Metal deforming – By pulling workpiece through closed periphery die – Utilizing plural metal-deforming tools
Reexamination Certificate
2000-03-13
2004-11-30
Cole, Elizabeth M. (Department: 1771)
Metal deforming
By pulling workpiece through closed periphery die
Utilizing plural metal-deforming tools
C072S378000, C148S500000, C148S579000, C148S595000, C148S598000, C148S612000, C148S645000, C428S606000
Reexamination Certificate
active
06823706
ABSTRACT:
TECHNICAL FIELD
The present invention relates to a steel wire used for reinforcement of rubber articles or the like having high strength and excellent ductility and a method of manufacturing the same.
BACKGROUND ART
In a conventional manufacturing process for a steel wire used for reinforcement of rubber articles such as steel radial tires or high pressure hoses, a high carbon steel rod containing about 0.70~0.90% in weight of carbon is drawn to an intermediate diameter and subjected to a heat treatment and brass plating to form a steel wire material, and then the steel wire material is drawn to the final diameter. When the steel wire thus obtained is used for reinforcement of a rubber article, the steel wire is embedded in non-vulcanized rubber in a form of a single wire or a steel cord formed by a plurality of the steel wire twisted together, and then heated to achieve vulcanization of the rubber and adhesion between the steel wire and the rubber.
Recently, a steel wire of higher strength is strongly desired with growing demand for conservation of energy and natural resource. In order to produce a steel wire of higher strength by the conventional manufacturing process described above, it is necessary to increase the amount of drawing performed on the steel wire material. However, when the amount of drawing is increased, ductility of the steel wire is deteriorated to cause frequent wire breakage in processing or poor durability in use. And in some cases, deterioration of ductility particularly at the surface layer of the steel wire can be a ruling factor on possible amount of drawing or achievable strength. This phenomenon is due to the fact that the drawing strain can concentrate more easily at the surface layer than can at the internal portion of the steel wire, making the surface layer become unable to withstand further drawing earlier than the internal portion. Moreover, deterioration of ductility at the surface layer can be aggravated by age hardening or poor lubrication due to heat generated by friction with drawing die. In order to overcome such problems in ductility, some improvements in drawing technique have been proposed.
Among such improvements in drawing technique, one approach is to control age hardening of steel wire by suppression of heat generation during drawing. For example, JP-A 8-24938 discloses a manufacturing method of a high tensile strength steel wire having such ductility that the steel wire can be given a large amount of torsion until it breaks when the wire is twisted to one direction wherein drawing at the final die is carried out with control of heat generation by limitation of friction coefficient and application of a skin pass with reduction of 2~11%.
Further, JP-A 8-218282 discloses a high tensile steel wire having torque reduction ratio of less than or equal to 7% in a torsion-torque test in which a steel wire is twisted to one direction and then twisted to the opposite direction. As a manufacturing method of such a steel wire, JP-A 8-218282 also discloses a drawing method wherein (1) drawing resistance is reduced by using dies of shorter bearing, (2) skin pass is adopted for the final drawing using double die, (3) dies with sintered diamond nib are used at several passes located downstream in order to reduce drawing force, and (4) temperature of lubricating fluid is maintained low.
However, even though a steel wire of less age hardening degree can be produced, the above drawing methods do not give essential improvement as to the concentration of strain at the surface layer, rather, causing more concentration of strain at the surface layer in case of applying excessively low reduction per die. Therefore, good ductility of a steel wire shown immediately after drawing can be largely deteriorated by preforming in cabling or by progression of age hardening due to heating in rubber.
Conventionally, ductility of a steel wire has been evaluated by value of breaking torsion which is defined as an amount of unidirectional torsion applied to a steel wire until the steel wire is broken, or by considering both value of breaking torsion and form of fracture. Another evaluating method is adopted in JP-A 8-218282 wherein ductility of a steel wire is evaluated by torsion-torque curve obtained in a torsion test in which a steel wire is twisted in one direction for a certain number of turns and then twisted in the opposite direction until the steel wire is broken.
However, steel wires showing good results in above evaluating methods do not always maintain good ductility after preforming such as cabling or after heat aging followed by preforming, and improvement in durability of rubber articles reinforced by such steel wires is not assured.
Generally, in production of a steel cord for reinforcement of rubber articles, steel wires are preformed so as to have minimum radius of curvature ranging from about 10 to 150 times their diameter. Particularly, production of such steel cords listed below comprises such a severe preforming that a steel filament is preformed so as to have minimum radius of curvature ranging from about 10 to 60 times its diameter. Therefore, when a conventional steel wire is used as a filament of such steel cords, ductility is considerably deteriorated by the severe preforming and further deteriorated largely by heating in rubber.
(1) A steel cord having so-called “open structure” comprising largely preformed steel filaments.
(2) A steel cord comprising a steel filament preformed into a polygonal spiral shape or wavy shape.
(3) A steel cord of core and sheath structure having a core comprising a steel filament formed into a wavy shape.
Another approach for controlling the deterioration of ductility accompanying with increase in tensile strength is to make distribution of strain in a steel wire developed by drawing more uniform so as to control deterioration of ductility in the surface layer where the strain reaches maximum. For example, JP-A 7-305285 discloses a method for manufacturing a steel wire wherein:
(1) reduction of each die used for drawing where drawing strain &egr; is less than 0.75 is set within a range between (22.67 &egr;+3)% and 29%, wherein &egr;=2ln(d
0
/d), d
0
is diameter in mm of steel wire material before drawing, and d is diameter in mm of steel wire after passing the die,
(2) reduction of each die used for drawing where &egr; is not less than 0.75 and not more than 2.25 is set within a range between 20% and 29%; and
(3) reduction of each die used for drawing where &egr; is more than 2.25 is set within a range between (−6.22 &egr;+43)% and (−5.56 &egr;+32.5)%.
By this method, substantial drawing strain at the surface area can be controlled, but controlling effect on age hardening due to heat generated by drawing is insufficient, and economical production becomes difficult with increasing drawing speed because of frequent wire breakage in cabling or drawing process.
In view of above problems of prior art, it is an object of the present invention to provide a steel wire having such a excellent ductility that the steel wire hardly breaks in cabling and little deteriorates by preforming or age hardening after preforming. And another object is to provide a method for economically manufacturing such a steel wire.
DISCLOSURE OF THE INVENTION
After various experiments and studies, the inventors found that very important points for achievement of above objects are;
(1) ductility of surface layer of a steel wire should be evaluated and regulated by a specially arranged repeated torsion test, and
(2) optimization of reduction per die at the final die is necessary as well as uniform distribution of strain induced by drawing for economical manufacturing of such a steel wire.
The present invention has been done based on the important points mentioned above and includes following aspects in which [1]~[4] relate to a steel wire having excellent ductility which little deteriorates by preforming or by age hardening after preforming, and [5]~[7] relate to a method
Fujita Masuhiro
Kaneko Yoshikazu
Kobayashi Toshiyuki
Masubuchi Hideki
Obana Naohiko
Bridgestone Corporation
Cole Elizabeth M.
Piziali Andrew
Sughrue & Mion, PLLC
LandOfFree
Steel wire and method of manufacturing the same does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Steel wire and method of manufacturing the same, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Steel wire and method of manufacturing the same will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3357481