Thermal barrier coating method

Coating processes – Coating by vapor – gas – or smoke – Metal coating

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C427S255340, C427S255700

Reexamination Certificate

active

06472018

ABSTRACT:

FIELD OF THE INVENTION
The present invention relates to thermal barrier coatings for components, such as gas turbine engine blades and vanes, wherein the thermal barrier coating exhibits improved coating life.
BACKGROUND OF THE INVENTION
Advancements in propulsion technologies have required gas turbine engines to operate at higher temperatures. This increase in operating temperature has required concomitant advancements in the operating temperatures of metal (e.g. superalloy) turbine engine components. Thermal barrier coatings have been used to meet these higher temperature requirements. Typical thermal barrier coatings comprise alumina and/or zirconia based ceramic which provide a thermal insulative layer to protect the metal component from the high temperatures.
Thermal barrier coatings have been applied to metal components by first coating the component with a bondcoat, which may comprise an inwardly or outwardly grown platinum modified diffusion aluminide bondcoat and/or MCrAlY overlay bondcoat where M is Ni and/or Co. After applying the bondcoat, the coated component typically is grit blasted and vacuum heat treated, or vice versa, to promote the formation of a thermally grown oxide (TGO) layer typically comprising alumina on the aluminum-rich underlying bondcoat. The component then is coated by electron beam physical vapor deposition with a thermal insulative layer of alumina, zirconia, or other ceramic material. For example, U.S. Pat. Nos. 5,716,720 and 5,856,027 describe a thermal barrier coating system comprising a clean platinum modified diffusion aluminide bondcoat on the substrate, a thermal grown alumina layer, and a thermal insulative ceramic layer on the alumina layer. The platinum modified diffusion aluminide bondcoat comprises an outwardly grown diffusion aluminide coating produced by CVD (chemical vapor deposition) processing using high substrate temperature and low activity coating gases that produce higher concentrations of Pt and Al and low concentrations of harmful refractory metal impurities (e.g. Mo, W, Cr, Ta, etc.) and surface active impurities (e.g. S,. P, Cl, B, etc.) at the outermost zone or region of the aluminide coating.
The life of a thermal barrier coating; i.e. time to coating spallation, is known to be related to the surface characteristics of the bondcoat and the particular phase of the thermally grown alumina present between the insulative layer and the bondcoat. Negative effects of bondcoat surface roughness on coating life have been reported by Jordan in “Bondcoat Strength and Stress Measurements in Thermal Barrier Coatings”, US Department of Energy Report (subcontract #95-01-SR030), Sep. 30, 1997, where it was reported that platinum aluminide bondcoat surfaces include grain boundary ridges that act as sites for stress concentration and damage accumulation during thermal cycling of thermal barrier coated substrates. Grain boundary ridges act as sites for preferential oxidation, void formation, and crack initiation which result in the thermally grown alumina spalling prematurely.
The formation of the thermally grown alumina layer on the aluminum-rich bondcoat involves several metastable transition phases, such as a cubic gamma alumina phase transforming to a tetragonal delta alumina phase then to a monoclinic theta alumina phase finally to a rhombohedral alpha alumina phase, the formation of which occurs by heterogeneous nucleation and growth of the alpha phase from the monoclinic theta phase. The sum of the metastable transitions involves a substantial molar volume reduction of approximately 9%, a significant portion of which is attributable to the final transition from the theta phase to alpha phase.
An object of the present invention is to provide a method of pretreating a superalloy or other substrate prior to coating with a thermal insulative layer of a thermal barrier coating system in a manner to reduce adverse effects of bondcoat surface roughness on life of the thermal barrier coating.
Another object of the present invention is to provide a method of pretreating a superalloy or other substrate prior to coating with a thermal insulative layer of a thermal barrier coating system in a manner to reduce adverse effects of metastable phases of thermally grown alumina on life of the thermal barrier coating.
A still further object of the present invention is to significantly increase the life of the thermal barrier coating system under high temperature cyclic oxidation conditions.
SUMMARY OF THE INVENTION
The present invention involves forming on a superalloy or other metallic substrate an outwardly grown diffusion aluminide bondcoat that has higher concentrations of Al and optionally Pt and lower concentration of a harmful refractory metal impurity (e.g. Mo, W, Cr, Ta, etc.) at an outermost zone or region of the bondcoat than at an innermost zone or region thereof and pretreating the bondcoat by repetitively moving the bondcoated substrate in contact with abrasive media in a container to reduce bondcoat grain boundary ridges, while leaving at least a portion, preferably all, of the outermost Al-rich zone or region of the original Al-rich bondcoat. The repetitive moving can be achieved by media bowl polishing.
The present invention also involves heat treating the pretreated bondcoated substrate under temperature and time conditions in air to form a stable alpha alumina layer on the bondcoat prior to deposition of the ceramic thermal insulative layer.
A thermal barrier coating system formed pursuant the present invention exhibits a significant increase in coating life (time to coating spallation) in cyclic oxidation tests at elevated temperatures.
The above objects and advantages of the present invention will become more readily apparent from the following description taken with the following drawings.


REFERENCES:
patent: 3873347 (1975-03-01), Walker et al.
patent: 4931102 (1990-06-01), Burke
patent: 5236745 (1993-08-01), Gupta et al.
patent: 5384200 (1995-01-01), Giles et al.
patent: 5626674 (1997-05-01), VanKuiken, Jr. et al.
patent: 5658614 (1997-08-01), Basta et al.
patent: 5671532 (1997-09-01), Rao et al.
patent: 5683825 (1997-11-01), Bruce et al.
patent: 5716720 (1998-02-01), Murphy
patent: 5759640 (1998-06-01), Mannava et al.
patent: 5792521 (1998-08-01), Wortman
patent: 5817372 (1998-10-01), Zheng
patent: 5856027 (1999-01-01), Murphy
patent: 5876860 (1999-03-01), Marijnissen et al.
patent: 6132520 (2000-10-01), Schilbe
patent: 6194026 (2001-02-01), Warnes et al.
patent: 6287644 (2001-09-01), Jackson et al.
Joseph K. Doychak; The Evolution and Growth of A12O3Scales on Beta-NiAl; NASA Contractor Report #CR-175097, May 1986; pp. 1-239.
D.M Lipkin, H. Schaffer, F. Adar, D.R. Clarke; Lateral Growth Kinetics of alpha-Alumina Accompanying the Formation of a Protective Scale on (111) NiAl During Oxidation at 1100°C; Materials Dept., Univ. of California, Feb. 4, 1997; pp. 1-10; Applied Physics Letters vol. 70 No. 19 (1997) pp. 2550-2552.
E. Jordan, D. Pease, M. Gell; Bond Strength and Stress Measurements in Thermal Barrier Coatings; Clemson University Research Foundation Subcontract #95-01-SR030, Apr. 1, 1997-Sep. 30, 1997, pp. 1-65; U.S. Department of Energy Report #DOE/MC/29061-96/00676.
Philip Vais and Robert A. Rapp; Cyclic Oxidation of Oxide Thermal Barrier Coatings; Material Science and Engineering, The Ohio State University, May 18, 1998; pp. 1-9; Electric Power Research Institute Report # TR112440 (1998).
B.H. Kear, F.S. Pettit, D.E. Fornwalt, L.P. Lemaire; On the Transient Oxidation of a Ni-15Cr-6A1 Alloy; Oxidation of Metals vol. 3, No. 6, 1971; pp. 557-569.
S.J. Wilson and J.D.C. McConnell; A Kinetic Study of the System Gamma-A1OOH/A12O3; Journal of Solid State Chemistry, 34, 1980; pp. 315-322.
B.A. Pint, A. Jain, L.W. Hobbs; The Effect of Ion Implanted Elements on the Theta to Alpha Phase Transformation of A12O3Scales Grown on Beta-NiAl; Mat. Res. Soc. Symp. Proc., vol. 288, 1998; pp. 1013-1018.
O. Unal, T.E. Mitchell, and A.H. Heuer; Microstructures of Y2O3—Stabilized ZrO2Electron Beam-Physical Vapor Dep

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Thermal barrier coating method does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Thermal barrier coating method, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Thermal barrier coating method will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2988968

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.