06783568

ABSTRACT:

BACKGROUND OF THE INVENTION
1. Technical Field
The present invention relates to a sintered steel material and to a method for the manufacture thereof.
2. Related Art
Sintered steel materials sintered from compacted mixtures comprising a hot working tool steel powder, iron powder and carbon additions in the form of graphite are known from EP-A-0 418 943 of common ownership herewith. The hot working tool steel is generally based upon one or more of those known as AISI H11, H12 and H13. Whilst components manufactured from these materials, such as valve seat inserts for internal combustion engines for example, perform well in operation, they do have some disadvantages associated with the manufacture thereof. In order to achieve the necessary wear resistance in applications such as valve seat inserts it is necessary to provide a certain minimum level of carbon in the structure due to the relatively low level of alloying additions in the hot working tool steels. However, carbon acts as an austenite stabiliser in steels. It is desirable not to have retained austenite in components such as are contemplated for use with these materials since austenite is unstable and if it gradually transforms to an untempered martensite during operation in an engine due to the high temperature environment, component size changes can result and the wear characteristics of the component can become unstable. Therefore, in order to remove austenite, multiple cryogenic and tempering thermal treatments are performed so as to obviate the presence of austenite. However, such multiple thermal treatments are by their very nature time consuming, and there re, expensive in terms of production costs. If the carbon level is restricted to obviate the retained austenite problem, then wear resistance is adversely affected.
EP-A-0 312 161, also of common ownership herewith, describes sintered steels made from compacted and sintered mixtures of high-speed tool steels, iron powder and carbon additions in the form of graphite. The high-speed tool steels contemplated for use are generally based on the M3/2 class. The sintered steels described in EP-A-0 312 161 are generally of lower carbon content than those described in EP-A-0 418 943. This is due to the fact that the alloying addition levels of the principal carbide forming elements of Mo, V and W are greater in these materials and which maintains the required high degree of wear resistance in applications such as valve seat inserts for example. As a result of the lower carbon level, there is less of a problem in removing austenite from the structure after sintering. However, the problem with the alloys described in EP-A-0 312 161 is one of material cost due to the relatively high level of alloying additions.
A further disadvantage of the materials described in EP-A-0 312 161 is their relatively low compressibility due to their relatively high alloying content and consequently higher work-hardening rate.
SUMMARY OF THE INVENTION
It is an object of the I)resent invention to provide a sintered steel material which is easier and more economic to manufacture, lower in material cost than other prior art materials whilst retaining a comparable level of performance in applications such as valve seat inserts for internal combustion engines for example. However, these criteria apply also to any applications requiring resistance to abrasive wear, and resistance to wear at elevated temperatures.
DETAILED DESCRIPTION
According to a first aspect of the present invention, there is provided a method for the manufacture of a material by a powder metallurgy route, the method comprising the steps of providing a first pre-alloyed steel powder having a composition comprising in weight %: C 0.5-2, Cr 3.5-6, (2Mo+W) 12-22, V 0.5-5, Co 0-12, Mn 0.1-0.5, Si 0.1-0.6, Fe balance apart from incidental impurities; providing a second pre-alloyed steel powder having a composition comprising in weight %: C 0.3-0.7, Cr 3-5.5, Mo 1-2.5, V 0.3-1.5, W 0-2, Mn 0.1-0.6, Si 0.8-1.2, Fe balance apart from incidental impurities; mixing together from 2 to 50 weight of the first pre-alloyed steel powder with 98 to 50 weight % of the second pre-alloyed steel powder, optionally up to 60 weight % of an iron powder and with carbon powder such that the final carbon content of the matrix of the sintered steel powder is a maximum of 1.1 weight %; compacting said mixture and sintering to form said sintered steel.
The maximum content of the first pre-alloyed steel powder is 50 wt %. However, this maximum is set by the economic advantage to be gained and it is preferred that the maximum content of the first pre-alloyed steel powder is 30 wt %.
A more preferred content of the first pre-alloyed steel powder is 5 to 20 wt %.
A preferred composition of the first pre-alloyed steel powder is in weight %: C 0.7-1.1; Cr 3.5-4.5; Mo 4.5-6.5; V 1.5-3.5; W 5.5-7; Mn 0-0.4; Si 0-0.4; Fe balance apart from incidental impurities.
Preferably, the content of iron powder is a minimum of 5 wt %.
More preferably, the content of iron powder in the mixture is from 10 to 50 wt %. The iron powder, for the purposes of the present invention is defined as an iron powder which has less than 1 wt % maximum of alloying additions therein and is substantially carbon free. If more than 60 wt % of iron powder is incorporated in the sintered steel, the wear resistance and thermal softening resistance of the product deteriorate.
Part of the total carbon content of the final sintered steel may be added as carbon powder in the form of graphite for example :to the initial powder mixture prior to compaction to form the initial un-sintered “green” compact. The carbon aids compaction by acting as a powder and die lubricant. Only sufficient carbon is added so as to produce a maximum carbon content of 1.1 wt % in the finished sintered ferrous matrix. However, in some embodiments of sintered steels according to the present invention, the total carbon content may be below this level as adequate wear resistance is provided by the regions in the sintered matrix constituted by the first pre-alloyed steel powder. These regions are rich in carbides formed from alloying constituents comprising principally Cr, Mo, V and W.
The microstructure of the sintered steels formed according to the method of the present invention comprises a matrix formed by regions derived from the second steel powder which regions comprise tempered martensite with a fine distribution of carbide precipitates and regions derived from the iron powder when present, comprising pearlite, occasional ferrite and bainite transition zones with the steel martensite regions. The matrix further includes a distribution of tempered martensite regions including spheroidal alloy carbide precipitates derived from the first alloy steel powder randomly dispersed throughout the matrix. The prior particle boundaries are well diffused as a result of the sintering step.
The structure of the sintered steel according to the present invention endows the material with good wear resistance by virtue of the dispersion of hard, alloy carbide containing particles from the first pre-alloyed steel powder distributed throughout the matrix. Thus, the wear properties are maintained whilst maintaining a relatively low overall carbon content which is beneficial in eliminating retained austenite. Furthermore, material costs are reduced due to a relatively low content of the first pre-alloyed steel powder which contains more of the expensive alloying elements.
According to a second aspect of the present invention, there is provided an article made by the second aspect of the present invention.
Articles according to the second aspect of the present invention may include components for internal combustion engines comprising valve seat inserts, tappets, cam followers for example. Other articles may include general engineering components requiring good wear resistance and include, for example, impeller and stator components for pumps.
The method of the present invention may also include the addition of die lubricant wax to the powder mi

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Sintered steel material does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Sintered steel material, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Sintered steel material will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFUS-PAI-O-3342058

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.