Thermoplastic silicone elastomers from compatibilized...

Synthetic resins or natural rubbers -- part of the class 520 ser – Synthetic resins – Mixing of two or more solid polymers; mixing of solid...

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C525S903000, C524S730000, C524S731000, C524S862000

Reexamination Certificate

active

06649704

ABSTRACT:

FIELD OF THE INVENTION
The present invention relates to a thermoplastic elastomer composition wherein a silicone base is blended with a polyamide resin and a compatibilizer and silicone gum contained in the base is dynamically vulcanized during the mixing process.
BACKGROUND OF THE INVENTION
Thermoplastic elastomers (TPEs) are polymeric materials which possess both plastic and rubbery properties. They have elastomeric mechanical properties but, unlike conventional thermoset rubbers, they can be re-processed at elevated temperatures. This re-processability is a major advantage of TPEs over chemically crosslinked rubbers since it allows recycling of fabricated parts and results in a considerable reduction of scrap.
In general, two main types of thermoplastic elastomers are known. Block copolymer thermoplastic elastomers contain “hard” plastic segments which have a melting point or glass transition temperature above ambient as well as “soft” polymeric segments which have a glass transition or melt point considerably below room temperature. In these systems, the hard segments aggregate to form distinct microphases and act as physical crosslinks for the soft phase, thereby imparting a rubbery character at room temperature. At elevated temperatures, the hard segments melt or soften and allow the copolymer to flow and to be processed like an ordinary thermoplastic resin.
Alternatively, a thermoplastic elastomer referred to as a simple blend (physical blend) can be obtained by uniformly mixing an elastomeric component with a thermoplastic resin. When the elastomeric component is also cross-linked during mixing, a thermoplastic elastomer known in the art as a thermoplastic vulcanizate (TPV) results. Since the crosslinked elastomeric phase of a TPV is insoluble and non-flowable at elevated temperature, TPVs generally exhibit improved oil and solvent resistance as well as reduced compression set relative to the simple blends.
Typically, a TPV is formed by a process known as dynamic vulcanization, wherein the elastomer and the thermoplastic matrix are mixed and the elastomer is cured with the aid of a crosslinking agent and/or catalyst during the mixing process. A number of such TPVs are known in the art, including some wherein the crosslinked elastomeric component can be a silicone polymer while the thermoplastic component is an organic, non-silicone polymer (i.e., a thermoplastic silicone vulcanizate or TPSiV). In such a material, the elastomeric component can be cured by various mechanisms, but it has been shown that the use of a non-specific radical initiator, such as an organic peroxide, can also result in at least a partial cure of the thermoplastic resin itself, thereby reducing or completely destroying the ability to re-process the composition (i.e., it no longer is a thermoplastic). In other cases, the peroxide can lead to the partial degradation of the thermoplastic resin. To address these problems, elastomer-specific crosslinkers, such as organohydrido silicon compounds, can be used to cure alkenyl-functional silicone elastomers.
Arkles, in U.S. Pat. No. 4,500,688, discloses semi-interpenetrating networks (IPN) wherein a vinyl-containing silicone fluid having a viscosity of 500 to 100,000 cS is dispersed in a conventional thermoplastic resin. Arkles only illustrates these IPNs at relatively low levels of silicone. The vinyl-containing silicone is vulcanized in the thermoplastic during melt mixing according to a chain extension or crosslinking mechanism which employs a silicon hydride-containing silicone component. This disclosure states that the chain extension procedure results in a thermoplastic composition when the vinyl-containing silicone has 2 to 4 vinyl groups and the hydride-containing silicone has 1 to 2 times the equivalent of the vinyl functionality. On the other hand, silicones which predominantly undergo crosslinking reaction result in thermoset compositions when the vinyl-containing silicone has 2 to 30 vinyl groups and the hydride-containing silicone has 2 to 10 times the equivalent of the vinyl functionality. Typical thermoplastics mentioned include polyamides, polyurethanes, styrenics, polyacetals and polycarbonates. This disclosure is expanded by Arkles in U.S. Pat. No. 4,714,739 to include the use of hybrid silicones which contain unsaturated groups and are prepared by reacting a hydride-containing silicone with an organic polymer having unsaturated functionality. Although Arkles discloses a silicone fluid content ranging from 1 to 40 weight percent (1 to 60% in the case of the '739 patent), there is no suggestion of any criticality as to these proportions or to the specific nature of the organic resin.
Publication WO 96/01291 to Advanced Elastomer Systems discloses thermoplastic elastomers having improved resistance to oil and compression set. These systems are prepared by first forming a cured rubber concentrate wherein a curable elastomeric copolymer is dispersed in a polymeric carrier not miscible therewith, the curable copolymer being dynamically vulcanized while this combination is mixed. The resulting rubber concentrate is, in turn, blended with an engineering thermoplastic to provide the desired TPE. Silicone rubber is disclosed as a possible elastomeric component, but no examples utilizing such a silicone are provided. Further, this publication specifically teaches that the polymeric carrier must not react with the cure agent for the curable copolymer.
Crosby et al. in U.S. Pat. No. 4,695,602 teach composites wherein a silicone semi-IPN vulcanized via a hydrosilation reaction is dispersed in a fiber-reinforced thermoplastic resin having a high flexural modulus. The silicones employed are of the type taught by Arkles, cited supra, and the composites are said to exhibit improved shrinkage and warpage characteristics relative to systems which omit the IPN.
Ward et al., in U.S. Pat. No. 4,831,071, disclose a method for improving the melt integrity and strength of a high modulus thermoplastic resin to provide smooth-surfaced, high tolerance profiles when the modified resin is melt-drawn. As in the case of the disclosures to Arkles et al., cited supra, a silicone mixture is cured via a hydrosilation reaction after being dispersed in the resin to form a semi-IPN, and the resulting composition is subsequently extruded and melt-drawn.
European Patent Application 0651009A1 to Sumitomo Bakelite Co., published May 3, 1995, discloses a thermoplastic elastomer composition which is prepared by dynamically heating a mixture comprising an unsaturated organic (i.e., non-silicone) rubber, a thermoplastic resin, an SiH-containing crosslinker, a hydrosilating catalyst and a compatibilizing agent.
U.S. Pat. No. 6,013,715 to Gornowicz et al. teaches the preparation of TPSiV elastomers wherein a silicone gum (or filled silicone gum) is dispersed in either a polyolefin or a poly(butylene terephthalate) resins and the gum is subsequently dynamically vulcanized therein via a hydrosilation cure system. The resulting elastomers exhibit an ultimate elongation at break of at least 25% and have significantly improved mechanical properties over the corresponding simple blends of resin and silicone gum in which the gum is not cured (i.e., physical blends). This is, of course, of great commercial significance since the vulcanization procedure, and the cure agents required therefor, add to both the complexity as well as the expense of the preparation and vulcanization would be avoided in many applications if essentially identical mechanical properties could be obtained without its employ.
Copending application Ser. No. 09/393029, filed on Sep. 9, 1999, discloses that the impact resistance of polyester and polyamide resins can be greatly augmented by preparing a thermoplastic silicone vulcanizate therefrom wherein the elastomeric component is a silicone rubber base which comprises a silicone gum and a silica filler and the weight ratio of the base to the resin ranges from 10:90 to 35:65. Although the resulting thermoplastic materials have improved impact resistance, they do not ex

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Thermoplastic silicone elastomers from compatibilized... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Thermoplastic silicone elastomers from compatibilized..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Thermoplastic silicone elastomers from compatibilized... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3182175

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.