ABSTRACT:
CROSS-REFERENCE TO RELATED APPLICATIONS
This application is related to application Ser. No. 08/942,830, filed Oct. 2, 1997 now U.S. Pat. No. 5,959,506.
BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to copolymers of maleic anhydride (MAN) and a C
1
-C
4
alkyl vinyl ether (AVE), and, more particularly, to solvent-free, fine white powders of such copolymers having advantageously high molecular weights and without taste or odor, for use in oral care products, particularly denture adhesives, and to a solvent-free process for making such copolymers.
2. Detailed Description of the Prior Art
British Pat. 906,230 described the preparation of copolymers of maleic anhydride and methyl vinyl ether in benzene as solvent. Example 1 also disclosed a copolymerization process in absence of solvent in which powdered maleic anhydride, methyl vinyl ether and initiator were precharged into an autoclave and reacted at 55° C. The specific viscosity (SV) of the product, however, was only 3.45 (1% in methyl ethyl ketone, MEK).
U.S. Pat. No. 5,047,490 described a polymerization process substantially the same as Example 1 of British 906,230. However, the reference does not disclose any procedure for separation of remaining traces of MVE from the product, other than distilling off the MVE from the reactor. Accordingly, such polymers inevitably carry a bad taste and odor which is unacceptable for oral care products such as denture adhesives. Furthermore, the SV of the polymers obtained therein was only 2 to 5.
Accordingly, it is an object of this invention to provide a solvent-free process for making high molecular weight copolymers of MAN and an AVE, particularly having an SV of >6, and which are without taste or odor, so that they can be used advantageously in commercial oral care products such as denture adhesives.
These and other objects and features of the invention will be made apparent from the following more particular description of the invention.
SUMMARY OF THE INVENTION
What is described herein is a solvent-free process for making fine powders of high molecular weight alternating copolymers of maleic anhydride (MAN) and a C
1
-C
4
alkyl vinyl ether (AVE), having a molecular structure of (A-B)
n
, where A=MAN and B=AVE, and n is an integer which is indicative of its molecular weight.
The copolymers obtained herein have a specific viscosity (SV) which is ≧6 (1% in MEK, 25° C.), corresponding to an absolute weight average molecular weight in excess of 3,500,000 (GPC/MALLS, water pH 9).
The solvent-free process of the invention is carried out by precharging an alkyl vinyl ether in an amount substantially greater than the 1:1 mole ratio required to provide a 1:1 mole ratio of AVE to MAN in the copolymer, adding a free radical initiator, heating the mixture to a reaction temperature of about 50° to 100° C., thereafter feeding molten MAN into the reactor over a predetermined period of time and holding the reactants at a defined temperature for a predetermined time. Unreacted AVE is then stripped off and a stabilizer antioxidant is added to the copolymer and the copolymer is dried.
The high molecular weight copolymers obtained thereby are odorless and tasteless and free of trace amounts of solvents characteristic of other known processes for making such copolymers.
DETAILED DESCRIPTION OF THE INVENTION
In accordance with the invention, there is provided herein a solvent-free process for making solvent-free, fine white powders of high molecular weight copolymers of maleic anhydride and a C
1
-C
4
alkyl vinyl ether, preferably methyl vinyl ether (MVE). In this invention, the specific viscosity (SV) of the solvent-free copolymers is >6 (1% wt/vol in MEK, 25° C.), corresponding to an absolute weight average molecular weight of at least 3,500,000 (GPC, water, pH 9).
The solvent-free polymerization process of the invention is carried out using an excess of alkyl vinyl ether as the reaction medium, preferably by precharging the alkyl vinyl ether into the reactor, adding a radical initiator, heating to a reaction temperature of about 50° to 100° C., and, thereafter, feeding molten maleic anhydride into the reactor over a predetermined period of time, followed by holding at a defined temperature for a predetermined period of time.
An effective amount of a food grade antioxidant stabilizer, such as t-butyl hydroquinone (TBHQ), butylated hydroxy-anisole (BHA), butylated hydroxy-toluene (BHT), propyl gallate (PG) and the like, preferably is added to the copolymer product before drying.
After adding stabilizer, the remaining AVE is stripped off, and the polymer is dried at about 40-100° C. under vacuum, to remove any remaining traces of AVE. The desired copolymer is obtained as a solvent-free, fine powder, of desired high SV, and it is odorless and tasteless.
In the preferred embodiments of the process of the invention, the MAN reactant is introduced into the precharged MVE over a period of at least 1 hour and the % solids of the copolymer in the polymerization mixture is about 10-40%. The MVE:MAN mole ratio is maintained at about 25:1 to 5:1, most preferably 12:1 to 7:1. The initiator concentration is 0.01 to 0.2%, most preferably 0.05 to 0.1% by wt., based on the copolymer obtained.
REFERENCES:
patent: 4948848 (1990-08-01), Tazi et al.
patent: 5003014 (1991-03-01), Tazi et al.
patent: 5830933 (1998-11-01), Synodis et al.
patent: 6008274 (1999-12-01), Meyer et al.
Choi Ling-Siu
Davis William J.
ISP Investments Inc.
Katz Walter
Maue Marilyn J.
LandOfFree
Solvent-free, fine white powders of high molecular weight... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Solvent-free, fine white powders of high molecular weight..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Solvent-free, fine white powders of high molecular weight... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2574464