ABSTRACT:
FIELD OF THE INVENTION
This invention relates to ceramic materials for thermal barrier coatings, to thermal barrier coatings made of such materials, and to metallic parts having such thermal barrier coatings. The thermal barrier coatings have particular utility in gas turbine engines. The preferred ceramic material is preferably composed of gadolinia and zirconia and has a cubic crystal structure.
BACKGROUND OF THE INVENTION
Gas turbine engines are well developed mechanisms for converting chemical potential energy, in the form of fuel, to thermal energy and then to mechanical energy for use in propelling aircraft, generating electric power, pumping fluids etc. At this time, the major available avenue for improved efficiency of gas turbine engines appears to be the use of higher operating temperatures. However, the metallic materials used in gas turbine engines are currently very near the upper limits of their thermal stability. In the hottest portion of modern gas turbine engines, metallic materials are used at gas temperatures above their melting points. They survive because they are air cooled. But providing air cooling reduces engine efficiency.
Accordingly, there has been extensive development of thermal barrier coatings for use with cooled gas turbine aircraft hardware. By using a thermal barrier coating, the amount of cooling air required can be substantially reduced, thus providing a corresponding increase in efficiency.
Such coatings are invariably based on ceramic. Mullite, alumina, etc. have been proposed, but zirconia is the current material of choice. Zirconia must be modified with a stabilizer to prevent the formation of the monoclinic phase, and typical stabilizers include yttria, calcia, ceria and magnesia. prevent the formation of the monoclinic phase, and typical stabilizers include yttria, calcia, ceria and magnesia.
Generally speaking, metallic materials have coefficients of thermal expansion which exceed those of ceramic materials. Consequently, one of the problems that must be addressed in the development of successful thermal barrier coatings is to match the coefficient of thermal expansion of the ceramic material to the metallic substrate so that upon heating, when the substrate expands, the ceramic coating material does not crack. Zirconia has a high coefficient of thermal expansion and this is a primary reason for the success of zirconia as a thermal barrier material on metallic substrates.
Thermal barrier coatings have been deposited by several techniques including thermal spraying (plasma, flame and HVOF), sputtering and electron beam physical vapor deposition (EBPVD). Of these techniques, electron beam physical vapor deposition is currently a preferred technique for demanding applications because it produces a unique coating structure. Electron beam physical vapor deposited ceramic materials, when applied according to certain parameters, have a columnar grain microstructure consisting of small columns separated by gaps which extend into the coating. These gaps allow substantial substrate expansion without coating cracking and/or spalling. See, e.g., commonly owned U.S. Pat. No. 4,321,311. According to U.S. Pat. No. 5,073,433 and commonly-owned U.S. Pat. No. 5,705,231, a similar structure (comprising segmentation cracks) although on a larger scale, can be obtained by plasma spray techniques.
Despite the success with the current use of electron beam physical vapor deposited zirconia base coatings, there is a continuing desire for improved coatings which exhibit superior thermal insulation capabilities, especially those improved in insulation capabilities when normalized for coating density. Weight is always a critical factor when designing gas turbine engines, particularly rotating parts. Ceramic thermal barrier coatings are not load supporting materials, and consequently they add weight without increasing strength. There is a strong desire for a ceramic thermal barrier material which adds the minimum weight while providing the maximum thermal insulation capability. In addition, there are obviously the normal desires for long life, stability, economy etc.
Although this coating was developed for application in gas turbine engines, the invention clearly has utility in other applications where high temperatures are encountered, such as furnaces and internal combustion engines.
REFERENCES:
patent: 3718499 (1973-02-01), Kanter
patent: 4321310 (1982-03-01), Ulion et al.
patent: 4321311 (1982-03-01), Strangman
patent: 4639399 (1987-01-01), Aprigliano
patent: 4996117 (1991-02-01), Chu et al.
patent: 5304519 (1994-04-01), Jackson et al.
patent: 5495979 (1996-03-01), Sastri et al.
patent: 5512382 (1996-04-01), Strangman
patent: 5562998 (1996-10-01), Strangman
patent: 5652044 (1997-07-01), Rickerby
patent: 5716720 (1998-02-01), Murphy
patent: 5722379 (1998-03-01), Binder et al.
patent: 5763107 (1998-06-01), Rickerby et al.
patent: 0 825 271 A1 (1998-02-01), None
M.A. Subramanian, G. Aravamudan and G. V. Subba Rao, “Oxide Pyrochlores—A Review”.
Harry L. Tuller and Peter K. Moon, “Fast Ion Conductors: Future Trends”.
M. J. Maloney, “High Efficiency Thermal Barrier Coatings for Advanced Alloy Airfoils”, Mar. 15, 1996.
Robert S. Roth, “Pyrochlore-Type Compounds Containing Double Oxides of Trivalent and Tetravalent Ions”, vol. 56, No. 1, Jan. 1956, Journal of Research of the National Bureau of Standards, pp. 17-25.
M. Kakihana, M.M. Milanova, M. Arima, T.Okubo, M. Yashima and M. Yoshimura, “Polymerized Complex Route to Synthesis of Pure Y2Ti2O7at 750° C Using Yttrium-Titanium Mixed-Metal Citric Acid Complex”, pp. 1673-1676.
Periodic Table of The Elements.
Patent Disclosure by M.J. Maloney, “Rare Earth Pyrochlore Zirconate Base Thermal Barrier Coatings” Fig. 5232.
Two Oxides, Figs 2373-2376 p. 103.
P. 341 Fd3mO7h.
Two Oxides, Figs. 6469-6470 p. 165.
Ronald A. McCauley, “Structural Characteristics of Pyrochlore Formation”, pp. 290-294.
Two Oxides, Figs. 4376-4377 pp. 135-136.
Ernest M. Levin and Howard F. McMurdie, “Phase Diagrams for Ceramists 1975 Supplement”, 3 pgs.
Morrison III F. Tyler
Turner Archene
United Technologies Corporation
LandOfFree
Thermal barrier coating systems and materials does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Thermal barrier coating systems and materials, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Thermal barrier coating systems and materials will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2464078