Staple fibers produced by a bulked continuous filament...

Stock material or miscellaneous articles – Coated or structually defined flake – particle – cell – strand,... – Staple length fiber

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C428S362000, C428S394000

Reexamination Certificate

active

06492020

ABSTRACT:

FIELD OF THE INVENTION
This invention relates to staple fibers, and more particularly, surface modified polyester staple fibers which are made by a bulked continuous filament (BCF) process, and fiber clusters made from such fibers which can be used as fiber filling material, especially polyester fiberfill.
BACKGROUND OF THE INVENTION
Polyester fiberfill is widely used as a relatively inexpensive filling material for pillows, quilts, sleeping bags, apparel, furniture cushions, mattresses and similar articles. Fiberfill is mostly produced from polyethylene terephthalate crimped staple. A wide range of such staple is available with different deniers, crimp geometry, crimp level, cut length, surface coating, cross-section and other properties. Polyester fiberfill is often coated with a silicone coating such as a polyaminosiloxane slickening agent and sometimes with other non-silicone slickeners, such as segmented polyethylene terephthalate/polyalkylene oxide. Such coatings improve the softness and the hand of the finished article and also contribute to reduce the tendency of the fiberfill to mat (i.e., to clump together) in the article during use. The overwhelming majority of staple filling fibers are carded and cross lapped to form batts which are then used as the filling material. Alternatively, the staple fibers are opened and blown as filling material in a final article.
Another type of filling material is fiber clusters, which are staple fibers which are formed into clusters before being used as a filling material. Contrary to batts made from staple fibers, fiber clusters can move within a ticking in a similar way to down or down/feather blends. Fiber clusters are currently produced from baled spiral crimp staple, made generally by a two step process (polymerization/spinning, then drawing). The staple fibers are first opened, then submitted to a rolling, or tumbling, action on roller cards, flat cards or by rolling against a wall of a cylinder. Known tumbling processes are disclosed in U.S. Pat. Nos. 4,618,531 and 4,783,364. Fiber clusters have gained acceptance in many filling end-uses in the last decade, and with increased volume and improved manufacturing processes, the price of such fiber clusters has slowly come down. However, the manufacture of fiber clusters is still a relatively low throughput and expensive process compared to carded batts, and this hinders further development of the market.
Crimp plays an essential role in the structure of fiber clusters and the ease of their formation. Moreover, crimp determines the filling power, softness and recovery from compression of fiberfill products. Commercial filling fibers may have either mechanical crimp or helical, or spiral, crimp. Mechanical crimp is produced by well known crimper box technology, while helical crimp is produced by asymmetrical quenching or by bicomponent conjugated spinning. Bicomponent conjugated fibers are produced either by spinning two polymers differing only in molecular chain length or by spinning two different polymers or copolymers. The crimp of these fibers results from differential shrinkage between the two polymers or their bicomponent structure when the fiber is exposed to heat. Halm et al., in U.S. Pat. No. 5,112,684, have demonstrated that fiber clusters for filling uses have been prepared from mechanically crimped fibers with specific configurations. Helical fiber clusters having a helical crimp are disclosed by Marcus in U.S. Pat. Nos. 4,618,531 and 4,783,364.
Practice has shown that helical crimp fibers made by asymmetrical quenching or by bicomponent conjugated spinning are the best feed materials for fiber clusters due to the ease of rolling as well as to the highly desired softness, refluffability and recovery from compression of the resulting fiber cluster filling. Feed fibers made by asymetric quenching or by bicomponent conjugated spinning form fiber clusters with spontaneous curling under low forces. Such fiber clusters have a uniform three dimensional entanglement, optimal bulk, and the best balance of softness and recovery from compression, as compared to fiber clusters formed by mechanical crimping. In addition, fibers which exhibit spontaneous curling produce fiber clusters with relatively few fibers sticking out of the fiber cluster, reducing the cohesion between the clusters. Low cohesion is particularly desirable in articles such as pillows and furniture back cushions, since it improves refluffability. Moreover, spontaneous curling not only improves the fiber cluster structure, but it also increases the cluster manufacturing throughput, by reducing the required rolling time.
Fiber spinning speed is typically much faster than the speeds of drawing/cutting and carding/tumbling processes for manufacturing staple fibers and staple fiber clusters. Under current conditions, matching a fiber spinning line with a staple fiber drawing/cutting process and a fiber cluster manufacturing process is very difficult and not economical. The low throughput processes used for producing fiber clusters according to known processes make it impractical to couple fiber spinning and drawing with fiber cluster production. Moreover, the two-step process for manufacturing staple fiber clusters of polymerization/spinning, then drawing/cutting is a complicated and high-cost process, because the uncoupled process requires extra material handling between process steps. In addition, its manufacturing and investment costs are high because it requires additional labor to operate a separate traditional draw machine, which operation is expensive. Moreover, the draw machine itself is expensive.
Thus, there exists a need for developing a simplified process for producing fibers which can be used to make fiber clusters. In particular, it would be desirable to minimize material handling by coupling the entire fiber/cluster manufacturing facility, including the spinning/drawing/cutting steps, as well as the cluster forming steps. Such a process would, ideally, produce low cohesion fiber clusters and would be much simpler and more economical, from a manufacturing standpoint, than the processes of the prior art.
Continuous jet bulking of yarns is widely used to produce carpet yarns, usually from polyamide or polypropylene. Machines for performing such continuous et bulking of yarns are available in the trade from Neumag of Neumunster, Germany, as well as other machine manufacturers. Neumag's standard high-speed continuous staple fiber producing line can produce items based on virtually any polymer, including polyester, as disclosed in “Easy routes to fibre production”, ITMA Report: MMF Equipment,
Textile Month
, December, 1995, pp. 15-20. However, it is not known to us e such a line to produce surface modified staple fiber. Nor is it known to use continuous jet bulking for producing polyester staple fiber for use in fiber clusters.
SUMMARY OF THE INVENTION
Applicants have found that polyester staple fibers produced by a bulked continuous filament (BCF) process can form fiber clusters much faster than conventional processes used for making asymetrically quenched or conjugated bicomponent fibers. The structure of such fiber clusters is very similar to the structure of fiber clusters produced from helical fibers, and the filling power of such fiber clusters can be equal to or better than such fiber clusters of the prior art, depending upon the structure of the fiber clusters and the bulking conditions.
Moreover, the BCF process of the present invention enables one to produce fibers with excellent durability and with bulk levels in end products, such as pillows and cushions, which are higher than the bulk levels of products made with cluster of the prior art. Surprisingly, these properties can be achieved under very gently rolling conditions.
Furthermore, the BCF process of the present invention enables one to adjust either the support bulk or the initial height of the end product independently, which is not possible with the prior art. This makes it possible to produce the optimal compression curve for an an en

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Staple fibers produced by a bulked continuous filament... does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Staple fibers produced by a bulked continuous filament..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Staple fibers produced by a bulked continuous filament... will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2963621

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.