Electrolysis: processes – compositions used therein – and methods – Electrolytic coating – Utilizing fused bath
Reexamination Certificate
1998-07-30
2001-06-19
Valentine, Donald R. (Department: 1741)
Electrolysis: processes, compositions used therein, and methods
Electrolytic coating
Utilizing fused bath
C205S383000, C205S384000, C205S387000, C204S243100, C204S244000, C204S245000, C204S247300, C204S290010, C204S290120, C204S290130, C204S293000, C204S247000
Reexamination Certificate
active
06248227
ABSTRACT:
FIELD OF THE INVENTION
This invention relates to non-carbon, metal-based, slow consumable anodes for use in cells for the electrowinning of aluminium by the electrolysis of alumina dissolved in a molten fluoride-containing electrolyte, and to methods for their fabrication and reconditioning, as well as to electrowinning cells containing such anodes and their use to produce aluminium.
BACKGROUND ART
The technology for the production of aluminium by the electrolysis of alumina, dissolved in molten cryolite, at temperatures around 950° C. is more than one hundred years old.
This process, conceived almost simultaneously by Hall and Héroult, has not evolved as many other electrochemical processes.
The anodes are still made of carbonaceous material and must be replaced every few weeks. The operating temperature is still not less than 950° C. in order to have a sufficiently high solubility and rate of dissolution of alumina and high electrical conductivity of the bath.
The carbon anodes have a very short life because during electrolysis the oxygen which should evolve on the anode surface combines with the carbon to form polluting CO
2
and small amounts of CO and fluorine-containing dangerous gases. The actual consumption of the anode is as much as 450 Kg/Ton of aluminium produced which is more than ⅓ higher than the theoretical amount of 333 Kg/Ton.
The frequent substitution of the anodes in the cells is still a clumsy and unpleasant operation. This cannot be avoided or greatly improved due to the size and weight of the anode and the high temperature of operation.
Several improvements were made in order to increase the lifetime of the anodes of aluminium electrowinning cells, usually by improving their resistance to chemical attacks by the cell environment and air to those parts of the anodes which remain outside the bath. However, most attempts to increase the chemical resistance of anodes were coupled with a degradation of their electrical conductivity.
U.S. Pat. No. 4,614,569 (Duruz et al.) describes anodes for aluminium electrowinning coated with a protective coating of cerium oxyfluoride, formed in-situ in the cell or pre-applied, this coating being maintained by the addition of cerium to the molten cryolite electrolyte. This made it possible to have a protection of the surface only from the electrolyte attack and to a certain extent from the gaseous oxygen but not from the nascent monoatomic oxygen.
EP Patent application 0 306 100 (Nyguen/Lazouni/ Doan) describes anodes composed of a chromium, nickel, cobalt and/or iron based substrate covered with an oxygen barrier layer and a ceramic coating of nickel, copper and/or manganese oxide which may be further covered with an in-situ formed protective cerium oxyfluoride layer.
Likewise, U.S. Pat. Nos. 5,069,771, 4,960,494 and 4,956,068 (all Nyguen/Lazouni/Doan) disclose aluminium production anodes with an oxidised copper-nickel surface on an alloy substrate with a protective barrier layer. However, full protection of the alloy substrate was difficult to achieve.
A significant improvement described in U.S. Pat. No. 5,510,008, and in International Application WO96/12833 (Sekhar/Liu/Duruz) involved micropyretically producing a body from nickel, aluminium, iron and copper and oxidising the surface before use or in-situ. By said micropyretic methods materials have been obtained whose surfaces, when oxidised, are active for the anodic reaction and whose metallic interior has low electrical resistivity to carry a current from high electrical resistant surface to the busbars. However it would be useful, if it were possible, to simplify the manufacturing process of these materials and increase their life to make their use economic.
Metal or metal-based anodes are highly desirable in aluminium electrowinning cells instead of carbon-based anodes. As described hereabove, many attempts were made to use metallic anodes for aluminium production, however they were never adopted by the aluminium industry because of their poor performance.
OBJECTS OF THE INVENTION
An object of the present invention is to provide a non-carbon, metal-based anode for the electrowinning of aluminium so as to eliminate carbon-generated pollution and reduce the frequency of anode replacement, such an anode having an outside layer well resistant to chemical electrolyte attack whose surface is electrochemically active for the oxidation of oxygen ions contained in the electrolyte and for the formation of gaseous oxygen.
A further object of the invention is to provide a metal-based anode capable of generating during normal electrolysis at its surface an electrochemically active oxide layer which slowly and progressively dissolves into the electrolyte.
A major object of the invention is to provide an anode for the electrowinning of aluminium which has no carbon so as to eliminate carbon-generated pollution and reduce the high cell voltage.
SUMMARY OF THE INVENTION
The invention relates to a non-carbon, metal-based slow-consumable anode of a cell for the electrowinning of aluminium by the electrolysis of alumina dissolved in a molten fluoride-based electrolyte. The anode self-forms during normal electrolysis an electrochemically-active oxide-based surface layer, the rate of formation of said layer being substantially equal to its rate of dissolution at the surface layer/electrolyte interface thereby maintaining its thickness substantially constant forming a limited barrier controlling the oxidation rate.
In this context, metal-based anode means that the anode contains at least one metal as such or as an alloy, intermetallic and/or cermet.
During normal operation, the anode thus comprises a metallic (un-oxidised) anode body (or layer) on which and from which the oxide-based surface layer is formed.
The electrochemically active oxide-based surface layer may contain an oxide as such, or in a multi-compound mixed oxide and/or in a solid solution of oxides. The oxide may be in the form of a simple, double and/or multiple oxide, and/or in the form of a stoichiometric or non-stoichiometric oxide.
The oxide-based surface layer has several functions. Besides protecting in some measure the metallic anode body against chemical attack in the cell environment and its electrochemical function for the conversion of oxygen ions to molecular oxygen, the oxide-based surface layer controls the diffusion of oxygen which oxidises the anode body to further form the surface layer.
When the oxide-based surface layer is too thin, in particular at the start-up of electrolysis, the diffusion of oxygen towards the metallic body is such as to oxidise the metallic anode body at the surface layer/anode body interface with formation of the oxide-based surface layer at a faster rate than the dissolution rate of the surface layer into the electrolyte, allowing the thickness of the oxide-based surface layer to increase. The thicker the oxide-based surface layer becomes, the more difficult it becomes for oxygen to reach the metallic anode body for its oxidation and therefore the rate of formation of the oxide-based surface layer decreases with the increasing thickness of the surface layer. Once the rate of formation of the oxide-based surface layer has met its rate of dissolution into the electrolyte an equilibrium is reached at which the thickness of the surface layer remains substantially constant and during which the metallic anode body is oxidised at a rate which substantially corresponds to the rate of dissolution of the oxide-based surface layer into the electrolyte.
In contrast to carbon anodes, in particular pre-baked carbon anodes, the consumption of the non-carbon, metal-based anodes according to the invention is at a very slow rate. Therefore, these slow consumable anodes in drained cell configurations do not need to be regularly repositioned in respect of their facing cathodes since the anode-cathode gap does not substantially change.
To practically realise the invention, the anode body can comprise an iron alloy which when oxidised will form an oxide-based surface layer containing a ferrite so
De Nora Vittorio
Duruz Jean-Jacques
Deshmukh Jayadeep R.
Moltech Invent S.A.
Valentine Donald R.
LandOfFree
Slow consumable non-carbon metal-based anodes for aluminium... does not yet have a rating. At this time, there are no reviews or comments for this patent.
If you have personal experience with Slow consumable non-carbon metal-based anodes for aluminium..., we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Slow consumable non-carbon metal-based anodes for aluminium... will most certainly appreciate the feedback.
Profile ID: LFUS-PAI-O-2477869