ABSTRACT:
The present invention relates to a thermally stable fire retardant laminate for printed circuit boards using a thermally stable aluminium hydroxide without the need for other fire retardant agents.
Printed circuit board laminate types are defined by the American NEMA (National Electrical Manufacturers Association) standard, the terminology is accepted world-wide. Generally, laminates are categorized according to the type of reinforcement used, i.e., cellulose paper or glass. Typically, the type FR-2 uses paper only, CEM-1 uses paper and woven glass, while type CEM-3 contains both woven and non-woven glass. The type FR-4 contains woven glass only.
To achieve the required V0 level of fire retardancy according to American Underwriters Laboratories' standard UL-94, it is necessary to add either fire retardant chemicals to the polymer system or build halogens or phosphorous into the backbone of the polymer itself On combustion, these additives help to extinguish the fire. However, in the process of doing so they produce toxic and corrosive gases. In the case of combustion of FR-2 laminates, which contain phosphorous compounds, phosphoric acid is formed. CEM-1, CEM-3 and FR-4 laminates which contain brominated epoxy resin, produce corrosive and toxic hydrogen bromide on combustion.
It is well known in the art that aluminium hydroxide may be used to improve the fire retardancy of synthetic polymer systems based on for example epoxy, polyester, and vinyl ester because the polymers decompose in the same temperature range as the aluminium hydroxide However, the thermal stability of the gibbsite form of aluminium hydroxide (Al(OH)
3
or sometimes represented as Al
2
O
3
.3H
2
O) is insufficient at the temperatures used to solder components to a printed circuit board laminate. This can result in blistering of the laminate thereby rendering it unusable.
It is known that when gibbsite type aluminium hydroxide is heat treated in air it is partially converted to the mono hydrate form, boehmite (AlOOH or Al
2
O
3
.H
2
O) which improves thermal stability but to the detriment of fire retardancy.
Japanese patent disclosure JP-A 60/203 438 describes a CEM-3 laminate containing heat treated gibbsite type aluminium hydroxide which has improved thermal stability over standard aluminium trihydroxide but which does not give the required level of fire retardancy so that brominated epoxy resin has to be used to achieve the UL 94 V0 rating. In such circumstances, and in the absence of superior fire properties, other inorganic materials such as talc or clay could also be used.
The object of the present invention is to produce a CEM-3 laminate which has good thermal stability, is halogen/phosphorous free and meets the UL 94 V0 requirement. A further object of the invention is to develop a thermally stable aluminium hydroxide which impart the required characteristics to the laminate.
It was possible to achieve the object of the invention by means of a laminate for printed circuit boards according to the invention, by a method for the preparation of the laminate according to the invention, by a printed circuit board made of the laminate according to the invention, and by a thermally stable aluminum hydroxide according to the invention.
The CEM-3 type laminates are as a rule constructed from two layers of woven fiberglass on the outsides and three layers of non-woven glass tissue in the core. According to the invention, the laminate for printed circuit boards has surface layers comprising curable resin-impregnated woven glass fabric and intermediate layers comprising curable resin-impregnated non-woven glass, and is characterized in that the intermediate layers contain 200% by weight to 275% by weight (based on the resin) of a thermally stable aluminum hydroxide of the molecular formula Al
2
O
3
·nH
2
O wherein 2.6<n<2.9.
The curable resin may be an unsaturated polyester resin, an epoxy, a vinyl ester or any suitable thermosetting compound which on combustion decomposes in the same temperature range as the thermally stable aluminium hydroxide.
The laminates may be based on epoxy resin which allows a batch process to be used. The laminates may also be produced by continuous process using unsaturated polyester or vinyl ester, i.e., resins which polymerize via a free radical mechanism. The nature of the invention however does not limit the manufacturing technique for the laminate.
When the production of the laminate is based on epoxy resin, as a rule two layers of woven glass preimpregnated with the epoxy resin are combined with three layers of non-woven glass preimpregnated with epoxy resin containing thermally stable aluminium hydroxide These five layers are usually then combined with one or two layers of copper foil on the outside and the assembly subjected to heat and pressure to polymerize the resin and consolidate the laminate.
Most epoxy resins used for electrical and electronic applications are derived from bisphenol A or cycloaliphatic species. The most common curing agent is dicyandiamide.
According to the method of the present invention, the intermediate layer comprising curable resin impregnated non-woven glass contain 200% by weight to 275% by weight, preferably 225% by weight to 250% by weight, of the thermally stable aluminium hydroxide relative to the weight pf the curable resin.
In the molecular formula, Al
2
O
3
.nH
2
O, n preferably has a value of 2.7 to 2.8.
A feature of the halogen and phosphorous free epoxy laminate of the present invention is the use of thermally stable aluminium hydroxide as the sole fire retardant.
The prior art describes the removal of a part of the water content of aluminium hydroxide as a means of improving it's thermal stability. If insufficient water is removed, the laminate containing the aluminium hydroxide does not survive the soldering operation. However, a limitation of the prior art is that if too much water is removed the resulting aluminium hydroxide may contain too little water of constitution to act effectively as a fire retardant.
A further complication is the formation of the more thermally stable phase aluminium hydroxide (boehmite), which not only contains one third of the amount of water as the original aluminium trihydroxide (gibbsite) it also holds it back to 520° C. before releasing it. This detracts further from fire retardant effectiveness.
It is well known in the art that the finer is the aluminium hydroxide starting material, the less is the tendency to form the undesirable boehmite phase on heating. However, at the particle sizes necessary to avoid boehmite formation (<1 &mgr;m), it becomes virtually impossible to process the material in synthetic resin. On the other hand, thermally stable aluminium hydroxide which is processable will contain too much boehmite thus preventing the production of a halogen-free epoxy laminate which passes UL 94 V0.
Essentially, the novel feature of the thermally stable aluminium hydroxide of the present invention is the surprisingly low boehmite content relative to the average particle size. This allows lower values of n to be obtained thereby improving water stability without compromising on fire properties' effectiveness. Thus, for n<2.6, there is insufficient water (and too much boehmite) to achieve the required fire properties whereas for n>2.9, there is too much water still present to achieve the required thermal resistance to soldering.
The decoupling of the relationship between boehmite formation and particle size is achieved by suitable mechanical treatment of relatively coarse particles (average size ca. 60 &mgr;m) of aluminium hydroxide prior to the thermal pretreatment step. A suitable mechanical treatment would be provided for example by the application of compressive forces to aluminium hydroxide to increase polycrystallinity. Without being bound to any particular theory, it appears that structural degradation by such means creates the conditions for a more easy diffusion of water to the exterior of the crystals thereby minimizing the tendency to build-up of hydrothermal
Aggleton Michael
Brown Neil
Bos Steven
Fisher Christen & Sabol
LandOfFree
Thermally stable aluminum hydroxide does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Thermally stable aluminum hydroxide, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Thermally stable aluminum hydroxide will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3151724