Catalyst – solid sorbent – or support therefor: product or process – Zeolite or clay – including gallium analogs – And additional al or si containing component
Reexamination Certificate
2001-09-24
2004-04-27
Dunn, Tom (Department: 1725)
Catalyst, solid sorbent, or support therefor: product or process
Zeolite or clay, including gallium analogs
And additional al or si containing component
C502S527120, C502S439000
Reexamination Certificate
active
06727201
ABSTRACT:
TECHNICAL FIELD
The present invention relates to a method for manufacturing a zeolite-carrying adsorption element and slurry used for attaching zeolite to a carrier (hereinafter referred to as “slurry for carrying zeolite”) used in the method of manufacturing the zeolite-carrying adsorption element. In particular, the present invention relates to a method of manufacturing the zeolite-carrying adsorption element used in an apparatus for removing organic solvent vapors by processing gases such as air containing the organic solvent vapors, and to slurry for carrying zeolite used in the method of manufacturing such a zeolite-carrying adsorption element.
BACKGROUND ART
Conventionally, an apparatus containing hydrophobic zeolite supported on a carrier to adsorb organic solvent vapors from gases, such as air containing the organic solvent vapors, has been known. For example, WO 91/16971 discloses a gas adsorption element obtained by immersing a cylindrical carrier having small permeable holes formed from silica alumina-type ceramic fibers in a slurry prepared by dispersing finely pulverized hydrophobic zeolite in a silica or alumina aqueous sol. Because the gas adsorption element contains hydrophobic zeolite carried on the surface, the element can selectively remove organic solvents from the air containing organic solvent vapors and water. Here, “hydrophobic zeolite” means zeolite containing a larger amount of SiO
2
, which exhibits stronger hydrophobicity than ordinary zeolite and, therefore, has a larger SiO
2
/Al
2
O
3
molar ratio than ordinary zeolite. Aqueous silica sol slurry is stable when the slurry is alkaline with a pH in the range of 9-11, whereas aqueous alumina sol slurry is stable when acidic with a pH of 3-5.
The pH range for inorganic binders such as silica sol and alumina sol is narrow as indicated above. Therefore, if slurry is prepared by mixing these binders with zeolite which becomes acidic when dispersed in water, the pH of the resulting slurry is outside the range in which the inorganic binders are stable, resulting in gelation of the inorganic binders and an increase in the slurry viscosity. This causes problems such as clogging of a carrier when the carrier is impregnated with slurry, leading to impaired productivity.
The amount of zeolite to be carried on an absorption element is usually 60 kg/m
3
or more, which requires a large amount of zeolite (about 17.5-25 wt %) to be formulated in slurry for the amount of an organic binder (about 15.8-20 wt % on solid basis). Such slurry has a high viscosity (about 30-35 mPa.s at 20° C.) and can clog a carrier when the carrier is impregnated with the slurry, resulting in low productivity.
In addition, although zeolite can maintain a stable crystal structure in slurry in a neutral pH range, the crystal structure tends to be destroyed due to dissolution of SiO
2
and Al
2
O
3
when the slurry becomes acidic or alkaline. In particular, the crystal structure is destroyed in an alkaline pH range more easily than in an acidic pH range, significantly impairing performance as an adsorption element of the product. Therefore, slurry containing zeolite and an inorganic binder must be adjusted to a pH at which either the zeolite or the inorganic binder is stable. Such slurry cannot be stored for a long period of time. In addition, SiO
2
is corroded by alkali more easily than Al
2
O
3
. For this reason, the crystal structure of hydrophobic zeolite is easily broken.
An object of the present invention is therefore to provide slurry for carrying zeolite which has viscosity not excessively high in spite of a large content of zeolite and binder, has a pH at which zeolite and a binder are stable, and therefore can be stored for a long time in a stable manner, and to provide a method of manufacturing a zeolite-carrying adsorption element using the slurry.
DISCLOSURE OF THE INVENTION
As a result of extensive studies, the inventor of the present invention has found that if an organic emulsion binder is used as a binder in slurry containing zeolite and a binder, the slurry may contain zeolite at a higher concentration, making it possible for zeolite to be impregnated more efficiently, can inhibit gelation of the binder, thereby allowing the slurry viscosity to be maintained in an appropriate range for a long period of time, and is almost free from pH change when a binder is added, which allows the zeolite slurry to be maintained at a pH suitable for storage of zeolite and allows the zeolite to maintain the crystal structure for a long period of time.
Specifically, the present invention provides slurry used for attaching zeolite to a carrier comprising zeolite and an organic emulsion binder dispersed in water.
The present invention further provides a method of manufacturing a zeolite-carrying adsorption element comprising causing a carrier to be impregnated with the slurry for carrying zeolite, drying the carrier, causing the carrier to be impregnated with an inorganic binder, and drying and firing the resulting carrier.
DETAILED DESCRIPTION
The slurry for carrying zeolite of the present invention comprises zeolite and an organic emulsion binder dispersed in water. Ordinary zeolite or hydrophobic zeolite having a high SiO
2
/Al
2
O
3
ratio can be used in the present invention without specific limitation. Hydrophobic zeolite, which has a high SiO
2
content and, therefore, is attacked by alkali and loses its crystal structure in slurry more easily than ordinary zeolite, is effectively used in the present invention which can maintain the zeolite crystal structure. Either one type of zeolite alone or a combination of two or more types of zeolite can be used in the present invention.
As an organic emulsion binder, one or more resins selected from the group consisting of (meth)acrylic resins, vinyl acetate resins, (meth)acrylic-styrene copolymer resins, styrene-butadiene copolymer resins, ethylene-vinyl acetate copolymer resins, and styrene-acrylonitrile-alkyl (meth)acrylate copolymer resins can be used in the present invention. Of these, an emulsion binder of styrene-acrylonitrile-alkyl (meth)acrylate copolymer resin is preferable due to excellent capability of attaching zeolite to inorganic fibers and the like.
The slurry for carrying zeolite of the present invention, which comprises zeolite and an organic emulsion binder dispersed in water, may further contain polyvinyl alcohol, as required. As examples of polyvinyl alcohol, PVA-117 and PVA-120 manufactured by Kuraray Co., Ltd. can be given. The addition of a surfactant such as polyvinyl alcohol is desirable because a surfactant increases zeolite attachment to carriers.
The slurry for carrying zeolite contains zeolite usually in an amount of 30-40 wt %, and preferably 33-37 wt %. The slurry containing zeolite in an amount in this range can efficiently impregnate a carrier with zeolite. Because the binder of the present invention is an organic emulsion binder, the content of zeolite in the slurry can be increased, thereby enabling zeolite to be efficiently impregnated in a carrier.
The slurry for carrying zeolite contains an organic emulsion binder usually in an amount of 3-7 wt %, and preferably 3-5 wt %, on a solid basis. The addition of an organic emulsion binder in the amount of the above range is desirable for increasing attachment of zeolite to the carrier and for improving impregnation of the carrier with zeolite.
The slurry for carrying zeolite usually has a viscosity in the range of 15-20 mPa.s, and preferably 15-17 mPa.s, at 20° C. The viscosity of the slurry for carrying zeolite in the above range is preferable to prevent the carrier from clogging when the carrier is impregnated with zeolite. In general, slurry for carrying zeolite easily clogs the carrier if the viscosity is 25 mPa.s or above. However, because the viscosity of the slurry of the present invention can be maintained in the above preferable range notwithstanding a high concentration of zeolite due to the use of an organic emulsion binder, the carrier can be efficiently impregnated with zeolite without being clogged.
Shimada Jun
Yamazaki Teruzi
Cooke Colleen P.
Dunn Tom
Nichias Co., Ltd.
Oblon & Spivak, McClelland, Maier & Neustadt P.C.
LandOfFree
Slurry for carrying zeolite and method for manufacturing... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Slurry for carrying zeolite and method for manufacturing..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Slurry for carrying zeolite and method for manufacturing... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-3264452