Coating processes – Spray coating utilizing flame or plasma heat – Metal oxide containing coating
Reexamination Certificate
1999-10-14
2001-08-07
Bareford, Katherine A. (Department: 1762)
Coating processes
Spray coating utilizing flame or plasma heat
Metal oxide containing coating
C427S456000, C427S142000, C427S258000, C427S287000, C427S405000
Reexamination Certificate
active
06270852
ABSTRACT:
FIELD OF THE INVENTION
The present invention relates generally to thermal barrier coatings, and relates more particularly to ceramic thermal barrier coating systems for superalloys.
BACKGROUND OF THE INVENTION
Thermal barrier coatings (TBCS) are widely used to reduce the operating temperatures of underlying substrates. For example, TBCs have been used for years in gas turbine engines, and more particularly in the turbine sections of such engines.
A typical TBC system utilizes a superalloy substrate, with a thin adherent alumina layer formed over the substrate, and a ceramic layer applied on the alumina layer. See, e.g., U.S. Pat. No. 4,321,311 to Strangman. Depending upon the particular superalloy, a separate bond coat, including but not limited to an MCrAlY or aluminide bond coat is provided on the substrate, and the adherent alumina layer is subsequently formed on the bond coat. M is selected from the group including nickel, cobalt, iron and combinations thereof. Alternatively, some superalloys can be oxidized to form an adherent alumina layer, and no separate bond coat is required. Exemplary alloys are described in commonly-owned U.S. Pat. Nos. 4,209,348 and 4,719,080 both to Duhl et al. A primary benefit of such superalloys is that there is no need to cover the substrate with a separate bond coat. The addition of a bond coat adds weight to a component without adding strength, which while undesirable generally, e.g., in gas turbine engines, is particularly undesirable on moving or rotating parts such as blades. On parts rotating at several thousands of revolutions per minute, the additional weight of the bond coat adds significantly to blade pull, e.g., corresponds to the centrifugal force due to the bond coat and increases with the square of the rotational speed. At elevated temperatures, the blade pull attributable to the bond coat also contributes to creep at the blade root, which affects the clearance between the blade tip and any surrounding structure and also affects engine efficiency and longevity. Moreover, a thick bond coat is subject to significant thermal fatigue due to the thermal stresses generated in the coat over the wide range of temperatures to which the component is exposed. Accordingly, use of superalloys capable of forming an adherent alumina layer are increasingly desired for use in rotating components such as turbine blades and compressor blade, as well as other moving components.
It is known that many ceramic materials, including stabilized or strengthened zirconia generally and by way of example zirconia having 7 percent by weight yttria (7YSZ) described in commonly-owned U.S. Pat. No. 4,321,311 to Strangman, are relatively transparent to oxygen. Accordingly, underlying metal will oxidize (at generally manageable and predicable rates), and will oxidize at an increasing rate as the temperature increases. It is also known that the ceramic layer will eventually spall or otherwise fail, which in turn influences the service life of the component. Under normal operating conditions, service life subsequent to ceramic spallation is affected by the remaining bond coat or alloy oxidation life. As a general rule, the superalloys capable of forming an alumina layer without the use of a separate bond coat tend to be less oxidation resistant than conventional superalloys which utilize a separate bond coat, and we believe that higher oxidation resistance of conventional superalloys is due at least in part to a higher aluminum content, e.g., in the bond coat used with the conventional superalloys, as well as the presence of an intervening layer (the bond coat) between the substrate and its environment.
It is further known that portions of the ceramic material occasionally fail prematurely, for example due to localized spallation or foreign object damage, e.g., particulates formed during combustion, debris entrained in air ingested by the engine, or debris generated by broken upstage components. Underlying, exposed component areas are then subjected to significantly increased temperatures, and oxidize at correspondingly higher rates thereby reducing the life of the component. With respect to components that do not include a separate bond coat, the substrate material is exposed directly to the higher temperatures and increased oxygen, and oxidizes at even higher rates. The higher oxidation rate occurring on unprotected portions of substrate material in turn accelerates failure of the surrounding ceramic and exposure of additional substrate material, and the increased temperatures can melt or otherwise damage the substrate material.
It is an object of the present invention to provide a TBC system, preferably but not necessarily incorporating a superalloy that forms an adherent alumina layer, providing the benefit of reduced weight while still limiting oxidation in the event that the ceramic fails.
It is another object of the invention to provide such a system in which the service life of an associated component is not significantly shortened in the event of ceramic failure.
SUMMARY OF THE INVENTION
According to one aspect of the invention, a thermal barrier coating system for a superalloy substrate is disclosed.
The substrate comprises a superalloy of the type that is capable of forming an adherent alumina layer. See, e.g., U.S. Pat. Nos. 4,209,348 and 4,719,080 both to Duhl et al. By way of example the substrate may define a turbine blade of a gas turbine engine. A bond coat is applied to at least one local area of the substrate, so that a remaining portion of the substrate remains uncovered. The local area is selected to be the area(s) at which a TBC typically fails first, e.g., the leading and trailing edges of the blade airfoil, or other area. Preferably, an alumina layer is formed on the remaining portion of the substrate and also on the bond coat. Even if an overlying ceramic layer fails, the underlying bond coat remains, and limits the rate at which the underlying substrate material oxidizes.
According to another aspect of the present invention, a superalloy article is disclosed.
The article includes a superalloy substrate, such as a turbine blade of a gas turbine engine. The superalloy is of the type that is capable of forming an adherent alumina layer. A bond coat of the article is applied to at least one local area of the substrate, so that a portion of the substrate remains exposed. In the case of a turbine blade, the bond coat is preferably applied to the leading and trailing edges of the blade.
According to yet another aspect of the present invention, a method is disclosed for reducing the weight of a ceramic coated article of the type including a superalloy substrate, an adherent bond coat on the substrate, an alumina layer formed on the bond coat and a ceramic later on the alumina layer.
The method includes the steps of providing a superalloy substrate comprising a material capable of forming an adherent alumina layer; applying a bond coat to at least one local area of the substrate such that a remaining portion of the substrate remains uncovered; forming a thin adherent alumina layer on the remaining portion of the substrate and on the bond coat; and applying a ceramic layer on the alumina layer.
According to still another aspect of the present invention, a thermal barrier coating system for a superalloy article is provided. The coating system includes a superalloy substrate, and an aluminide coating and an MCrAlY bond coat applied to a localized area. The bond coat may be applied to a local area of the substrate with the aluminide being applied over the substrate and the bond coat, or the aluminide may be applied to the substrate with the bond coat being applied over a local area of the aluminide. A thin adherent alumina layer is formed over the aluminide and the bond coat, with a ceramic layer is on the alumina layer.
REFERENCES:
patent: Re. 32121 (1986-04-01), Gupta et al.
patent: 4005989 (1977-02-01), Preston
patent: 4209348 (1980-06-01), Duhl et al.
patent: 4321311 (1982-03-01), Strangman
patent: 4585481 (1986-04-01), Gupta et al.
patent: 471908
Bose Sudhangshu
Gupta Dinesh K.
Marcin Jeanine T.
Ulion Nicholas E.
Bareford Katherine A.
Morrison F. Tyler
United Technologies Corporation
LandOfFree
Thermal barrier coating system utilizing localized bond coat... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Thermal barrier coating system utilizing localized bond coat..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Thermal barrier coating system utilizing localized bond coat... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2540586