Superconducting conductors and their method of manufacture

Electrical resistors – With terminal – With three or more terminals

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C174S125100, C505S236000

Reexamination Certificate

active

06657533

ABSTRACT:

BACKGROUND OF THE INVENTION
The invention relates to superconducting conductors such as composite superconductors.
Superconductors are generally classified as either low or high temperature superconductors. An important property of the superconductor is the disappearance of its electrical resistance when it is cooled below its critical temperature T
c
. For a given superconductor operating below T
c
, a maximum amount of current—referred to as the critical current (I
c
) of the superconductor—exists which can be carried by the superconductor at a specified magnetic field and temperature below its critical temperature (T
c
) and critical magnetic field (H
c
) Under these conditions, any current in excess of I
c
causes the onset of resistance in the superconductor.
The transition characteristics of low temperature superconducting (LTS) and high temperature superconducting (HTS) materials are quite different. In particular, for an LTS material, the transition between superconducting and non-superconducting occurs rather abruptly. This transition characteristic has made the use of LTS materials attractive in current limiting applications. Such LTS current limiting devices limit the flow of excessive current in electrical systems caused by, for example, short circuits, lightning strikes, or common power fluctuations. However, because the transition temperature of LTS materials is relatively low (i.e., generally about T
c
=4 K to 30 K), the cost associated with cooling such materials to temperatures below their T
cs
is high. Moreover, the cryogens used to achieve such low temperature add substantial cost and complexity, thereby lowering reliability of devices using such LTS materials, and must be handled with great care.
On the other hand, the transition characteristic of an HTS material is generally not abrupt. Rather, upon reaching its critical temperature or critical current value, the superconductivity of the HTS material gradually diminishes as its temperature or current flow rises until it reaches a temperature or current value at which the material no longer has any superconductivity characteristic.
Because of the significant non-linearities in the current-to-voltage (I-V) characteristics of both HTS and LTS materials over a range which includes both superconducting and non-superconducting states, small inhomogeneities in the critical current of the superconducting conductor, caused for example, by localized differences in diameter or composition, can lead to an inhomogeneous voltage distribution along the superconducting conductor, and localized thermal destruction of the superconducting conductor at the hot spots in this distribution.
SUMMARY OF THE INVENTION
The invention features an electrical conductor well-suited for superconducting current-limiting applications. The electrical conductor includes an elongated superconductor member including a superconducting material extending along its length. In one aspect, the superconductor member is a composite having superconducting material and a non-superconducting, electrically conductive matrix material. In another aspect, the superconductor member is a bulk superconducting material. In yet another aspect, the superconductor member is a composite having superconducting material mechanically supported by an substantially non-conductive matrix material. The electrical conductor is configured to control the manner in which the superconductor member transitions from its superconducting state to its non-superconducting (i.e., normal) state due to, for example, a fault current condition.
In a general aspect of the invention, the electrical conductor includes a thermal conductor attached to and along the length of the superconductor member, and an electrically-insulative material disposed between the thermal conductor and length of superconductor member, the electrically-insulative material having a thickness for allowing heat from the superconductor member to be conveyed to the thermal conductor.
In another aspect of the invention, a superconducting current-limiting device includes a support structure (e.g., an inner support tube) and the above-described electrical conductor disposed on the support structure.
In general, the superconductor member serves to carry the current during non-fault conditions with low electrical loss. In a preferred embodiment, a superconducting composite having the superconducting material and metal matrix, the matrix can provide an alternate current path to compensate for localized inhomogeneities in the superconductor during non-fault conditions. On the other hand, during a fault condition, the member carries the fault current with a high resistance for short periods of time. The thermal conductor serves as a thermal stabilizer and a heat sink during transient fault current events. In general, the thermal conductor prevents the superconducting material from getting too hot during a fault condition. The electrical conductor must not get too hot for two reasons: 1) it must have a quick thermal recovery characteristic, and 2) rapid large changes in temperature can cause thermal stresses sufficient to destroy the superconducting material. The thermal conductor is directly or indirectly thermally connected to a cooling channel. The cooling channel can be a liquid cryogen bath, gas cooling, or a conduction-cooling path (i.e., copper or alumina).
The electrically insulative material acts as a small thermal and electrical barrier having a two fold purpose. First, the insulative material prevents current transfer from the superconductor member into the thermal conductor. Second, the insulative material causes a delay in the heat transfer between superconductor member and the thermal barrier so that the superconducting material can completely revert to its normal, non-superconducting state.
The electrically-insulative material provides a thermal barrier that reduces the time needed for the superconductor to transition from a superconducting state to a non-superconducting state, thereby reducing the amount of current flowing through the superconducting material of the member and lowering the total current flowing through the electrical conductor. As a result, possible damage to the superconductor member caused by the excessive current flow and mechanical stresses (e.g., hoop stresses) is minimized.
Embodiments of either of the aspects of the invention may include one or more of the following features.
The superconducting material is in the form of a plurality of superconducting filaments, the superconducting filaments surrounded by a non-superconducting, metal matrix (e.g., silver or silver alloy). Alternatively, the superconducting material is in monolithic form as a coating on a non-conductive, or preferably a conductive, ceramic buffer layer supported on a metal substrate (e.g., a nickel, copper or aluminum alloy).
The thermal conductor is formed of spaced-apart thermally-conductive elements. The electrically-insulative material and the thermal conductor, together, form a first laminate. A second laminate is disposed on the first laminate and includes a second sheet of electrically-insulative material disposed on the first plurality of the thermal conductive elements of the first laminate and a second thermal conductor (preferably formed of a second plurality of spaced-apart thermally-conductive elements) attached to the second electrically-insulative material.
The thermally-conductive elements of the first laminate and the thermally-conductive elements of the second laminate are offset from each other relative to the length of the superconductor member. As a result, the electrical conductor has increased mechanical strength, particularly in wound structures.
In certain embodiments, the first laminate is attached to a first side of the length of the superconductor member and the second laminate is attached to a second, opposite side of the length of the superconductor member. The superconductor member in this form is “sandwiched” between two stabilizer members, thereby providing improved thermal stabil

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Superconducting conductors and their method of manufacture does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Superconducting conductors and their method of manufacture, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Superconducting conductors and their method of manufacture will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3178879

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.