Silicon-aluminum mixed oxide

Compositions: ceramic – Ceramic compositions – Aluminum compound containing

Reexamination Certificate

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

C501S128000, C423S327200, C423S336000

Reexamination Certificate

active

06455455

ABSTRACT:

INTRODUCTION AND BACKGROUND
This invention relates to a silicon-aluminum mixed oxide, a process for the production thereof as well as the use as a polishing agent in dispersions which are used, for example, for polishing electronic components, in particular for CMP applications.
The patent specification EP-0 585 544 discloses pulverulent silicon-aluminum mixed oxides produced by flame hydrolysis which are of amorphous structure and have a composition of from 65 to 72.1 wt. % Al
2
O
3
and from 27.9 to 35 wt. % SiO
2
and a BET surface area of between 20 and 200 m
2
/g
SUMMARY OF THE INVENTION
The invention provides a silicon-aluminum mixed oxide powder produced by flame hydrolysis and having a composition of from 1 to 99.999 wt. % Al
2
O
3
, preferably 40 to 80 wt. % Al
2
O
3
, the remainder being SiO
2
, wherein the powder exhibits an amorphous structure in the X-ray diffraction pattern and consists of intergrown primary particles, and in these primary particles crystallites are present, and these crystallites have sizes of one to 200 namometers and the specific surface area of the powder is 5 to 300 m
2
/g, preferably 50 to 150 m
2
/g.
The invention also provides a process for the production of the silicon-aluminum oxide powder produced by flame hydrolysis according to the invention, wherein silicon halide and aluminum halide are vaporized in a particular ratio to one another and are homogeneously mixed with air, oxygen and hydrogen in a mixing unit by means of a carrier gas. This mixture then undergoes combustion in a burner of known construction. After the separation of the solids from the vapour phase, any traces of halide possibly adhering to the product are separated off in a further processing step by means of moist air at elevated temperature.
It has now been found that silicon-aluminum mixed oxides according to the invention which are made into a dispersion exhibit outstanding properties as polishing agents.
These dispersions can be used in particular for polishing in the electronics industry (CMP).


REFERENCES:
patent: 3130008 (1964-04-01), Stokes et al.
patent: 4960738 (1990-10-01), Hori et al.
patent: 5061474 (1991-10-01), Pauli et al.
patent: 5380687 (1995-01-01), Mangold et al.
patent: 5384306 (1995-01-01), König et al.
patent: 5424258 (1995-06-01), Mangold et al.
patent: 5432137 (1995-07-01), Nishihara et al.
patent: 6197469 (2001-03-01), Kerner et al.
patent: 0023588 (1981-02-01), None
patent: 0554908 (1993-08-01), None
patent: 0585544 (1994-03-01), None

LandOfFree

Say what you really think

Search LandOfFree.com for the USA inventors and patents. Rate them and share your experience with other people.

Rating

Silicon-aluminum mixed oxide does not yet have a rating. At this time, there are no reviews or comments for this patent.

If you have personal experience with Silicon-aluminum mixed oxide, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Silicon-aluminum mixed oxide will most certainly appreciate the feedback.