ABSTRACT:
A two-stage bonding technique for bonding high density silicon nitride and other ceramic materials to stainless steel and other hard metals, and multilayered ceramic-metal composites prepared by the technique are disclosed. The technique involves initially slurry coating a surface of the ceramic material at about 1500.degree. C. in a vacuum with a refractory material and the stainless steel is then pressure bonded to the metallic coated surface by brazing it with nickel-copper-silver or nickel-copper-manganese alloys at a temperature in the range of about 850.degree. to 950.degree. C. in a vacuum. The two-stage bonding technique minimizes the temperature-expansion mismatch between the dissimilar materials.
REFERENCES:
patent: 2972808 (1961-02-01), Litton
patent: 3915369 (1975-10-01), Schmidt-Bruecken et al.
patent: 4055451 (1977-10-01), Cockbein et al.
patent: 4131459 (1978-12-01), Fletcher et al.
patent: 4263353 (1981-04-01), Patel
patent: 4293619 (1981-10-01), Landingham et al.
patent: 4325647 (1982-04-01), Maier et al.
patent: 4343865 (1982-08-01), Graham
patent: 4347089 (1982-08-01), Loehman
patent: 4394170 (1983-07-01), Sawaoka
patent: 4404262 (1983-09-01), Watmough
patent: 4469658 (1984-09-01), Kimura
patent: 4470537 (1984-09-01), Diem et al.
patent: 4492737 (1985-01-01), Conolly
patent: 4505418 (1985-03-01), Neidig et al.
patent: 4553472 (1985-11-01), Munro et al.
patent: 4614689 (1986-09-01), Ikeda et al.
patent: 4626451 (1986-12-01), Tanaka et al.
Metals Handbook, 8th Edition, vol. 1, p. 30, 1961.
R. L. Landingham and T. E. Shell, "Bonding Dense Si.sub.3 N.sub.4 Components to Steel for Elevated-Temperature Cycling Applications", UCRL-90188, Lawrence Livermore National Laboratory, Livermore, Calif., 94550, Draft, 9/20/84.
R. L. Landingham and T. E. Shell, Extended Abstract, 6/8/84.
R. L. Landingham and T. E. Shell, Abstract, 1/6/83.
S. A. Huffsmith and R. L. Landingham, "Pressure Bonding Molybdenum Alloy (TZM) to Reaction-Bonded Silicon Nitride", UCID-17805, Lawrence Livermore National Laboratory, Livermore, Calif., 94550, 6/8/84.
Ceramic Age, "High Temperature Metal Ceramic Seals", p. 15, Apr. 1954.
Landingham Richard L.
Shell Thomas E.
Carnahan L. E.
Godici Nicholas P.
Heinrich Samuel M.
Hightower Judson R.
Rajender Shyamala T.
LandOfFree
Steel bonded dense silicon nitride compositions and method for t does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Steel bonded dense silicon nitride compositions and method for t, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Steel bonded dense silicon nitride compositions and method for t will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-1674114