Plastic and nonmetallic article shaping or treating: processes – Optical article shaping or treating – Light polarizing article or holographic article
Reexamination Certificate
2000-05-16
2003-02-04
Vargot, Mathieu D. (Department: 1732)
Plastic and nonmetallic article shaping or treating: processes
Optical article shaping or treating
Light polarizing article or holographic article
C264S002500
Reexamination Certificate
active
06514437
ABSTRACT:
BACKGROUND OF THE INVENTION
The present invention relates to a stamper protecting layer set in a molding apparatus for use in molding an optical disk, an optical disk molding apparatus with the stamper protecting layer, and an optical disk molding method carried out with the optical disk molding apparatus.
Conventionally, optical disks are molded by a molding apparatus
1
shown in FIG.
6
. The molding apparatus
1
is in a concentric structure with respect to a center axis
4
, and therefore a part of the apparatus to the left of the center axis
4
is not illustrated in FIG.
6
. The molding apparatus
1
has two molds
2
and
10
made of steel materials, for example a stainless steel. The mold
2
is movable for opening and includes a stamper
3
for forming pits representing recording information on an optical disk to be molded. The mold
10
is fixed and has a sprue
6
to inject a resin therethrough to form the optical disk.
The optical disk is molded with the use of the above molding apparatus
1
in a manner as will be described hereinbelow. After the stamper
3
is set to the mold
2
, the resin is injected through the sprue
6
to a cavity
5
defined between the closed molds
2
and
10
where the optical disk is molded. Concaves and convexes
9
formed on the stamper
3
are transferred to the resin. After the transfer of the concaves and convexes
9
, the filled resin is cooled and then the mold
2
is opened. When the mold
2
is completely opened, both the resin present in the sprue
6
and a molded body formed by the cavity
5
which becomes the optical disk are pressed up by an ejection rod
7
, to thereby separate the molded body from the mold
2
. After the ejection, the molded body is carried outside the molding apparatus
1
by a take-out device.
In a sequence of the above processes, when the resin supplied through the sprue
6
is filled into the cavity
5
, a tensile force acting in a radial direction of the stamper
3
because of a viscosity of the resin and a thermal stress due to temperature changes during the repeated heating and cooling are exerted to the stamper
3
. Meanwhile, the tensile force due to the viscosity of the resin and the thermal stress do not act on the mold
2
. As a result of this, a friction force is brought about between the mold
2
and stamper
3
in a direction I which is a diametrical direction of the optical disk, thereby wearing the stamper
3
and mold
2
at a contact part
8
. The wear is generally called an adhesive wear, which involves digging into the mold
2
and stamper
3
. Namely, microscopically, contact surfaces of the stamper
3
and mold
2
are not completely flat and have irregularities. Thus, projections in the irregularities cause the formation of adhesive portions and then the adhesive portions formed between the stamper
3
and mold
2
cause digging out from (i.e. wear of) the stamper
3
or mold
2
due to the friction force in the I direction. Because of projections and recesses formed consequent to the wear, as shown in
FIG. 7
, several-&mgr;m projecting parts
21
are formed at the contact part
8
of the mold
2
and thus projecting parts
22
corresponding to the projecting parts
21
appear at a recording face
9
a
of the stamper
3
having the above-mentioned concaves and convexes
9
. The projecting parts
22
at the recording face
9
a
are transferred to the molded body. Therefore, if the projecting parts
22
at the recording face
9
a
exceed a tolerance, the molded body is rejected, which leads to a yield decrease. The stamper
3
is required to be exchanged when characteristics of the molded body are over an acceptable limit.
However, it takes considerable time to exchange the stamper
3
, lowering productivity of optical disks. The number of exchange times for the stamper
3
should thus be reduced. To cope with this, a surface
2
a
of the mold
2
is coated in some cases to restrict the wear at the contact part
8
between the stamper
3
and mold
2
. TiN is primarily used for the coating. While a wear resistance of the surface
2
a
of the mold
2
is improved in the presence of the coating layer, the TiN is adhered to the surface
2
a
of the mold
2
by plasma vapor deposition, in other words, an adhesive force of the TiN to the mold
2
is not strong. As such, if the coating layer is partly separated by the above-discussed friction force in the I direction, an abrasive wear acting on the stamper
3
by the separated TiN is stronger because the TiN has a hardness as large as approximately ten times the hardness of the stamper
3
. The cut waste of the stamper
3
scraped off by the separated TiN produces the projecting parts
22
of the recording face
9
a
of the stamper
3
, similar to the previously-mentioned case. With the use of the coating layer, although the stamper
3
undergoes less adhesive wear, the separated TiN brings about projecting parts
22
on the recording face
9
a,
making it difficult to secure mechanical characteristics of the optical disk as the molded body.
For solving the above disadvantages, fats and oils such as wax or the like, or lubricant oil are sometimes applied to the surface
2
a
of the mold
2
. However, the fats and oils such as wax or the like lack stability under high temperature for a long time. Moreover, the fats and oils emit moisture contained therein when heated, thus adversely influencing the stamper
3
or mold
2
. To uniformly apply the fats and oils to the surface
2
a
of the mold
2
is a difficult task, and reproducibility is poor. In addition, foreign matter such as dust, etc. readily adhere to the fats and oils to thereby decrease the quality of the molded body. Metallic components contained in a mineral oil which is a kind of the lubricant oil react to and affect the stamper
3
and mold
2
.
SUMMARY OF THE INVENTION
The present invention is devised to solve the above-described disadvantages, and has for its object to provide a stamper protecting layer for a molding apparatus for an optical disk, an optical disk molding apparatus with the stamper protecting layer and an optical disk molding method which improve quality and production of optical disks.
According to a first aspect of the present invention, there is provided a stamper protecting layer arranged on a whole surface of a stamper opposed to a first mold of molds for molding an optical disk and interposed between the first mold and the stamper fitted to the first mold to form pits representing recording information on the optical disk.
The stamper protecting layer is so constructed as to absorb forces generated by extension and shrinkage of the stamper in a diametrical direction of the stamper relative to the first mold thereby preventing the stamper from being deformed upon molding of the optical disk.
According to the first aspect of the present invention, the stamper protecting layer is provided between the stamper and the first mold so as to absorb the forces generated by extension and shrinkage of the stamper relative to the mold in the diametrical direction of the stamper, to thereby prevent the stamper from being deformed when the optical disk is molded. The stamper protecting layer eliminates direct contact between the stamper and the first mold and absorbs the forces generated by extension and shrinkage of the stamper upon molding. The stamper is prevented from being deformed which would otherwise be caused by the projections and recesses consequent to the wear digging of the stamper or the first mold.
Accordingly, the quality and production of optical disks manufactured with the use of the stamper are improved.
According to a second aspect of the present invention, there is provided an optical disk molding apparatus comprising:
molds for molding an optical disk;
a stamper for being fitted to a first mold of the molds to form pits representing recording information on the optical disk; and
a stamper protecting layer arranged on a whole surface of the stamper opposed to the first mold and interposed between the first mold and the stamper, and being so con
Higashida Takaaki
Kadoriku Shinji
Maruyama Yoshio
Yutani Hiroshi
Vargot Mathieu D.
Wenderoth , Lind & Ponack, L.L.P.
LandOfFree
Stamper protecting layer for optical disk molding apparatus,... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Stamper protecting layer for optical disk molding apparatus,..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Stamper protecting layer for optical disk molding apparatus,... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3157245