Specialized metallurgical processes – compositions for use therei – Processes – Free metal or alloy reductant contains magnesium
Patent
1977-02-17
1978-09-12
Dean, R.
Specialized metallurgical processes, compositions for use therei
Processes
Free metal or alloy reductant contains magnesium
75162, 148 115C, C22C 901
Patent
active
041134753
ABSTRACT:
A copper base alloy of superior tarnish resistance consisting essentially of 7.0 to 8.5% aluminum by weight and 1.5 to 2.5% nickel by weight with the balance (89-91.5 wt %) being essentially copper.
The process by which the alloy is prepared is controlled so that the alloy is primarily single phased, i.e., a face centered cubic alpha phase solid solution containing a fine dispersion of nickel aluminide compound (NiAl) and less than 2 volume percent of the brittle intermetallic phases known as beta and gamma. By composition control and by producing an essentially single phased microstructure, the alloys of the invention are capable of forming a stable oxide film having high tarnish resistance.
The alloy, upon prolonged exposure indoors to ambient air and frequent handling, develops a very thin, tight, uniform oxide film which, although visible, is still attractive and does not mask the basic warm tone of the base metal. This film, when intact, serves to protect the underlying metal from further oxidation, and when damaged, is self-healing and reestablishes itself to provide a uniform protective and decorative film.
REFERENCES:
patent: 1496269 (1924-06-01), Iytaka
patent: 2210671 (1940-08-01), Kelly
patent: 2210672 (1940-08-01), Kelly
patent: 2210673 (1940-08-01), Kelly
patent: 2430419 (1947-11-01), Edens
patent: 2715577 (1955-08-01), Payne et al.
patent: 2798826 (1957-07-01), Klement
patent: 2870051 (1959-01-01), Klement
patent: 3259491 (1966-07-01), Pryor
patent: 3297437 (1967-01-01), Bosman
patent: 3341369 (1967-09-01), Caule et al.
patent: 3347717 (1967-10-01), Eichelman et al.
patent: 3364016 (1968-01-01), Mikawa
patent: 3402043 (1968-09-01), Smith
patent: 3416915 (1968-12-01), Mikawa
patent: 3783037 (1974-01-01), Brook et al.
patent: 3901692 (1975-08-01), Mikawa
patent: 3923500 (1975-12-01), Kitazawa et al.
patent: 3976479 (1976-08-01), Mitchell
patent: 4016010 (1977-04-01), Caron et al.
The Journal of the Institute of Metals, 1937, vol. LXI, pp. 83-102.
The Journal of the Institute of Metals, 1939, vol. LXV, pp. 217, 220, 222, 223.
Dean R.
Kennecott Copper Corporation
Lorusso Anthony M.
Skiff Peter K.
Sniado John L.
LandOfFree
Tarnish resistant copper alloy does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Tarnish resistant copper alloy, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Tarnish resistant copper alloy will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2382316