Stainless steel

Metal treatment – Process of modifying or maintaining internal physical... – Heating or cooling of solid metal

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C148S607000

Reexamination Certificate

active

06340400

ABSTRACT:

The present invention relates to a stainless steel having improved hardness and crack resistance whilst on the other hand corrosion resistance is not affected.
The most common stainless ball bearing steel known in the art is 440C. comprising about 0.95-1.20 wt % C., 16-18 wt % Cr, 0.75 wt % Mo, <1.0 wt % Si, <1.0 wt % Mn, <0.4 wt % P, <0.03 wt % S. Such a steel is austenitized at around 1040° C. after which it is hardened in a usual way. The final hardness is around HRC 58-60.
For some application this hardness is insufficient in the long term making a regular replacement of ball bearing components necessary. Replacement is always necessary if cracking occurs. This cracking originates from quenching.
A further use of 440C. steel is in tools. However, the same drawbacks in the use of ball bearing steels are found being in certain conditions insufficient wear resistance and the risk of introducing cracks during quenching.
The invention aims to provide a stainless steel having increased hardness without resulting in increased tendency of cracking.
According to the invention this is realized with a stainless steel comprising: 0.8-1.4 wt % C., 18-26 wt % Cr, 2-4 wt % Ni, 0-1 wt % Mo, 0 wt % Pb and <0.6 wt % Si. Because of the composition given above it is possible to lower the austenitizing temperature to below 1050° C. and more particular to below 1040° C., for example to 950° C. This lower austenitizing temperature saves heat treatment costs and it was found that it also did reduce the tendency of cracking during subsequent quenching the nickel percentage will have an effect on the structure to be obtained. According to the invention it is aimed to realize a fully austenitic structure in contrast to the prior art wherein some ferrite will be present. This austenite will during quenching be converted to martensite. If ferrite is present such a transformation will not automatically be observed. However, if the nicklel percentage is too high hardening will be affected.
The carbon percentage can be up to 1.4%. Above 1.4 carbon will result in hardening problems.
More particular the stainless steel described above comprises between 0.9 and 1.0 wt % C. The chromium percentage is preferably between 20-24 wt %. The stainless steel described above can be used for all imaginable applications, such as tools. However, a special use is in the field of ball bearings. It has been found that the corrosion resistance of the above stainless steel is sufficient because around 13-14 wt % Cr will be in solution of the FCC. phase if it is austenitized above about 840° C. Hardening can both be effected throughout the component to be prepared by furnace hardening or surface hardening can be used.
An article from the steel described above can be realized both by starting from a rolled item and machining or through powder metallurgy. The last method would be attractive if articles have to be made with complicated shape.
It is remarked that from the Japanese application 60-210837/62-70551 a steel powder is known used for production of valve seats. To that end Pb or Sn is introduced for self lubrication which was thought to be essential at that time for valve seats. There is no information about heat treatment and resulting hardness.


REFERENCES:
patent: 2916337 (1959-12-01), Fike et al.
patent: 24 47 137 (1975-04-01), None
patent: 0 295 111 (1988-12-01), None
patent: 60-210837 (1985-10-01), None
patent: 07316748 (1995-12-01), None
patent: 090 87944 (1997-03-01), None

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Stainless steel does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Stainless steel, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Stainless steel will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-2869364

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.