Superelastic guiding member

Details Superelastic guiding member Superelastic guiding member

2000-06-07

2002-10-08

Wyszomierski, George (Department: 1742)

Metal treatment

Stock

Mechanical memory

C148S426000, C420S456000, C604S530000

Reexamination Certificate

active

06461453

ABSTRACT:

BACKGROUND OF THE INVENTION
This invention relates to the field of medical devices, and more particularly to guiding means such as guidewires for advancing catheters within body lumens in procedures such as percutaneous transluminal coronary angioplasty (PTCA).
In typical PTCA procedures a guiding catheter having a preformed distal tip is percutaneously introduced into the cardiovascular system of a patient in a conventional Seldiger technique and advanced therein until the distal tip of the guiding catheter is seated in the ostium of a desired coronary artery. A guidewire is positioned within an inner lumen of a dilatation catheter and then both are advanced through the guiding catheter to the distal end thereof. The guidewire is first advanced out of the distal end of the guiding catheter into the patient's coronary vasculature until the distal end of the guidewire crosses a lesion to be dilated, then the dilatation catheter having an inflatable balloon on the distal portion thereof is advanced into the patient's coronary anatomy over the previously introduced guidewire until the balloon of the dilatation catheter is properly positioned across the lesion. Once in position across the lesion, the balloon is inflated to a predetermined size with radiopaque liquid at relatively high pressures (e.g. greater than 4 atmospheres) to compress the arteriosclerotic plaque of the lesion against the inside of the artery wall and to otherwise expand the inner lumen of the artery. The balloon is then deflated so that blood flow is resumed through the dilated artery and the dilatation catheter can be removed therefrom.
Conventional guidewires for angioplasty and other vascular procedures usually comprise an elongated core member with one or more tapered sections near the distal end thereof and a flexible body such as a helical coil disposed about the distal portion of the core member. A shapable member, which may be the distal extremity of the core member or a separate shaping ribbon which is secured to the distal extremity of the core member extends through the flexible body and is secured to a rounded plug at the distal end of the flexible body. Torquing means are provided on the proximal end of the core member to rotate, and thereby steer, the guidewire while it is being advanced through a patient's vascular system.
Further details of dilatation catheters, guidewires, and devices associated therewith for angioplasty procedures can be found in U.S. Pat. No. 4,323,071 (Simpson et al.); U.S. Pat. No. 4,439,185 (Lundquist); U.S. Pat. No. 4,516,972 (Samson); U.S. Pat. No. 4,538,622 (Samson etal); U.S. Pat. No. 4,554,929 (Samson etal.); U.S. Pat. No. 4,616,652 (Simpson); and U.S. Pat. No. 4,638,805 (Powell).
Steerable dilatation catheters with fixed, built-in guiding members, such as described in U.S. Pat. No. 4,582,181 (now Re 33,166) are frequently used because they have lower deflated profiles than conventional over-the-wire dilatation catheters and a lower profile allows the catheter to cross tighter lesions and to be advanced much deeper into a patient's coronary anatomy.
A major requirement for guidewires and other guiding members, whether they be solid wire or tubular members, Is that they have sufficient columnar strength to be pushed through a patient's vascular system or other body lumen without kinking. However, they must also be flexible enough to avoid damaging the blood vessel or other body lumen through which they are advanced. Efforts have been made to improve both the strength and flexibility of guidewires to make them more suitable for their intended uses, but these two properties are for the most part diametrically opposed to one another in that an increase in one usually involves a decrease in the other.
The prior art makes reference to the use of alloys such as NITINOL, which is an acronym for Ni—Ti Naval Ordnance Laboratory. These alloys have shape memory and/or superelastic characteristics and may be used in medical devices which are designed to be inserted into a patient's body. The shape memory characteristics allow the devices to be deformed to facilitate their insertion into a body lumen or cavity and then be heated within the body so that the device returns to its original shape. Superelastic characteristics on the other hand generally allow the metal to be deformed and restrained in the deformed condition to facilitate the insertion of the medical device containing the metal into a patient's body, with such deformation causing the phase transformation. Once within the body lumen the restraint on the superelastic member can be removed, thereby reducing the stress therein so that the superelastic member can return to its original undeformed shape by the transformation back to the original phase.
Alloys having shape memory/superelastic characteristics generally have at least two phases. These phases are a martensite phase, which has a relatively low tensile strength and which is stable at relatively low temperatures, and an austenite phase, which has a relatively high tensile strength and which is stable at temperatures higher than the martensite phase.
Shape memory characteristics are imparted to the alloy by heating the metal at a temperature above which the transformation from the martensite phase to the austenite phase is complete, i.e. a temperature above which the austenite phase is stable. The shape of the metal during this heat treatment is the shape “remembered”. The heat treated metal is cooled to a temperature at which the martensite phase is stable, causing the austenite phase to transform to the martensite phase. The metal in the martensite phase is then plastically deformed, e.g. to facilitate the entry thereof into a patient's body. Subsequent heating of the deformed martensite phase to a temperature above the martensite to austenite transformation temperature causes the deformed martensite phase to transform to the austenite phase and during this phase transformation the metal reverts back to its original shape.
The prior methods of using the shape memory characteristics of these alloys in medical devices intended to be placed within a patient's body presented operational difficulties. For example, with shape memory alloys having a stable martensite temperature below body temperature, it was frequently difficult to maintain the temperature of the medical device containing such an alloy sufficiently below body temperature to prevent the transformation of the martensite phase to the austenite phase when the device was being inserted into a patient's body. With intravascular devices formed of shape memory alloys having martensite-to-austenite transformation temperatures well above body temperature, the devices could be introduced into a patient's body with little or no problem, but they had to be heated to the martensite-to-austenite transformation temperature which was frequently high enough to cause tissue damage and very high levels of pain.
When stress is applied to a specimen of a metal such as NITINOL exhibiting superelastic characteristics at a temperature above which the austenite is stable (i.e. the temperature at which the transformation of martensite phase to the austenite phase is complete), the specimen deforms elastically until it reaches a particular stress level where the alloy then undergoes a stress-induced phase transformation from the austenite phase to the martensite phase. As the phase transformation proceeds, the alloy undergoes significant increases in strain but with little or no corresponding increases in stress. The strain increases while the stress remains essentially constant until the transformation of the austenite phase to the martensite phase is complete. Thereafter, further increase in stress are necessary to cause further deformation. The martensitic metal first yields elastically upon the application of additional stress and then plastically with permanent residual deformation.
If the load on the specimen is removed before any permanent deformation has occurred, th

Affiliated with

Also associated with

Rating

Superelastic guiding member does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Superelastic guiding member, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Superelastic guiding member will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFUS-PAI-O-2992372