Tin mill black plate for canmaking, and method of manufacturing

Details Tin mill black plate for canmaking, and method of manufacturing Tin mill black plate for canmaking, and method of manufacturing

1993-04-06

1994-11-01

Yee, Deborah

Stock material or miscellaneous articles

All metal or with adjacent metals

Composite; i.e., plural, adjacent, spatially distinct metal...

428679, 148651, 148603, 148529, 427328, C21D 800, C23C 1800

Patent

active

053606760

ABSTRACT:
A raw plated steel sheet for can comprises recrystallized particles containing approximately C<0,004%, Si<0.03%, Mn:0.05-0.6%, P<0.02%, S<0.02%, N<0.01%, Al:0.005-0.1%, Nb:0,001-0.1%, B:0.0001-0.005% in weight. The maximum diameter of a particle is less than about 30 .mu.m, and an area ratio of particles ranging about 5-25 .mu.m being more than about 50%. Such a steel sheet has excellent processing characteristics and good uniformity in product quality.

REFERENCES:
patent: 4889566 (1989-12-01), Okada et al.
patent: 5156694 (1992-10-01), Yamazaki et al.

Affiliated with

Also associated with

Rating

Tin mill black plate for canmaking, and method of manufacturing does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Tin mill black plate for canmaking, and method of manufacturing, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Tin mill black plate for canmaking, and method of manufacturing will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-1801705