ABSTRACT:
TECHNICAL FIELD
The present invention relates to a process for producing a solid electrolytic capacitor and more specifically, relates to a solid electrolytic capacitor using a conducting polymer as the electrolyte.
BACKGROUND OF THE INVENTION
1. Conventional Materials for Solid Electrolytic Layer
Electrolytic capacitors comprise an oxide film layer functioning as a dielectric material and an electrode drawn out from the oxide film layer, the oxide film layer being formed on an anode electrode comprising a valve action metal such as tantalum and aluminium and being arranged with micro-pores and etching pits.
Herein, the electrode is drawn out, via an electrolytic layer with electric conductivity, from the oxide film layer. Accordingly, the electrolytic layer serves as a practical cathode in such electrolytic capacitors. For an aluminium electrolytic capacitor, for example, a liquid electrolyte is used as a practical electrode, while the cathode electrode only serves for the electrical connection between the liquid electrolyte and an external terminal.
The electrolytic layer functioning as a practical cathode should essentially be adhesive to the oxide film layer, and be dense and uniform. Specifically, the adhesion inside the micro-pores and etching pits of the anode electrode significantly influences the electrical performance. Conventionally, therefore, numerous electrolytic layers have been proposed.
Solid electrolytic capacitors comprise solid electrolytes with electric conductivity, in place of liquid electrolytes defective of any impedence characteristic in the high-frequency region due to the ion conductivity. Specifically, manganese dioxide and 7, 7, 8, 8-tetracyanoquinodimethane (TCNQ) complex have been known as such solid electrolytes.
More specifically, a solid electrolytic layer comprising manganese dioxide is produced by dipping an anode element comprising sintered tantalum in an aqueous manganese nitrate solution, followed by thermal decomposition at a temperature around 300° C. to 400° C. The oxide film layer in capacitors comprising such solid electrolytic layer is readily damaged during the thermal decomposition of manganese dioxide, so the leakage current is likely to increase; because the specific resistance of manganese dioxide is high, additionally, the resulting impedence characteristic is not sufficiently satisfactory.
Furthermore, the lead wire is damaged at the thermal process. Therefore, a post-process is needed to additionally arrange an outer connecting terminal.
Alternatively, a solid electrolytic capacitor comprising the TCNQ complex as described in Japanese Patent Laid-open No. 58-191414 has been known as one of the aforementioned solid electrolytic capacitors, which is produced by thermally melting the TCNQ complex, and dipping an anode electrode in the resulting melt TCNQ complex or coating the resulting melt TCNQ complex on the anode electrode. The TCNQ complex is highly conductive, with the resultant great effects in terms of frequency characteristic and temperature performance.
Because the melting point of the TCNQ complex and the decomposition point thereof are very close so the melt TCNQ complex is readily converted to an insulating substance under some temperature condition, the temperature control of the complex is tough during the process of capacitor production; additionally because the TCNQ complex per se is defective of thermal resistance. the characteristic properties of the complex are distinctively modified by the soldering heat during the mounting process on a print board.
2. Application of Conducting Polymer
So as to overcome the inconvenience of manganese dioxide and TCNQ complex, furthermore, attempts have been made in recent years about the use of conducting polymers such as polypyrrole as solid electrolytic layer.
Conducting polymers typically including polypyrrole are primarily produced by chemical oxidation polymerization (chemical polymerization) and electrolytic oxidation polymerization (electrolytic polymerization). It has been difficult to produce a dense layer with a large strength by chemical polymerization.
By electrolytic polymerization, alternatively, a voltage should be applied to a subject material on which an oxide film layer is to be formed. Therefore, it is difficult to apply electrolytic polymerization to an anode electrode with an insulating oxide film layer formed on the surface thereof for electrolytic capacitors. Hence, a process has been proposed, comprising preliminarily forming a conductive precoating layer, for example a conducting polymer layer formed by chemical polymerization using an oxidant, on the surface of an oxide film layer, and subsequently forming an electrolytic layer by electrolytic polymerization using the precoating layer as an electrode (Japanese Patent Laid-open 63-173313, Japanese Patent Laid-open 63-158829; manganese dioxide functions as the precoating layer).
However, the process of preliminarily forming the precoating layer is complicated; and by electrolytic polymerization, a solid electrolytic layer is formed, starting from the proximity of an outer electrode arranged on the positive electrode face covered with the oxide film layer for the purpose of polymerization. Accordingly, it has been very difficult to continuously form a conducting polymer film of a uniform thickness over a wide range.
Thus, another attempt has been made to form an electrolytic layer comprising a conducting polymer film, by winding an anode electrode and a cathode electrode, both in foil shapes, while a separator is interposed between these electrodes, to form a so-called wound capacitor element, allowing the capacitor element to be impregnated with a monomer such as pyrrole and an oxidant, to form the conducting polymer film by chemical polymerization alone.
Such wound capacitor element has been known for aluminium electrolytic capacitors. It has been desired to avoid any complicated electrolytic polymerization by supporting the conducting polymer layer with a separator and to enlarge the capacity of the resulting capacitor by using an electrode in a foil shape of a larger surface area.
Both the electrodes and the separator can be supported at a constant fastening strength by using the wound capacitor element, which is indicated to make contribution to the adhesion between both the electrodes and the electrolytic layer.
When the capacitor element is impregnated with a mixture solution of the monomer and an oxidant, the monomer and the oxidant are rapidly polymerized together, so that the resulting solid electrolytic layer is never formed deeply inside the capacitor element. Thus, it has been found that the desired electrical performance can never be yielded.
Then, an attempt has been made to lower the polymerization temperature of the solution during the polymerization reaction, with the resultant more or less great electrical performance. Nevertheless, the resulting pressure resistance is still insufficient, disadvantageously.
Additionally, chemical polymerization at low temperature requires strict temperature control and a complicated apparatus, so that the final product is disadvantageously costly.
3. Poly(ethylenedioxythiophene) of Interest
Alternatively, various conducting polymers have been examined. A technique (Japanese Patent Laid-open 2-15611) focused on poly(ethylenedioxythiophene) (PEDT) at a slow reaction velocity and with excellent adhesion to the oxide film layer of the anode electrode has been reported.
With attention focused on the slow polymerization velocity of poly(ethylenedioxythiophene), the present inventors have submitted an application (Japanese Patent application 8-131374) of an invention to generate poly(ethylenedioxythiophene) inside a capacitor element, comprising winding through the medium of a separator an anode electrode foil and a cathode electrode foil to fabricate a capacitor element, allowing the capacitor element to be impregnated with a mixture solution of a monomer and an oxidant solution, and generating a solid electrolyte poly(ethylenedioxythiophene) by the che
Kaneko Atsuko
Murakami Toshiyuki
Nogami Katsunori
Shimada Akihiro
Dinkins Anthony
Nippon Chemi-Con Corporation
Price and Gess
LandOfFree
Solid electrolytic capacitor and process for producing the same does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Solid electrolytic capacitor and process for producing the same, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Solid electrolytic capacitor and process for producing the same will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2486852