belt retractor mentioned above (that is, the structure absent the present invention) is basic and well known in the art, further description about this structure will be omitted.
In the seat belt retractor shown in
FIG. 2
, reduction gears and a clutch are provided m the speed-reduction/clutch mechanism casing
10
to reduce the speed of rotation of a pinion
12
driven by a motor
11
and to transmit the rotation to the torsion bar
3
. Since this portion of
FIG. 2
is not related directly to the present invention, further description about this structure will be omitted.
As described above, the torsion bar functions as a load limiter which produces torsional torque whereby the seat belt is allowed to be pulled out with somewhat resistance in the event of an emergency such as a vehicle collision. For this, it is preferable that the number of turns until broken is so large as to withstand as large a torque as possible.
In a conventional manner to achieve this property of a torsion bar, steel of which the carbon content is 0.06-0.18 wt % is used as the material of the torsion bar and spheroidizing annealing is conducted to the steel. That is, in the manufacturing process of torsion bars, wire rods are processed by acid cleaning, primary drawings, spheroidizing annealing, acid cleaning, surface treatment, and secondary drawing and the processed wire rods are used as the material for torsion bars.
SUMMARY OF THE INVENTION
However, the conventional manufacturing process of torsion bars requires spheroidizing annealing as mentioned above, making the process complex and increasing the cost.
The present invention is made to solve this problem and provide a torsion bar for a seat belt retractor which can be manufactured without spheroidizing annealing.
A first embodiment to solve the aforementioned problem is a torsion bar to be used as a load limiter in a seat belt retractor: characterized in that the torsion bar is made of steel of which the carbon content is 0.04 wt % or less.
Inventors of this invention discovered, through various experimentations about the material of a torsion bar to be used as a load limiter in a seat belt retractor, that steel of which the carbon content is 0.04 wt % enables one to manufacture a torsion bar which can provide enough properties as a load limiter such as the number of torsional turns and the torsional torque even without spheroidizing annealing. This is because as the carbon content is decreased, the percentage of ferrite in the steel is increased and the uniformity of tissue of the steel may be improved. In the conventional one having 0.06 wt % or more of carbon content, enough property in the number of torsional turns can not be obtained when a spheroidizing annealing process is omitted.
In the first embodiment of the invention, the constituents of the steel besides carbon are not limited and may be the same constituents of steel used as the material for a conventional torsion bar.
A second embodiment to solve the aforementioned problem is a torsion bar to be used as a load limiter in a seat belt retractor characterized in that the torsion bar is made of steel containing 0.04 wt % or less of carbon and at least one of 0.01-0.05 wt % of Ti and 0.01-0.05 wt % of Nb.
This second embodiment of the invention further contains at least one of 0.01-0.05 wt % of Ti and 0.01-0.05 wt % of Nb in addition to the constituents of the steel of the first embodiment. Ti and/or Nb is added to fix N and C and form deposit including P, S, thereby improving workability. Less than 0.01 wt % of Ti or Nb less provides too poor efficiency, while more than 0.05 wt % of Ti or Nb rather harms than improves the workability. Therefore, the content is limited to the aforementioned range.
As described in the above, according to the present invention, a torsion bar can be manufactured without spheroidizing annealing process, and a seat belt retractor can be provided which can provide uniform properties such as the number of torsional turns and the torsional load.
REFERENCES:
patent: 4533391 (1985-08-01), Borneman et al.
patent: 6186432 (2001-02-01), Koning
Kanamori Yasushi
Mishina Joji
Nishizawa Muneo
Takata Corporation
Yee Deborah
LandOfFree
Torsion bar for seat belt retractor does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Torsion bar for seat belt retractor, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Torsion bar for seat belt retractor will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2864191