Titanium material superior in upset-forgeability and method...

Details Titanium material superior in upset-forgeability and method... Titanium material superior in upset-forgeability and method...

2006-03-21

2006-03-21

Yee, Deborah (Department: 1742)

Metal treatment

Stock

Titanium, zirconium, or hafnium base

C148S670000, C420S417000

Reexamination Certificate

active

07014722

ABSTRACT:
In finifsh-cogging a high-purity titanium material into a cylindrical form as the final shape, if cylindrical cogging is performed in all stages of warm forging or if cylindrical cogging is performed in the initial stage of the warm forging, there is no need of peripherally restricting the cylindrical cogging material, so that even if longitudinal upset-forging is effected with an upsetting ratio of 2, the condition that the major diameter/minor diameter ratio of the section after forging is not more than 1.01 can be satisfied, developing superior upset-forgeability. This makes it possible, in producing disk-like targets for sputtering, to minimize cutting loss produced during the rolling and machining and to maximize the yield of products; therefore, the material can be widely used as a semiconductor material for electrodes and the like using a high-purity titanium material.

REFERENCES:
patent: 5026520 (1991-06-01), Bhowal et al.
patent: 40 23 962 (1991-04-01), None
patent: 55-154640 (1980-11-01), None
patent: 57-202935 (1982-12-01), None
patent: 60-3936 (1985-01-01), None
patent: 62-072448 (1987-04-01), None
patent: 62-284053 (1987-12-01), None
patent: 62-286640 (1987-12-01), None
patent: 03-140447 (1991-06-01), None
patent: 5-237581 (1993-09-01), None
patent: 05237581 (1993-09-01), None
patent: 08-081747 (1996-03-01), None
patent: 8-232061 (1996-09-01), None
patent: 08232061 (1996-09-01), None
patent: 62-286639 (1997-12-01), None
patent: 11-269621 (1999-10-01), None

Affiliated with

Also associated with

Rating

Titanium material superior in upset-forgeability and method... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Titanium material superior in upset-forgeability and method..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Titanium material superior in upset-forgeability and method... will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-3606031