Stock material or miscellaneous articles – Structurally defined web or sheet – Continuous and nonuniform or irregular surface on layer or...
Reexamination Certificate
2000-06-21
2003-12-09
Loney, Donald J. (Department: 1772)
Stock material or miscellaneous articles
Structurally defined web or sheet
Continuous and nonuniform or irregular surface on layer or...
C428S409000, C428S428000, C428S702000
Reexamination Certificate
active
06660365
ABSTRACT:
FIELD OF THE INVENTION
The present invention provides a coating for glass substrates and the like which resist accumulation of dirt and water stains. Coated glass substrates of the invention can be used in insulated glass units wherein the coating of the invention is carried on an exterior surface of one pane of glass while a reflective coating is applied on the opposite side of the same pane of glass.
BACKGROUND OF THE INVENTION
Keeping windows and other glass surfaces clean is a relatively expensive, time-consuming process. While cleaning any individual window is not terribly troublesome, keeping a larger number of windows clean can be a significant burden. For example, with modern glass office towers, it takes significant time and expense to have window washers regularly clean the exterior surfaces of the windows.
Windows and other glass surfaces can become “dirty” or “soiled” in a variety of ways. Two of the primary manners in which windows can collect dirt involve the action of water on the glass surface. First, the water itself can deposit or collect dirt, minerals or the like onto the surface of the glass. Obviously, dirty water landing on the glass will leave the entrained or dissolved dirt on the glass upon drying. Even if relatively clean water lands on the exterior surface of a window, each water droplet sitting on the window will tend to collect dust and other airborne particles as it dries. These particles and any other chemicals which become dissolved in the water will become more concentrated over time, leaving a characteristic spot or drying ring on the glass surface.
The second way in which water tends to give a window or other glass surface a soiled or less attractive appearance is tied to an attack on the glass surface itself. As a droplet of even relatively clean water sits on a glass surface, it will begin to leach alkaline components from the glass. For a typical soda lime glass, the soda and lime will be leached out of the glass, increasing the pH of the droplet. As the pH increases, the attack on the glass surface will become more aggressive. As a result, the glass which underlies a drying water droplet will become a little bit rougher by the time the water droplet completely dries. In addition, the alkaline components which were leached out of the glass will be redeposited on the glass surface as a drying ring. This dried alkaline material not only detracts from the appearance of the glass; it will also tend to go back into solution when the glass surface is wetted again, rapidly increasing the pH of the next water droplet to coalesce on the glass surface.
In storing and shipping plate glass, the presence of water on the surfaces between adjacent glass sheets is a chronic problem. One can take steps to shield the glass from direct contact with water. However, if the glass is stored in a humid environment, water can condense on the glass surface from the atmosphere.
This becomes more problematic when larger stacks of glass are collected. Large stacks of glass have a fairly large thermal mass and will take a long time to warm up. As a consequence, they will often be cooler than the ambient air when ambient temperature increases (e.g., in the morning), causing moisture in the air to condense on the surface of the glass. Due to limited air circulation, any moisture which does condense between the sheets of glass will take quite a while to dry. This gives the condensed moisture a chance to leach the alkaline components out of the glass and adversely affect the glass surface. The rate of attack can be slowed down somewhat by applying an acid to the surface of the glass. This is commonly done by including a mild acid, e.g., adipic acid, in the separating agent used to keep glass sheets from sticking to and scratching one another.
A number of attempts have been made to enable a glass sheet to keep a clean appearance longer. One avenue of current investigation is a “self-cleaning” surface for glass and other ceramics. Research in this area is founded on the ability of certain metal oxides to absorb ultraviolet light and photocatalytically break down biological materials such as oil, plant matter, fats and greases, etc. The most powerful of these photocatalytic metal oxides appears to be titanium dioxide, though other metal oxides which appear to have this photocatalytic effect include oxides of iron, silver, copper, tungsten, aluminum, zinc, strontium, palladium, gold, platinum, nickel and cobalt.
While such photocatalytic coatings may have some benefit in removing materials of biological origin, their direct impact on other materials is unclear and appears to vary with exposure to ultraviolet light. As a consequence, the above-noted problems associated with water on the surface of such coated glasses would not be directly addressed by such photocatalytic coatings.
A number of attempts have been made to minimize the effect of water on glass surfaces by causing the water to bead into small droplets. For example, U.S. Pat. No. 5,424,130 (Nakanishi, et al., the teachings of which are incorporated herein by reference) suggests coating a glass surface with a silica-based coating which incorporates fluoroalkyl groups. The reference teaches applying a silicone alkoxide paint onto the surface of the glass, drying the paint and then burning the dried paint in air. Nakanishi, et al. stress the importance of substituting part of the non-metalic atoms, i.e., oxygen in a layer of SiO
2
, with a fluoroalkyl group. Up to 1.5% of the oxygen atoms should be so substituted. Nakanishi, et al. state that if less than 0.1% of the oxygen atoms are substituted with a fluoroalkyl group, the glass won't repel water properly because the contact angle of water on the glass surface will be less than 80°.
Such “water repellent” coatings do tend to cause water on the surface of the glass to bead up. If the coating is applied to an automobile windshield or the like where a constant flow of high velocity air is blowing over the surface, this water beading effect can help remove water from the glass surface by allowing the droplets to blow off the surface. However, in more quiescent applications, these droplets will tend to sit on the surface of the glass and slowly evaporate. As a consequence, this supposed “water repellent” coating will not solve the water-related staining problems noted above. To the contrary, by causing the water to bead up more readily, it may actually exacerbate the problem.
Other silica coatings have been applied to the surface of glass in various fashions. For example, U.S. Pat. No. 5,394,269 (Takamatsu, et al.) proposes a “minutely rough” silica layer on the surface of glass to reduce reflection. This roughened surface is achieved by treating the surface with a supersaturated silica solution in hydrosilicofluoric acid to apply a porous layer of silica on the glass sheet. By using a multi-component of sol gel solution, they claim to achieve a surface which has small pits interspersed with small “islet-like land regions” which are said to range from about 50-200 nm in size. While this roughened surface may help reduce reflection at the air/glass interface, it appears unlikely to reduce the water-related staining problems discussed above. If anything, the porous nature of this coating appears more likely to retain water on the surface of the glass. In so doing, it seems probable that the problems associated with the long-term residence of water on the glass surface would be increased.
SUMMARY OF THE INVENTION
In one aspect, the present invention provides a glass article which has a water-sheeting coating and a method of applying such a coating. In accordance with a first embodiment of this invention, a glass article has at least one coated surface bearing a water-sheeting coating. This water-sheeting coating comprises silica sputtered directly onto an exterior surface of the glass. The water-sheeting coating has an exterior face which is substantially non-porous, but which has an irregular surface. This water-sheeting coating desirably reduces the wetting angle of
Hartig Klaus
Krisko Annette
O'Shaughnessy Roger D.
Cardinal CG Company
Fredrikson & Byron , P.A.
Loney Donald J.
LandOfFree
Soil-resistant coating for glass surfaces does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Soil-resistant coating for glass surfaces, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Soil-resistant coating for glass surfaces will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3133718